Influence of non-thermal plasma on structural and electrical properties of globular and nanostructured conductive polymer polypyrrole in water suspension.

ABSTRACT: Non-thermal plasma has proved its benefits in medicine, plasma assisted polymerization, food industry and many other fields. Even though, the ability of non-thermal plasma to modify surface properties of various materials is generally known, only limited attention has been given to exploitations of this treatment on conductive polymers. Here, we show study of non-thermal plasma treatment on properties of globular and nanostructured polypyrrole in the distilled water. We observe that plasma presence over the suspension level doesn't change morphology of the polymer (shape), but significantly influences its elemental composition and physical properties. After 60 min of treatment, the relative concentration of chloride counter ions decreased approximately 3 and 4 times for nanostructured and globular form, respectively and concentration of oxygen increased approximately 3 times for both forms. Simultaneously, conductivity decrease (14 times for globular and 2 times for nanostructured one) and changes in zeta potential characteristics of both samples were observed. The modification evolution was dominated by multi-exponential function with time constants having values approximately 1 and 10 min for both samples. It is expected that these time constants are related to two modification processes connected to direct presence of the spark and to long-lived species generated by the plasma.

SUBMITTER: Galar P

PROVIDER: S-EPMC5678096 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Nanostructured Conductive Polypyrrole for Antibacterial Components in Flexible Wearable Devices.

Project description:The power generated by flexible wearable devices (FWDs) is normally insufficient to eradicate bacteria, and many conventional antibacterial strategies are also not suitable for flexible and wearable applications because of the strict mechanical and electrical requirements. Here, polypyrrole (PPy), a conductive polymer with a high mass density, is used to form a nanostructured surface on FWDs for antibacterial purposes. The conductive films with PPy nanorods (PNRs) are found to sterilize 98.2 ± 1.6% of Staphylococcus aureus and 99.6 ± 0.2% of Escherichia coli upon mild electrification (1 V). Bacteria killing stems from membrane stress produced by the PNRs and membrane depolarization caused by electrical neutralization. Additionally, the PNR films exhibit excellent biosafety and electrical stability. The results represent pioneering work in fabricating antibacterial components for FWDs by comprehensively taking into consideration the required conductivity, mechanical properties, and biosafety.

| S-EPMC10013960 | biostudies-literature

Aqueous Processable One-Dimensional Polypyrrole Nanostructured by Lignocellulose Nanofibril: A Conductive Interfacing Biomaterial.

Project description:One-dimensional (1D) nanomaterials of conductive polypyrrole (PPy) are competitive biomaterials for constructing bioelectronics to interface with biological systems. Synergistic synthesis using lignocellulose nanofibrils (LCNF) as a structural template in chemical oxidation of pyrrole with Fe(III) ions facilitates surface-confined polymerization of pyrrole on the nanofibril surface within a submicrometer- and micrometer-scale fibril length. It yields a core-shell nanocomposite of PPy@LCNF, wherein the surface of each individual fibril is coated with a thin nanoscale layer of PPy. A highly positive surface charge originating from protonated PPy gives this 1D nanomaterial a durable aqueous dispersity. The fibril-fibril entanglement in the PPy@LCNFs facilely supported versatile downstream processing, e.g., spray thin-coating on glass, flexible membranes with robust mechanics, or three-dimensional cryogels. A high electrical conductivity in the magnitude of several to 12 S·cm-1 was confirmed for the solid-form PPy@LCNFs. The PPy@LCNFs are electroactive and show potential cycling capacity, encompassing a large capacitance. Dynamic control of the doping/undoping process by applying an electric field combines electronic and ionic conductivity through the PPy@LCNFs. The low cytotoxicity of the material is confirmed in noncontact cell culture of human dermal fibroblasts. This study underpins the promises for this nanocomposite PPy@LCNF as a smart platform nanomaterial in constructing interfacing bioelectronics.

| S-EPMC10428162 | biostudies-literature

Electrical Stimulation Using Conductive Polymer Polypyrrole Counters Reduced Neurite Outgrowth of Primary Prefrontal Cortical Neurons from NRG1-KO and DISC1-LI Mice.

Project description:Deficits in neurite outgrowth, possibly involving dysregulation of risk genes neuregulin-1 (NRG1) and disrupted in schizophrenia 1 (DISC1) have been implicated in psychiatric disorders including schizophrenia. Electrical stimulation using conductive polymers has been shown to stimulate neurite outgrowth of differentiating human neural stem cells. This study investigated the use of the electroactive conductive polymer polypyrrole (Ppy) to counter impaired neurite outgrowth of primary pre-frontal cortical (PFC) neurons from NRG1-knock out (NRG1-KO) and DISC1-locus impairment (DISC1-LI) mice. Whereas NRG1-KO and DISC1-LI exhibited reduced neurite length and number of neurite branches compared to wild-type controls, this was not apparent for cultures on electroactive Ppy. Additionally, the use of the Ppy substrate normalised the synaptophysin and PSD95 protein and mRNA expression whereas both are usually reduced by NRG1-KO or DISC1-LI. Our findings support the utility of Ppy mediated electrical stimulation to prevent the reduction of neurite outgrowth and related synaptic protein expression in the primary PFC neurons from NRG1-KO and DISC1-LI mice, providing proof-of-concept for treating neurodevelopmental diseases including schizophrenia.

| S-EPMC5309772 | biostudies-literature

Polypyrrole-chitosan conductive biomaterial synchronizes cardiomyocyte contraction and improves myocardial electrical impulse propagation.

Project description:Background: The post-myocardial infarction (MI) scar interrupts electrical impulse propagation and delays regional contraction, which contributes to ventricular dysfunction. We investigated the potential of an injectable conductive biomaterial to restore scar tissue conductivity and re-establish synchronous ventricular contraction. Methods: A conductive biomaterial was generated by conjugating conductive polypyrrole (PPY) onto chitosan (CHI) backbones. Trypan blue staining of neonatal rat cardiomyocytes (CMs) cultured on biomaterials was used to evaluate the biocompatibility of the conductive biomaterials. Ca2+ imaging was used to visualize beating CMs. A cryoablation injury rat model was used to investigate the ability of PPY:CHI to improve cardiac electrical propagation in the injured heart in vivo. Electromyography was used to evaluate conductivity of scar tissue ex vivo. Results: Cell survival and morphology were similar between cells cultured on biomaterials-coated and uncoated-control dishes. PPY:CHI established synchronous contraction of two distinct clusters of spontaneously-beating CMs. Intramyocardial PPY:CHI injection into the cryoablation-induced injured region improved electrical impulse propagation across the scarred tissue and decreased the QRS interval, whereas saline- or CHI-injected hearts continued to have delayed propagation patterns and significantly reduced conduction velocity compared to healthy controls. Ex vivo evaluation found that scar tissue from PPY:CHI-treated rat hearts had higher signal amplitude compared to those from saline- or CHI-treated rat heart tissue. Conclusions: The PPY:CHI biomaterial is electrically conductive, biocompatible and injectable. It improved synchronous contraction between physically separated beating CM clusters in vitro. Intra-myocardial injection of PPY:CHI following cardiac injury improved electrical impulse propagation of scar tissue in vivo.

| S-EPMC5957007 | biostudies-literature

Intrinsic electrical conductivity of nanostructured metal-organic polymer chains.

Project description:One-dimensional conductive polymers are attractive materials because of their potential in flexible and transparent electronics. Despite years of research, on the macro- and nano-scale, structural disorder represents the major hurdle in achieving high conductivities. Here we report measurements of highly ordered metal-organic nanoribbons, whose intrinsic (defect-free) conductivity is found to be 10(4) S m(-1), three orders of magnitude higher than that of our macroscopic crystals. This magnitude is preserved for distances as large as 300 nm. Above this length, the presence of structural defects (~ 0.5%) gives rise to an inter-fibre-mediated charge transport similar to that of macroscopic crystals. We provide the first direct experimental evidence of the gapless electronic structure predicted for these compounds. Our results postulate metal-organic molecular wires as good metallic interconnectors in nanodevices.

| S-EPMC3644075 | biostudies-literature

Solid-state nanostructured materials from self-assembly of a globular protein-polymer diblock copolymer.

Project description:Self-assembly of three-dimensional solid-state nanostructures containing approximately 33% by weight globular protein is demonstrated using a globular protein-polymer diblock copolymer, providing a route to direct nanopatterning of proteins for use in bioelectronic and biocatalytic materials. A mutant red fluorescent protein, mCherryS131C, was prepared by incorporation of a unique cysteine residue and site-specifically conjugated to end-functionalized poly(N-isopropylacrylamide) through thiol-maleimide coupling to form a well-defined model protein-polymer block copolymer. The block copolymer was self-assembled into bulk nanostructures by solvent evaporation from concentrated solutions. Small-angle X-ray scattering and transmission electron microscopy illustrated the formation of highly disordered lamellae or hexagonally perforated lamellae depending upon the selectivity of the solvent during evaporation. Solvent annealing of bulk samples resulted in a transition toward lamellar nanostructures with mCherry packed in a bilayer configuration and a large improvement in long-range ordering. Wide-angle X-ray scattering indicated that mCherry did not crystallize within the block copolymer nanodomains and that the ?-sheet spacing was not affected by self-assembly. Circular dichroism showed no change in protein secondary structure after self-assembly, while UV-vis spectroscopy indicated approximately 35% of the chromophore remained optically active.

| S-EPMC4059825 | biostudies-literature

Nanostructured polymer films with metal-like thermal conductivity.

Project description:Due to their unique properties, polymers - typically thermal insulators - can open up opportunities for advanced thermal management when they are transformed into thermal conductors. Recent studies have shown polymers can achieve high thermal conductivity, but the transport mechanisms have yet to be elucidated. Here we report polyethylene films with a high thermal conductivity of 62 Wm-1 K-1, over two orders-of-magnitude greater than that of typical polymers (~0.1 Wm-1 K-1) and exceeding that of many metals and ceramics. Structural studies and thermal modeling reveal that the film consists of nanofibers with crystalline and amorphous regions, and the amorphous region has a remarkably high thermal conductivity, over ~16 Wm-1 K-1. This work lays the foundation for rational design and synthesis of thermally conductive polymers for thermal management, particularly when flexible, lightweight, chemically inert, and electrically insulating thermal conductors are required.

| S-EPMC6467866 | biostudies-other

Infiltration of biomineral templates for nanostructured polypyrrole.

Project description:Biomineral templates like sea urchin spine, nacre or eggshell were applied in the polymerisation of pyrrole. The insufficient infiltration of pyrrole into the CaCO3 structure of the biomineral templates was improved using three different and universally applicable approaches and the electrochemical properties of the received polypyrrole were examined.

| S-EPMC9086734 | biostudies-literature

Electrical and Thermal and Self-Healing Properties of Graphene-Thermopolyurethane Flexible Conductive Films.

Project description:We fabricated graphene-thermopolyurethane (G-TPU) flexible conductive film by a blending method and systematically investigated the electrical, thermal and self-healing properties of the G-TPU flexible conductive film by infrared light and electricity. The experimental results demonstrate that the G-TPU composite films have good conductivity and thermal conductivity in the appropriate mass content of graphene in the composite film. The composite films have the good electro-thermal and infrared light thermal response performances and electro-thermal response performance is closely related to the mass content of graphene in the composite film, but the infrared light thermal response performance is not. The scratch on the composite film can be completely healed, using electricity or infrared light. The healing efficiency of the composite film healed using infrared light is higher than that of using the electricity, while the healing time of the composite film is shorter. Regardless of the self-healing method, the temperature of the self-healing is a very important factor. The self-healing conductive composite film still exhibits a good conductivity.

| S-EPMC7221931 | biostudies-literature

Polymer Gel with Tunable Conductive Properties: A Material for Thermal Energy Harvesting.

Project description:The spontaneous gelation of poly(4-vinyl pyridine)/pyridine solution produces materials with conductive properties that are suitable for various energy conversion technologies. The gel is a thermoelectric material with a conductivity of 2.2-5.0 × 10-6 S m-1 and dielectric constant ε = 11.3. On the molecular scale, the gel contains various types of hydrogen bonding, which are formed via self-protonation of the pyridine side chains. Our measurements and calculations revealed that the gelation process produces bias-dependent polymer complexes: quasi-symmetric, strongly hydrogen-bonded species, and weakly bound protonated structures. Under an applied DC bias, the gelled complexes differ in their capacitance/conductive characteristics. In this work, we exploited the bias-responsive characteristics of poly(4-vinyl pyridine) gelled complexes to develop a prototype of a thermal energy harvesting device. The measured device efficiency is S = ΔV/ΔT = 0.18 mV/K within the temperature range of 296-360 K. Investigation of the mechanism underlying the conversion of thermal energy into electric charge showed that the heat-controlled proton diffusion (the Soret effect) produces thermogalvanic redox reactions of hydrogen ions on the anode. The charge can be stored in an external capacitor for heat energy harvesting. These results advance our understanding of the molecular mechanisms underlying thermal energy conversion in the poly(4-vinyl pyridine)/pyridine gel. A device prototype, enabling thermal energy harvesting, successfully demonstrates a simple path toward the development of inexpensive, low-energy thermoelectric generators.

| S-EPMC9798393 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data