Thae use of microfluic spinning fiber as an ophthalmology suture showing the good anastomotic strength control.

ABSTRACT: Adjusting the mechanical strength of a biomaterial to suit its intended application is very important for realizing beneficial outcomes. Microfluidic spinning fiber have been attracting attention recently due to their various advantages, but their mechanical strength has unfortunately not been a subject of concentrated research, and this lack of research has severely limited their applications. In the current work, we showed the mechanical properties of microfibers can be tuned easily and provided a mathematical explanation for how the microfluidic spinning method intrinsically controls the mechanical properties of a microfluidic spinning fiber. But we were also able to adjust the mechanical properties of such fibers in various other ways, including by using biomolecules to coat the fiber or mixing the biomolecules with the primary component of the fiber and by using a customized twisting machine to change the number of single microfiber strands forming the fiber. We used the bundle fiber as an ophthalmology suture that resulted in a porcine eye with a smoother post-operative surface than did a nylon suture. The results showed the possibility that the proposed method can solve current problems of the microfibers in practical applications, and can thus extend the range of applications of these microfibers.

SUBMITTER: Park D

PROVIDER: S-EPMC5701120 | biostudies-literature | 2017 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Thae use of microfluic spinning fiber as an ophthalmology suture showing the good anastomotic strength control.

Park DoYeun D Yong In Sung IS Cho Kyong Jin KJ Cheng Jie J Jung Youngmee Y Kim Soo Hyun SH Lee Sang-Hoon SH

Scientific reports 20171124 1

Adjusting the mechanical strength of a biomaterial to suit its intended application is very important for realizing beneficial outcomes. Microfluidic spinning fiber have been attracting attention recently due to their various advantages, but their mechanical strength has unfortunately not been a subject of concentrated research, and this lack of research has severely limited their applications. In the current work, we showed the mechanical properties of microfibers can be tuned easily and provid ...[more]

PMID: 29176617

Similar Datasets

Project description:PurposeTo assess the mechanical properties, tendon resistance to suture cutout, and knot size of a broad variety of high-strength sutures and tapes available for arthroscopic rotator cuff repair.MethodsNine different types of high-strength sutures and tapes for arthroscopic rotator cuff repair were studied: 6 were tapes (FiberTape, Hi-Fi Tape, Permatape, SutureTape, UltraTape, and XBraid TT), and 3 were sutures (Dynacord, FiberWire, and Ultrabraid). First, mechanical tensile testing of suture loops (n = 6) was performed. Second, the suture material was passed through an intact human cadaveric rotator cuff tendon (supraspinatus or infraspinatus), and cyclic as well as load-to-failure testing was performed, 8 times for each suture or tape. Statistical analysis of groups (tapes vs sutures) and between each suture and each tape was performed.ResultsMaterial testing revealed significant differences with superior mechanical properties of tapes compared with sutures regarding load for 3 mm of displacement (201 N vs 84 N, P < .0001), displacement at 200 N (3.6 mm vs 6.6 mm, P < .0001), stiffness (46 N/mm vs 25 N/mm, P < .0001), and ultimate load to failure (509 N vs 288 N, P < .0001). FiberTape showed the highest ultimate load to failure (805.5 ± 36.1 N), the highest load necessary for 3 mm of displacement (376.2 ± 19.1 N), and the lowest displacement at a 200-N load (2 ± 0.1 mm). Permatape had the highest stiffness (58.5 ± 5.3 N/mm). FiberTape had the highest knot height (9.5 ± 1.3 mm) and knot width (3.8 ± 0.7 mm) of a suture loop with 7 square knots. The typical failure mode in the cadaveric study part was tendon cut through.ConclusionsBiomechanical in vitro testing showed that high-strength suture tapes compared with regular high-strength sutures have significantly better mechanical properties in both dry-laboratory testing and human cadaveric rotator cuff tendon pullout testing. FiberTape outperformed the other tapes and the sutures used in this analysis. Nonetheless, differences in tendon testing appeared to be less substantial than in dry-laboratory testing, and FiberTape had the highest knot height and width.Clinical relevanceFiberTape revealed the most favorable biomechanical performance in dry-laboratory and rotator cuff tendon testing. It may provide the best repair strength in vivo; however, it also has the largest knot size.

Dataset Information

Thae use of microfluic spinning fiber as an ophthalmology suture showing the good anastomotic strength control.

Publications

Thae use of microfluic spinning fiber as an ophthalmology suture showing the good anastomotic strength control.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets