Biocompatible, degradable thermoplastic polyurethane based on polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone copolymers for soft tissue engineering.

ABSTRACT: Biodegradable synthetic polymers have been widely used as tissue engineering scaffold materials. Even though they have shown excellent biocompatibility, they have failed to resemble the low stiffness and high elasticity of soft tissues because of the presence of massive rigid ester bonds. Herein, we synthesized a new thermoplastic polyurethane elastomer (CTC-PU(BET)) using poly ester ether triblock copolymer (polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone triblock copolymer, PCTC) as the soft segment, aliphatic diisocyanate (hexamethylene diisocyanate, HDI) as the hard segment, and degradable diol (bis(2-hydroxyethyl) terephthalate, BET) as the chain extender. PCTC inhibited crystallization and reduced the melting temperature of CTC-PU(BET), and BET dramatically enhanced the thermal decomposition and hydrolytic degradation rate when compared with conventional polyester-based biodegradable TPUs. The CTC-PU(BET) synthesized in this study possessed a low tensile modulus and tensile strength of 2.2 MPa and 1.3 MPa, respectively, and an elongation-at-break over 700%. Meanwhile, it maintained a 95.3% recovery rate and 90% resilience over ten cycles of loading and unloading. In addition, the TPU could be electrospun into both random and aligned fibrous scaffolds consisting of major microfibers and nanobranches. 3T3 fibroblast cell culture confirmed that these scaffolds outperformed the conventional biodegradable TPU scaffolds in terms of substrate-cellular interactions and cell proliferation. Considering the advantages of this TPU, such as ease of synthesis, low cost, low stiffness, high elasticity, controllable degradation rate, ease of processability, and excellent biocompatibility, it has great prospects to be used as a tissue engineering scaffold material for soft tissue regeneration.

SUBMITTER: Mi HY

PROVIDER: S-EPMC5695921 | biostudies-literature | 2017 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Biocompatible, degradable thermoplastic polyurethane based on polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone copolymers for soft tissue engineering.

Mi Hao-Yang HY Jing Xin X Napiwocki Brett N BN Hagerty Breanna S BS Chen Guojun G Turng Lih-Sheng LS

Journal of materials chemistry. B 20170501 22

Biodegradable synthetic polymers have been widely used as tissue engineering scaffold materials. Even though they have shown excellent biocompatibility, they have failed to resemble the low stiffness and high elasticity of soft tissues because of the presence of massive rigid ester bonds. Herein, we synthesized a new thermoplastic polyurethane elastomer (CTC-PU(BET)) using poly ester ether triblock copolymer (polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone triblock copolymer, P ...[more]

PMID: 29170715

Similar Datasets

Project description:Thermoplastic elastomers (TPEs) that are closed-loop recyclable are needed in a circular material economy, but many current materials degrade during recycling, and almost all are pervasive hydrocarbons. Here, well-controlled block polyester TPEs featuring regularly placed sodium/lithium carboxylate side chains are described. They show significantly higher tensile strengths than unfunctionalized analogues, with high elasticity and elastic recovery. The materials are prepared using controlled polymerizations, exploiting a single catalyst that switches between different polymerization cycles. ABA block polyesters of high molar mass (60-100 kg mol-1; 21 wt % A-block) are constructed using the ring-opening polymerization of ε-decalactone (derived from castor oil; B-block), followed by the alternating ring-opening copolymerization of phthalic anhydride with 4-vinyl-cyclohexene oxide (A-blocks). The polyesters undergo efficient functionalization to install regularly placed carboxylic acids onto the A blocks. Reacting the polymers with sodium or lithium hydroxide controls the extent of ionization (0-100%); ionized polymers show a higher tensile strength (20 MPa), elasticity (>2000%), and elastic recovery (>80%). In one case, sodium functionalization results in 35× higher stress at break than the carboxylic acid polymer; in all cases, changing the quantity of sodium tunes the properties. A leading sample, 2-COONa75 (M n 100 kg mol-1, 75% sodium), shows a wide operating temperature range (-52 to 129 °C) and is recycled (×3) by hot-pressing at 200 °C, without the loss of mechanical properties. Both the efficient synthesis of ABA block polymers and precision ionization in perfectly alternating monomer sequences are concepts that can be generalized to many other monomers, functional groups, and metals. These materials are partly bioderived and have degradable ester backbone chemistries, deliver useful properties, and allow for thermal reprocessing; these features are attractive as future sustainable TPEs.

Dataset Information

Biocompatible, degradable thermoplastic polyurethane based on polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone copolymers for soft tissue engineering.

Publications

Biocompatible, degradable thermoplastic polyurethane based on polycaprolactone-block-polytetrahydrofuran-block-polycaprolactone copolymers for soft tissue engineering.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets