2H-NbS2 film as a novel counter electrode for meso-structured perovskite solar cells.

ABSTRACT: We report the use of 2H-NbS2 film as a novel counter electrode in perovskite solar cells fabricated with a cold isostatic pressing method. The 2H-NbS2 film, which was prepared through an exfoliation method followed by restacking from LixNbS2 powder, shows high electrical conductivity of 8.7?×?103?S?cm-1 and work function of 5.20?eV. The two-dimensional transition metal dichalcogenide was used for the first time as a counter electrode in meso-structured perovskite solar cells. Through this process, we demonstrated a new alternative to noble metals. The perovskite solar cell base on the 2H-NbS2 counter electrode showed an open-circuit voltage of 1.046?V, comparable to that of gold, and a power conversion efficiency of 8.3%.

SUBMITTER: Shao F

PROVIDER: S-EPMC5935697 | biostudies-literature | 2018 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

2H-NbS2 film as a novel counter electrode for meso-structured perovskite solar cells.

Shao Feng F Tian Zhangliu Z Qin Peng P Bu Kejun K Zhao Wei W Xu Li L Wang Deliang D Huang Fuqiang F

Scientific reports 20180504 1

We report the use of 2H-NbS2 film as a novel counter electrode in perovskite solar cells fabricated with a cold isostatic pressing method. The 2H-NbS2 film, which was prepared through an exfoliation method followed by restacking from LixNbS2 powder, shows high electrical conductivity of 8.7 × 103 S cm-1 and work function of 5.20 eV. The two-dimensional transition metal dichalcogenide was used for the first time as a counter electr ...[more]

PMID: 29728660

Similar Datasets

Project description:As the essential component of a quantum dot-sensitized solar cell (QDSC), the counter electrode (CE) plays an important role in electron transfer and catalytic reduction acquisition throughout the device. A novel route to design multilayer functionalized Cu2S thin films as CEs with high catalytic activity and enhanced stability, as well as large specific surface area and high conductivity, is presented. Firstly, Mo-based films were prepared by magnetron sputtering on a glass substrate, and then porous CuZnMo conductive films were formed by etching with hydrochloric acid. Secondly, indium tin oxide (ITO) film was sputtered onto the porous structure to act as a protective layer, and a porous ITO/CuZnMo structured film was obtained after optimization. In the third step, multilayer Cu(x)/ITO/CuZnMo structured films were acquired by sputtering Cu films. Finally, multilayer Cu2S(t)/ITO/CuZnMo functionalized film CEs were obtained via in situ sulfidation of sputtered Cu films. The functions of conduction and resistance to electrolyte corrosion were produced and enhanced by annealing an ITO layer at high temperature prior to Cu deposition, while catalytic activity enabled by Cu2S was realized from Cu film sulfidation. The multilayer Cu2S/ITO(500 °C)/CuZnMo functionalized films exhibit high catalytic activity and enhanced stability for resistance to electrolyte corrosion. Taking multilayer Cu2S/ITO(500 °C)/CuZnMo films as CEs, the QDSCs demonstrated good stability of power conversion efficiency (PCE) after 500 h of irradiation, from an initial 4.21% to a final 4.00%. Furthermore, the thickness of Cu2S film modulated by the duration of Cu sputtering was investigated. It was found that the QDSCs using multilayer Cu2S(40 min)/ITO/CuZnMo functionalized film with a Cu2S thickness of 1.2 μm as CE exhibit the best performance, and the R ct value was 0.57 Ω. The best photovoltaic performance with a PCE of 5.21% (V oc = 533.1 mV, J sc = 18.80 mA cm-2, FF = 52.84%) was achieved under AM 1.5 radiation with an incident power of 100 mW cm-2. This design of a multilayer functionalized CE introduces potential alternatives to the common brass-based CE for long-term QDSCs with high performance.

Dataset Information

2H-NbS2 film as a novel counter electrode for meso-structured perovskite solar cells.

Publications

2H-NbS<sub>2</sub> film as a novel counter electrode for meso-structured perovskite solar cells.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets