ABSTRACT: Fluoropolymer nanocomposites of poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) were prepared using fluorinated barium strontium titanate (Ba1-xSrxTiO3, BSTO) nanoparticles (NPs) by low-temperature synthesis using a modified liquid-solid solution process. The exact stoichiometry of as-synthesized BSTO NPs was confirmed by X-ray diffraction analysis along with lattice parameter calculations. The synthesized BSTO NPs were fluorinated using 2,2,2-trifluoroacetic acid as a fluorous ligand. The BSTO NPs showed high solubility in the fluorous system (polymer and solvent) on account of their modified surface. The root-mean-square roughness of the fluorinated BSTO/PVdF-HFP nanocomposite was 76 times lower than that of the nonfluorinated BSTO/PVdF-HFP nanocomposite. The dielectric constant of the fluorinated BSTO/PVdF-HFP nanocomposite exhibited Curie temperature behavior. The dielectric constant of the nanocomposite predicted using the modified Kerner model at room temperature agreed well with the experimental values.

SUBMITTER: Han W

PROVIDER: S-EPMC5840133 | biostudies-literature | 2018 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Tunable Dielectric Properties of Poly(vinylidenefluoride-co-hexafluoropropylene) Films with Embedded Fluorinated Barium Strontium Titanate Nanoparticles.

Han Wooje W Kim Taehee T Yoo Byungwook B Park Hyung-Ho HH

Scientific reports 20180306 1

Fluoropolymer nanocomposites of poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) were prepared using fluorinated barium strontium titanate (Ba1-xSrxTiO3, BSTO) nanoparticles (NPs) by low-temperature synthesis using a modified liquid-solid solution process. The exact stoichiometry of as-synthesized BSTO NPs was confirmed by X-ray diffraction analysis along with lattice parameter calculations. The synthesized BSTO NPs were fluorinated using 2,2,2-trifluo ...[more]

PMID: 29511304

Similar Datasets

Project description:Nitric oxide (NO) releasing polymers have been widely applied as biomaterials for a variety of biomedical implants and devices. However, the chemical leaching of NO donors and their byproduct species is almost always observed during the application of polymers doped with NO donors, unless the donor is covalently linked to the polymer. Herein, we report the first NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluorinated copolymer prepared by incorporating a fluorinated S-nitrosothiol as the NO donor. Under physiological conditions, the resulting polymeric films can release NO for 16?days. Importantly, due to both fluorine-fluorine and electrostatic charge interactions between the fluorinated NO donor and the PVDF-HFP copolymer, the total chemical leaching of the fluorinated NO donor and its disulfide product after 9?day was only 0.6% (mol%) of the initial amount of NO donor loaded into the film. These new NO release PVDF-HFP films exhibit antimicrobial and anti-biofilm activities against both Gram positive S. aureus and Gram negative P. aeruginosa strains. The NO-releasing PVDF-HFP polymer can also be coated on Teflon tubing to release NO under physiological conditions for extended time periods. This NO-releasing PVDF-HFP copolymer with greatly reduced chemical leaching could help enhance the biocompatibility and antimicrobial activity of various biomedical devices. STATEMENT OF SIGNIFICANCE: Fluoropolymers have been widely used in creating various biomedical implants and devices. However, nitric oxide (NO) release fluoropolymers have not been well studied to date. Additionally, in the application of biomaterials doped with NO donors, a significant amount of NO donors and their byproducts almost always leach into aqueous environment. We now report an NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluoropolymer by incorporating a new fluorinated S-nitrosothiol. The NO release can last for 16?days under physiological conditions. The total chemical leaching was determined to be only 0.6?mol% of the initial S-nitrosothiol loaded. As expected, significant antimicrobial/anti-biofilm activities of the NO release PVDF-HFP film were observed against Gram positive S. aureus and Gram negative P. aeruginosa bacterial strains.

Dataset Information

Tunable Dielectric Properties of Poly(vinylidenefluoride-co-hexafluoropropylene) Films with Embedded Fluorinated Barium Strontium Titanate Nanoparticles.

Publications

Tunable Dielectric Properties of Poly(vinylidenefluoride-co-hexafluoropropylene) Films with Embedded Fluorinated Barium Strontium Titanate Nanoparticles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets