New ZnO@Cardanol Porphyrin Composite Nanomaterials with Enhanced Photocatalytic Capability under Solar Light Irradiation.

ABSTRACT: This work describes the synthesis, characterization, and photocatalytic activity of new composite nanomaterials based on ZnO nanostructures impregnated by lipophlilic porphyrins derived from cashew nut shell liquid (CNSL). The obtained nanomaterials were characterized by X-ray diffraction (XRD), UV-Vis diffuse reflectance spectroscopy (DRS), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), and steady-state photoluminescence spectra (PL). The results confirm nanostructures showing average diameter of 55 nm and an improved absorption in the visible region. Further, the FTIR analysis proved the existence of non-covalent interactions between the porphyrin molecules and ZnO. The photocatalytic activity of prepared photocatalysts was investigated by degradation of rhodamine B (RhB) in aqueous solution under visible light irradiation and natural sunlight. It was demonstrated that the photocatalytic activity increases in the presence of the porphyrins and, also, depends on the irradiation source. The development of composite photocatalysts based on porphyrins derived from CNSL provides an alternative approach to eliminate efficiently toxic wastes from water under ambient conditions.

SUBMITTER: Ribeiro VGP

PROVIDER: S-EPMC5666920 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

ZnO Nanorods with High Photocatalytic and Antibacterial Activity under Solar Light Irradiation.

Project description:ZnO nanorods (NRs) with an average length and diameter of 186 and 20 nm, respectively, were prepared through a mild solvothermal route and used as photocatalysts either as dispersed powder or immobilized on glass slides. The ZnO NRs were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). Dispersed ZnO NRs and, to a lesser extent, immobilized ZnO NRs were demonstrated to exhibit high photocatalytic activity under simulated sunlight of low intensity (5.5 mW/cm²) both for the degradation of the Orange II dye and for Escherichia coli bacterial decontamination (2.5-fold survival decrease after 180 min irradiation for immobilized NRs). SEM, atomic force microscopy (AFM), fluorescence spectroscopy, and epifluorescence microscopy demonstrate that cell surface damages are responsible of bacterial inactivation. The immobilized ZnO NRs could be reused up to five times for bacterial decontamination at comparable efficiency and therefore have great potential for real environmental applications.

| S-EPMC6266891 | biostudies-literature

Surface Modification of ZnO with Sn(IV)-Porphyrin for Enhanced Visible Light Photocatalytic Degradation of Amaranth Dye.

Project description:Two hybrid composite photocatalysts, denoted as SnP/AA@ZnO and SnP@ZnO, were fabricated by a reaction of trans-dihydroxo[5,10,15,20-tetrakis(4-pyridyl)porphyrinato]tin(IV) (SnP) and ZnO with and without pretreatment of adipic acid (AA), respectively. In SnP@ZnO, SnP and ZnO are likely held together by a coordinative interaction between the pyridyl N atoms of SnP and the Zn atoms on the surface of ZnO. In the case of SnP/AA@ZnO, the SnP centers were robustly coupled with ZnO nanoparticles through the AA anchors. SnP/AA@ZnO exhibited largely enhanced photocatalytic activities for the degradation of anionic amaranth (AM) dye under a visible light irradiation, compared to SnP, ZnO, and SnP@ZnO. The degradation efficiency of AM by SnP/AA@ZnO was 95% within 60 min at a rate constant of 0.048 min-1. The remarkable photocatalytic oxidation performance of SnP/AA@ZnO was mainly attributed to the synergistic effect between SnP and ZnO. This study is valuable for the development of highly effective composite photocatalytic systems in advanced oxidation processes and is of importance for the treatment of wastewater containing dyes.

| S-EPMC10536602 | biostudies-literature

ZnO Porous Nanosheets with Partial Surface Modification for Enhanced Charges Separation and High Photocatalytic Activity Under Solar Irradiation.

Project description:ZnO porous nanosheets (PNSs) with partial surface modification were fabricated by means of depositing amorphous BiVO4 on basic zinc carbonate nanosheets followed by calcining at 500 °C. At low levels of anchored amorphous BiVO4, the surface of ZnO PNSs was partially evolved into Bi3.9Zn0.4V1.7O10.5 (BZVO). The measurements for photocurrent and photoluminescence demonstrate that partial-surface BZVO-modified ZnO PNSs (ZB_0.01) could significantly inhibit the recombination of photoinduced carriers. This should be ascribable to the driving from surface potential difference produced by non-junction part and vertical p-n BZVO/ZnO junction part on the surface of ZB_0.01. Furthermore, the photocatalytic efficiency in degradation of reactive brilliant red for ZB_0.01 under weak solar irradiation is about 8 times higher than that under strong visible-light illumination. The discussion regarding reasons for this enhancement demonstrates that each component in photocatalysts having rational valence-band maximum and conduction-band minimum energy levels is essential to obtain high-activity sunlight-driven catalysts.

| S-EPMC6497717 | biostudies-literature

Magnetic ZnO Crystal Nanoparticle Growth on Reduced Graphene Oxide for Enhanced Photocatalytic Performance under Visible Light Irradiation.

Project description:Magnetite zinc oxide (MZ) (Fe3O4/ZnO) with different ratios of reduced graphene oxide (rGO) was synthesized using the solid-state method. The structural and optical properties of the nanocomposites were analyzed using transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, Fourier-transform infrared spectroscopy (FTIR), ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis/DRS), and photoluminescence (PL) spectrophotometry. In particular, the analyses show higher photocatalytic movement for crystalline nanocomposite (MZG) than MZ and ZnO nanoparticles. The photocatalytic degradation of methylene blue (MB) with crystalline ZnO for 1.5 h under visible light was 12%. By contrast, the photocatalytic activity for MZG was more than 98.5%. The superior photocatalytic activity of the crystalline nanocomposite was detected to be due to the synergistic effect between magnetite and zinc oxide in the presence of reduced graphene oxide. Moreover, the fabricated nanocomposite had high electron-hole stability. The crystalline nanocomposite was stable when the material was used several times.

| S-EPMC8070817 | biostudies-literature

Solar Driven Photocatalytic Activity of Porphyrin Sensitized TiO2: Experimental and Computational Studies.

Project description:The absence of a secure long-term sustainable energy supply is recognized as a major worldwide technological challenge. The generation of H2 through photocatalysis is an environmentally friendly alternative that can help solve the energy problem. Thus, the development of semiconductor materials that can absorb solar light is an attractive approach. TiO2 has a wide bandgap that suffers from no activity in the visible spectrum, limiting its use of solar radiation. In this research, the semiconductor absorption profile was extended into the visible region of the solar spectrum by preparing porphyrin-TiO2 (P-TiO2) composites of meso-tetra(4-bromophenyl)porphyrin (PP1) and meso-tetra(5-bromo-2-thienyl)porphyrin (PP2) and their In(III), Zn(II) and Ga(III) metal complexes. Density functional theory (DFT) and time-dependent density functional theory (TD-DFT) calculations were performed on the porphyrins to gain insight into their electron injection capability. The results demonstrate that P-TiO2 systems merit further in-depth study for applications that require efficient photocatalytic H2 generation.

| S-EPMC8197238 | biostudies-literature

Towards the Continuous Hydrothermal Synthesis of ZnO@Mg2Al-CO3 Core-Shell Composite Nanomaterials.

Project description:Core-shell Zinc Oxide/Layered Double Hydroxide (ZnO@LDH) composite nanomaterials have been produced by a one-step continuous hydrothermal synthesis process, in an attempt to further enhance the application potential of layered double hydroxide (LDH) nanomaterials. The synthesis involves two hydrothermal reactors in series with the first producing a ZnO core and the second producing the Mg2Al-CO3 shell. Crystal domain length of single phase ZnO and composite ZnO was 25 nm and 42 nm, respectively. The ZnO@LDH composite had a specific surface area of 76 m2 g-1, which was larger than ZnO or Mg2Al-CO3 when produced separately (53 m2 g-1 and 58 m2 g-1, respectively). The increased specific surface area is attributed to the structural arrangement of the Mg2Al-CO3 in the composite. Platelets are envisaged to nucleate on the core and grow outwards, thus reducing the face-face stacking that occurs in conventional Mg2Al-CO3 synthesis. The Mg/Al ratio in the single phase LDH was close to the theoretical ratio of 2, but the Mg/Al ratio in the composite was 1.27 due to the formation of Zn2Al-CO3 LDH from residual Zn2+ ions. NaOH concentration was also found to influence Mg/Al ratio, with lower NaOH resulting in a lower Mg/Al ratio. NaOH concentration also affected morphology and specific surface area, with reduced NaOH content in the second reaction stage causing a dramatic increase in specific surface area (> 250 m2 g-1). The formation of a core-shell composite material was achieved through continuous synthesis; however, the final product was not entirely ZnO@Mg2Al-CO3. The product contained a mixture of ZnO, Mg2Al-CO3, Zn2Al-CO3, and the composite material. Whilst further optimisation is required in order to remove other crystalline impurities from the synthesis, this research acts as a stepping stone towards the formation of composite materials via a one-step continuous synthesis.

| S-EPMC7602976 | biostudies-literature

Photocatalytic degradation of dissolved organic matter under ZnO-catalyzed artificial sunlight irradiation system.

Project description:This study investigates the photocatalytic degradation of dissolved organic matter (DOM) under ZnO-assisted artificial sunlight system at various conditions (ZnO dosage, pH, and the presence of Cl-, SO42-, and HCO3-). The results show that the degradation of DOM follows a pseudo-first-order kinetics. Fluorescence excitation-emission matrices coupled with parallel factor (EEM-PARAFAC) analysis decomposes DOM into two fluorophores (C1 and C2). The total removals and photodegradation rates calculated with DOC, UV254, and the Fmax of C1 are similar, increasing with higher ZnO dosages and being highest in pH 7 and lowest in pH 4. ZnO dosage has a similar effect on DOM degradation when assessed using C2, as with C1, but pH effect is not consistent. As for the anions, HCO3- shows the strongest inhibition for DOC, UV254 and C1 while Cl- has the strongest facilitation effect for C2. The total removal and photodegradation rates calculated with the Fmax of C1 and C2 are higher than those calculated using DOC and UV254. This study demonstrates that the successful application of EEM-PARAFAC analysis in addition to traditional parameters can provide further insight into the photocatalytic degradation mechanisms associated with DOM in conjunction with a ZnO catalyst under artificial sunlight.

| S-EPMC7403426 | biostudies-literature

Synthesis and Characterization of ZnO-TiO2/Carbon Fiber Composite with Enhanced Photocatalytic Properties.

Project description:Herein, we prepared a novel photocatalytic ZnO-TiO2 loaded carbon nanofibers composites (ZnO-TiO2-CNFs) via electrospinning technique followed by a hydrothermal process. At first, the electrospun TiO2 NP-embedded carbon nanofibers (TiO2-CNFs) were achieved using electrospinning and a carbonization process. Next, the ZnO particles were grown into the TiO2-CNFs via hydrothermal treatment. The morphology, structure, and chemical compositions were studied using state-of-the-art techniques. The photocatalytic performance of the ZnO-TiO2-CNFs composite was studied using degrading methylene blue (MB) under UV-light irradiation for three successive cycles. It was noticed that the ZnO-TiO2-CNFs nanocomposite showed better MB removal properties than that of other formulations, which might be due to the synergistic effects of carbon nanofibers and utilized metal oxides (ZnO and TiO2). The adsorption characteristic of carbon fibers and matched band potentials of ZnO and TiO2 combinedly help to boost the overall photocatalytic performance of the ZnO-TiO2-CNFs composite. The obtained results from this study indicated that it can be an economical and environmentally friendly photocatalyst.

| S-EPMC7600166 | biostudies-literature

Photoactive ZnO Materials for Solar Light-Induced Cu<sub>x</sub>O-ZnO Catalyst Preparation.

Project description:In this work, the solar light-induced redox photoactivity of ZnO semiconductor material was used to prepare CuxO-ZnO composite catalysts at room temperature with a control of the chemical state of the copper oxide phase. Cu₂(I)O-ZnO and Cu(II)O-ZnO composite catalysts were prepared by using Cu(acac)₂ in tetrahydrofuran-water and Cu(NO₃)₂ in water as metallic precursor, respectively. Prior to the implementation of the photon-assisted synthesis method, the most efficient photoactive ZnO material was selected from among different ZnO materials prepared by the low temperature polyol and precipitation methods with carbonates and carbamates as precipitation agents. The photocatalytic degradation of the 4-chlorophenol compound in water under simulated solar light was taken as a model reaction. The ZnO support materials were characterized by X-ray diffraction (XRD), surface area and porosimetry measurements, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and the synthesis method strongly influenced their photoactivity in terms of 4-chlorophenol degradation and of total organic carbon removal. The most photoactive ZnO material was prepared by precipitation with carbonates and calcined at 300 °C, benefitting from a high specific surface area and a small mean crystallite size for achieving a complete 4-chlorophenol mineralization within 70 min of reaction, with minimum Zn2+ released to the solution. Besides thermal catalysis applications, this work has opened a new route for the facile synthesis of Cu₂O-ZnO heterojunction photocatalysts that could take place under solar light of the heterojunction built between the p-type semi-conductor Cu₂O with direct visible light band gap and the ZnO semiconductor phase.

| S-EPMC6266916 | biostudies-literature

ZnO@SnO2 engineered composite photoanodes for dye sensitized solar cells.

Project description:Layered multi-oxide concept was applied for fabrication of photoanodes for dye-sensitized solar cells based on ZnO and SnO2, capitalizing on the beneficial properties of each oxide. The effect of different combinations of ZnO@SnO2 layers was investigated, aimed at exploiting the high carrier mobility provided by the ZnO and the higher stability under UV irradiation pledged by SnO2. Bi-oxide photoanodes performed much better in terms of photoconversion efficiency (PCE) (4.96%) compared to bare SnO2 (1.20%) and ZnO (1.03%). Synergistic cooperation is effective for both open circuit voltage and photocurrent density: enhanced values were indeed recorded for the layered photoanode as compared with bare oxides (Voc enhanced from 0.39 V in case of bare SnO2 to 0.60 V and Jsc improved from 2.58 mA/cm(2) pertaining to single ZnO to 14.8 mA/cm(2)). Improved functional performances of the layered network were ascribable to the optimization of both high chemical capacitance (provided by the SnO2) and low recombination resistance (guaranteed by ZnO) and inhibition of back electron transfer from the SnO2 conduction band to the oxidized species of the electrolyte. Compared with previously reported results, this study testifies how a simple electrode design is powerful in enhancing the functional performances of the final device.

| S-EPMC4588567 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data