The formation of (NiFe)S2 pyrite mesocrystals as efficient pre-catalysts for water oxidation.

ABSTRACT: Designing intricate structures and searching for functional materials has attracted wide interest in nanoscience. Herein we have fabricated (NiFe)S2 pyrite mesocrystals in the form of nearly-single crystalline porous cubes, and studied their self-optimization to realize efficient activity toward water oxidation under electrochemical conditions. The growth mechanism of the mesocrystals was a non-classical mechanism, which was initiated by the formation of a large quantity of small nickel sulfide clusters, followed by the aggregation and transformation of these small clusters in an oriented manner. When these mesocrystals were tested for water oxidation under electrocatalytic conditions, the materials served as pre-catalysts and immediately self-optimized to form amorphous S-doped metal (oxy)hydroxides, which are the real catalytically active materials. As a result, the observed overpotential to reach a current density of 10 mA cm-2 on glassy carbon electrodes was less than 260 mV. The growth mechanism studied here may provide opportunities for constructing intricate sulfide structures, and the self-optimization process during water oxidation can inspire new thoughts on electrocatalysis.

SUBMITTER: Ni B

PROVIDER: S-EPMC5914147 | biostudies-literature | 2018 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The formation of (NiFe)S<sub>2</sub> pyrite mesocrystals as efficient pre-catalysts for water oxidation.

Ni Bing B He Ting T Wang Jia-Ou JO Zhang Simin S Ouyang Chen C Long Yong Y Zhuang Jing J Wang Xun X

Chemical science 20180201 10

Designing intricate structures and searching for functional materials has attracted wide interest in nanoscience. Herein we have fabricated (NiFe)S<sub>2</sub> pyrite mesocrystals in the form of nearly-single crystalline porous cubes, and studied their self-optimization to realize efficient activity toward water oxidation under electrochemical conditions. The growth mechanism of the mesocrystals was a non-classical mechanism, which was initiated by the formation of a large quantity of small nick ...[more]

PMID: 29732061

Similar Datasets

Project description:Layered double hydroxides (LDHs) are an ideal platform to host catalytic metal centers for water oxidation (WO) owing to the high accessibility of water to the interlayer region, which makes all centers potentially reachable and activated. Herein, we report the syntheses of three iridium-doped zinc-aluminum LDHs (Ir-LDHs) nanomaterials (1-3, with about 80 nm of planar size and a thickness of 8 nm as derived by field emission scanning electron microscopy and powder X-ray diffraction studies, respectively), carried out in the confined aqueous environment of reverse micelles, through a very simple and versatile procedure. These materials exhibit excellent catalytic performances in WO driven by NaIO4 at neutral pH and 25 °C, with an iridium content as low as 0.5 mol % (∼0.8 wt %), leading to quantitative oxygen yields (based on utilized NaIO4, turnover number up to ∼10,000). Nanomaterials 1-3 display the highest ever reported turnover frequency values (up to 402 min-1) for any heterogeneous and heterogenized catalyst, comparable only to those of the most efficient molecular iridium catalysts, tested under similar reaction conditions. The boost in activity can be traced to the increased surface area and pore volume (>5 times and 1 order of magnitude, respectively, higher than those of micrometric materials of size 0.3-1 μm) estimated for the nanosized particles, which guarantee higher noble metal accessibility. X-ray absorption spectroscopy (XAS) studies suggest that 1-3 nanomaterials, as-prepared and after catalysis, contain a mixture of isolated, single octahedral Ir(III) sites, with no evidence of Ir-Ir scattering from second-nearest neighbors, excluding the presence of IrO2 nanoparticles. The combination of the results obtained from XAS, elemental analysis, and ionic chromatography strongly suggests that iridium is embedded in the brucite-like structure of LDHs, having four hydroxyls and two chlorides as first neighbors. These results demonstrate that nanometric LDHs can be successfully exploited to engineer efficient WOCs, minimizing the amount of iridium used, consistent with the principle of the noble-metal atom economy.

Project description:Four heterotrinuclear complexes containing the ligands 3,5-bis(2-pyridyl)pyrazolate (bpp-) and 2,2':6',2''-terpyridine (trpy) of the general formula {[RuII(trpy)]2(μ-[M(X)2(bpp)2])}(PF6)2, where M = CoII, MnII and X = Cl-, AcO- (M = CoII, X = Cl-: Ru2Co-Cl2 ; M = MnII, X = Cl-: Ru2Mn-Cl2 ; M = CoII, X = AcO-: Ru2Co-OAc2 ; M = MnII, X = AcO-: Ru2Mn-OAc2 ), have been prepared for the first time. The complexes have been characterized using different spectroscopic techniques such as UV-vis, IR, and mass spectrometry. X-Ray diffraction analyses have been used to characterize the Ru2Mn-Cl2 and Ru2Mn-OAc2 complexes. The cyclic voltammograms (CV) for all four complexes in organic solvent (CH3CN or CH2Cl2) display three successive reversible oxidative waves corresponding to one-electron oxidations of each of the three metal centers. The oxidized forms of the complexes Ru2Co-OAc2 and Ru2Mn-OAc2 are further characterized by EPR and UV-vis spectroscopy. The magnetic susceptibility measurements of all complexes in the temperature range of 2-300 K reveal paramagnetic properties due to the presence of high spin Co(ii) and Mn(ii) centers. The complexes Ru2Co-OAc2 and Ru2Mn-OAc2 act as precatalysts for the water oxidation reaction, since the acetato groups are easily replaced by water at pH = 7 generating the active catalysts, {[Ru(H2O)(trpy)]2(μ-[M(H2O)2(bpp)2])}4+ (M = CoII: Ru2Co-(H2O)4 ; M = MnII: Ru2Mn-(H2O)4 ). The photochemical water oxidation reaction is studied using [Ru(bpy)3]2+ as the photosensitizer and Na2S2O8 as a sacrificial electron acceptor at pH = 7. The Co containing complex generates a TON of 50 in about 10 minutes (TOFi = 0.21 s-1), whereas the Mn containing complex only generates a TON of 8. The water oxidation reaction of Ru2Co-(H2O)4 is further investigated using oxone as a sacrificial chemical oxidant at pH = 7. Labelled water oxidation experiments suggest that a nucleophilic attack mechanism is occurring at the Co site of the trinuclear complex with cooperative involvement of the two Ru sites, via electronic coupling through the bpp- bridging ligand and via neighboring hydrogen bonding.

Dataset Information

The formation of (NiFe)S2 pyrite mesocrystals as efficient pre-catalysts for water oxidation.

Publications

The formation of (NiFe)S<sub>2</sub> pyrite mesocrystals as efficient pre-catalysts for water oxidation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets