ABSTRACT: In mixed-valent Kondo lattice systems, such as YbAl3, interactions between localized and delocalized electrons can lead to fluctuations between two different valence configurations with changing temperature or pressure. The impact of this change on the momentum-space electronic structure is essential for understanding their emergent properties, but has remained enigmatic. Here, by employing a combination of molecular beam epitaxy and in situ angle-resolved photoemission spectroscopy we show that valence fluctuations can lead to dramatic changes in the Fermi surface topology, even resulting in a Lifshitz transition. As the temperature is lowered, a small electron pocket in YbAl3 becomes completely unoccupied while the low-energy ytterbium (Yb) 4f states become increasingly itinerant, acquiring additional spectral weight, longer lifetimes, and well-defined dispersions. Our work presents a unified picture of how local valence fluctuations connect to momentum-space concepts such as band filling and Fermi surface topology in mixed valence systems.How the electronic structure of a mixed-valence system changes with respect to local chemical environment remains elusive. Here, Chatterjee et al. show that valence fluctuations of YbAl3 can lead to dramatic changes in the Fermi surface topology in reciprocal space.

SUBMITTER: Chatterjee S

PROVIDER: S-EPMC5636910 | biostudies-literature | 2017 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Lifshitz transition from valence fluctuations in YbAl<sub>3</sub>.

Chatterjee Shouvik S Ruf Jacob P JP Wei Haofei I HI Finkelstein Kenneth D KD Schlom Darrell G DG Shen Kyle M KM

Nature communications 20171011 1

In mixed-valent Kondo lattice systems, such as YbAl<sub>3</sub>, interactions between localized and delocalized electrons can lead to fluctuations between two different valence configurations with changing temperature or pressure. The impact of this change on the momentum-space electronic structure is essential for understanding their emergent properties, but has remained enigmatic. Here, by employing a combination of molecular beam epitaxy and in situ angle-resolved photoemission spectroscopy w ...[more]

PMID: 29021552

Similar Datasets

Project description:A temperature induced valence phase transition from Yb3+ at higher temperatures to Yb2+ at lower temperatures was observed at T = 110(1) K for intermetallic YbPd2Al3. The title compound has been prepared from the elements in sealed tantalum ampoules. The structure was refined from single-crystal data and the title compound was found to crystallize in the hexagonal YNi2Al3 type structure with space group P6/mmm and lattice parameters of a = 929.56(7) and c = 420.16(3) pm (300 K data). Full ordering of the Pd and Al atoms within the [Pd2Al3] ?- polyanion was observed. Magnetic measurements revealed an anomaly in the dc susceptibility data and intermediate valent Yb at higher temperature, as observed from the effective magnetic moment. The proposed valence phase transition was also observed as a ?-type anomaly in heat capacity measurements (T = 108.4(1) K), however, no systematic shift of the ?-peak was observed in field dependent heat capacity measurements. An antiferromagnetic ordering at this temperature, however, could be excluded, based on field-dependent susceptibility measurements and magnetization isotherms. No dynamic phenomenon was observed in ac susceptibility measurements, excluding e.g. spin-glass behavior. Subsequent temperature dependent single-crystal and powder X-ray diffraction experiments indicated a steep increase in the length of the c axis around T = 110 K upon cooling. However, no structural phase transition was found via single-crystal diffraction experiments conducted at 90 K. The anomaly was also observed in other physical measurements of e.g. the electrical resistivity, indicating a clear change in the electronic structure of the material. X-ray photoelectron spectroscopy conducted at room temperature shows the presence of both, Yb2+ and Yb3+, underlining the mixed-valent state. Members of the solid solution Yb1-x Ca x Pd2Al3 (x = 0.33, 0.67, 1) were finally used to further study the charge ordering and the present temperature induced valence phase transition.

Dataset Information

Lifshitz transition from valence fluctuations in YbAl3.

Publications

Lifshitz transition from valence fluctuations in YbAl<sub>3</sub>.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets