Mechanically Robust and Thermally Stable Colorful Superamphiphobic Coatings.

ABSTRACT: Colorful super anti-wetting coatings are receiving growing attention, but are challenging to invent. Here, we report a general method for preparing mechanically robust and thermally stable colorful superamphiphobic coatings. A composite of palygorskite (PAL) nanorods and iron oxide red (IOR) was prepared by solid-state grinding or hydrothermal reaction, which was then modified by hydrolytic condensation of silanes to form a suspension. Superamphiphobic coatings were prepared by spray-coating the suspension onto substrates. The superamphiphobicity depends upon the surface microstructure and chemical composition, which are controllable by the PAL/IOR concentration and the solid-state grinding time. The colorful coatings show excellent superamphiphobicity with high contact angles and low sliding angles for water and various organic liquids of low surface tension, e.g., toluene and n-decane. The coatings also feature high mechanical, chemical and thermal stability, which is superior to all the reported colorful super anti-wetting coatings. Moreover, superamphiphobic coatings of different colors can be prepared via the same procedure using the other metal oxides instead of IOR. We believe the colorful superamphiphobic coatings may find applications in many fields like anti-climbing of oils and restoration of cultural relics, as the coatings are applicable onto various substrates.

SUBMITTER: Tian N

PROVIDER: S-EPMC5936788 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thermally-Conductive and Mechanically-Robust Graphene Nanoplatelet Reinforced UO2 Composite Nuclear Fuels.

Project description:Low thermal transport behavior along the radial direction of nuclear fuel pellets and pellet-cladding mechanical interaction significantly impact fuel performance and the safety of current nuclear energy systems. Here we report a new strategy of advanced fuel design in which highly thermally-conductive and mechanically-robust graphene nanoplatelets are incorporated into UO2 fuel matrix to improve fuel thermal-mechanical properties. The 2D geometry of the graphene nanoplatelets enables a unique lamellar structure upon fuel consolidation by spark plasma sintering. The thermal conductivity along the radial direction of the sintered fuel pellets at room temperature reaches 12.7 and 19.1 wm-1K-1 at 1 wt.% and 5 wt.% loadings of the graphene nanoplatelets, respectively, representing at least 74% and 162% enhancements as compared to pure UO2 fuel pellets. Indentation testing suggests great capability of the 2D graphene nanoplatelets to deflect and pin crack propagation, drastically improving the crack propagation resistance of fuel matrix. The estimated indentation fracture toughness reaches 3.5 MPa·m1/2 by 1 wt.% loading of graphene nano-platelets, representing a 150% improvement over 1.4 MPa·m1/2 for pure UO2 fuel pellets. Isothermal annealing of the composite fuel indicates that the graphene nano-platelet is able to retain its structure and properties against reaction with UO2 matrix up to 1150 °C.

| S-EPMC5812999 | biostudies-literature

Biomimetic Super Anti-Wetting Coatings from Natural Materials: Superamphiphobic Coatings Based on Nanoclays.

Project description:Superamphiphobic coatings (SAPCs) that resist wetting of water and low-surface-tension liquids have generated widespread attention in academia, but are very challenging to invent. Liquid adhesion, low stability, complicated and expensive preparation methods are the typical characteristics of SAPCs, which seriously hinder real-world applications of SAPCs. Here, we report a comprehensive study about preparation of SAPCs from abundant nanoclays with fibrous, plate-like and porous microstructures. The SAPCs are prepared simply by hydrolytic condensation of silanes in the presence of nanoclays, followed by spray-coating the as-formed suspensions onto substrates. The SAPCs feature high superamphiphobicity for various liquids down to a surface tension of 23.8 mN m-1 (n-decane), and high mechanical, chemical and thermal stability. The superamphiphobicity and stability depend on microscale and nanoscale surface morphology of the coatings, which are controllable by the microstructures of nanoclays and their acid activation. The fibrous nanoclays with moderate aspect ratio like palygorskite are the most suitable building blocks for the preparation of SAPCs by effectively forming the reentrant surface morphology. We believe that the findings will promote the progress of SAPCs, and pave the way for the development of clay-based super anti-wetting coatings.

| S-EPMC6089923 | biostudies-literature

Waterborne superamphiphobic coatings with network structure for enhancing mechanical durability.

Project description:Superamphiphobic coatings may significantly change the wettability of a substrate, and so are attractive for applications in aero/marine engineering, biotechnology, and heat transfer. However, the coatings are caught in a double bind when their durability is considered, as they are vulnerable to mechanical abrasion. Meanwhile, the wide use of organic solvents for preparing the coatings generates environmental pollution. Here, we present a waterborne superamphiphobic coating through one-step spraying that repels a wide range of liquids. By tailoring the repellence of the nano-silica to waterborne resin, a network structure is constructed to protect the embedded nano-silica from damage. Thus, the coatings are durable against 725 cycles of friction tester abrasion under a load of 250 g, showing a significant improvement in the mechanical durability by 3-25 times. Moreover, our coating also shows excellent comprehensive durability, including resistance to oil-flow erosion, falling sand impact, chemical attack, thermal treatment, etc. This strategy can be introduced to various waterborne resins, demonstrating its universality, and may offer a new insight to design sustainable superamphiphobic coatings for long-term practical applications.

| S-EPMC9168828 | biostudies-literature

Sorting Liquid Droplets by Surface Tension Using Devices with Quasi-Superamphiphobic Coatings.

Project description:Any solid surface with homogenous or varying surface energy can spontaneously show variable wettability to liquid droplets with different or identical surface tensions. Here, we studied a glass slide sprayed with a quasi-superamphiphobic coating consisting of a hexane suspension of perfluorosilane-coated nanoparticles. Four areas on the glass slide with a total length of 7.5 cm were precisely tuned via ultraviolet (UV) irradiation, and droplets with surface tensions of 72.1-33.9 mN m-1 were categorized at a tilting angle of 3°. Then, we fabricated a U-shaped device sprayed with the same coating and used it to sort the droplets more finely by rolling them in the guide groove of the device to measure their total rolling time and distance. We found a correlation between ethanol content/surface tension and rolling time/distance, so we used the same device to estimate the alcoholic strength of Chinese liquors and to predict the surface tension of ethanol aqueous solutions.

| S-EPMC7240524 | biostudies-literature

The Waterborne Superamphiphobic Coatings with Antifouling, High Temperature Resistance, and Corrosion Resistance.

Project description:Water-based superamphiphobic coatings are environment-friendly, which have attracted tremendous attention recently, but the performances are severely limited by the dispersibility of hydrophobic particles. To solve the poor dispersibility of modified silica powder with hydrophobicity, silica dispersion was blended with polytetrafluoroethylene (PTFE) emulsion and modified aluminum tripolyphosphate (ATP) dispersion to successfully prepare water-based coatings. Multifunctional coatings were prepared by one-step spraying. It possessed good adhesion (grade 1), excellent antifouling, impact resistance, chemical stability (acid and alkali resistance for 96 h of immersion), and corrosion resistance (3.5 wt % NaCl solutions for 20 days). More importantly, the superamphiphobic coatings had high contact angles (CAs) and low slide angles (SAs) for ethylene glycol (CAs = 154 ± 0.8°; SAs = 13 ± 0.7°) and water (CAs = 158 ± 0.7°; SAs = 4 ± 0.3°). Furthermore, the composite coating was still hydrophobic after 35 cycles of wear with high roughness sandpaper (120 mesh) under three different loads, which maintained superamphiphobicity at 425 °C. This work is expected to provide a facile idea and method for the preparation of waterborne superamphiphobic coatings.

| S-EPMC10116617 | biostudies-literature

Superamphiphobic coatings based on liquid-core microcapsules with engineered capsule walls and functionality.

Project description:Microcapsules with specific functional properties, related to the capsule wall and core, are highly desired in a number of applications. In this study, hybrid cellulose microcapsules (1.2 ± 0.4 µm in diameter) were prepared by nanoengineering the outer walls of precursor capsules. Depending on the preparation route, capsules with different surface roughness (raspberry or broccoli-like), and thereby different wetting properties, could be obtained. The tunable surface roughness was achieved as a result of the chemical and structural properties of the outer wall of a precursor capsule, which combined with a new processing route allowed in-situ formation of silica nanoparticles (30-40 nm or 70 nm in diameter). By coating glass slides with "broccoli-like" microcapsules (30-40 nm silica nanoparticles), static contact angles above 150° and roll-off angles below 6° were obtained for both water and low surface-tension oil (hexadecane), rendering the substrate superamphiphobic. As a comparison, coatings from raspberry-like capsules were only strongly oleophobic and hydrophobic. The liquid-core of the capsules opens great opportunities to incorporate different functionalities and here hydrophobic superparamagnetic nanoparticles (SPIONs) were encapsulated. As a result, magnetic broccoli-like microcapsules formed an excellent superamphiphobic coating-layer on a curved geometry by simply applying an external magnetic field.

| S-EPMC5832152 | biostudies-literature

Effect of Incorporated ZnO Nanoparticles on the Corrosion Performance of SiO2 Nanoparticle-Based Mechanically Robust Epoxy Coatings.

Project description:This paper presents the studies of the development of a high-performance epoxy coating for steel substrates. To this end, it investigated the synergistic effect of incorporating zinc oxide (ZnO) nanoparticles into nanosilica containing epoxy formulations. The mechanical properties of the epoxy coating formulations were improved by modifying the surfaces of the silica nanoparticles (5 wt.%) with 3-glycidoxypropyl trimethoxysilane, which ensured their dispersal through the material. Next, the ZnO nanoparticles (1, 2, or 3 wt.%) were incorporated to improve the corrosion performance of the formulations. The anticorrosive properties of the coatings were examined by electrochemical impedance spectroscopy (EIS) of coated mild steel specimens immersed in 3.5% NaCl solution over different time intervals (1 h to 30 days). Incorporation of the ZnO nanoparticles and the nanosilica into the coating formulation improved the corrosion resistance of the epoxy coating even after long-term exposure to saline test solutions. Finally, to evaluate how the nanoparticles affected the chemical and morphological properties of the prepared coatings, the coatings were characterized by scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, and X-ray diffraction (XRD).

| S-EPMC7504416 | biostudies-literature

Inhibiting Bacterial Adhesion by Mechanically Modulated Microgel Coatings.

Project description:Bacterial infection is a severe problem especially when associated with biomedical applications. This study effectively demonstrates that poly- N-isopropylmethacrylamide based microgel coatings prevent bacterial adhesion. The coating preparation via a spraying approach proved to be simple and both cost and time efficient creating a homogeneous dense microgel monolayer. In particular, the influence of cross-linking density, microgel size, and coating thickness was investigated on the initial bacterial adhesion. Adhesion of Staphylococcus aureus ATCC 12600 was imaged using a parallel plate flow chamber setup, which gave insights in the number of the total bacteria adhering per unit area onto the surface and the initial bacterial deposition rates. All microgel coatings successfully yielded more than 98% reduction in bacterial adhesion. Bacterial adhesion depends both on the cross-linking density/stiffness of the microgels and on the thickness of the microgel coating. Bacterial adhesion decreased when a lower cross-linking density was used at equal coating thickness and at equal cross-linking density with a thicker microgel coating. The highest reduction in the number of bacterial adhesion was achieved with the microgel that produced the thickest coating ( h = 602 nm) and had the lowest cross-linking density. The results provided in this paper indicate that microgel coatings serve as an interesting and easy applicable approach and that it can be fine-tuned by manipulating the microgel layer thickness and stiffness.

| S-EPMC6335679 | biostudies-literature

Thermally Stable, Latent Olefin Metathesis Catalysts.

Project description:Highly thermally stable N-aryl,N-alkyl N-heterocyclic carbene (NHC) ruthenium catalysts were designed and synthesized for latent olefin metathesis. These catalysts showed excellent latent behavior toward metathesis reactions, whereby the complexes were inactive at ambient temperature and initiated at elevated temperatures, a challenging property to achieve with second generation catalysts. A sterically hindered N-tert-butyl substituent on the NHC ligand of the ruthenium complex was found to induce latent behavior toward cross-metathesis reactions, and exchange of the chloride ligands for iodide ligands was necessary to attain latent behavior during ring-opening metathesis polymerization (ROMP). Iodide-based catalysts showed no reactivity toward ROMP of norbornene-derived monomers at 25 °C, and upon heating to 85 °C gave complete conversion of monomer to polymer in less than 2 hours. All of the complexes were very stable to air, moisture, and elevated temperatures up to at least 90 °C, and exhibited a long catalyst lifetime in solution at elevated temperatures.

| S-EPMC3263927 | biostudies-literature

Stable Thermally-Modulated Nanodroplet Ultrasound Contrast Agents.

Project description:Liquid perfluorocarbon-based nanodroplets are stable enough to be used in extravascular imaging, but provide limited contrast enhancement due to their small size, incompressible core, and small acoustic impedance mismatch with biological fluids. Here we show a novel approach to overcoming this limitation by using a heating-cooling cycle, which we will refer to as thermal modulation (TM), to induce echogenicity of otherwise stable but poorly echogenic nanodroplets without triggering a transient phase shift. We apply thermal modulation to high-boiling point tetradecafluorohexane (TDFH) nanodroplets stabilized with a bovine serum albumin (BSA) shell. BSA-TDFH nanodroplets with an average diameter under 300 nanometers showed an 11.9 ± 5.4 mean fold increase in echogenicity on the B-mode and a 13.9 ± 6.9 increase on the nonlinear contrast (NLC) mode after thermal modulation. Once activated, the particles maintained their enhanced echogenicity (p < 0.001) for at least 13 h while retaining their nanoscale size. Our data indicate that thermally modulated nanodroplets can potentially serve as theranostic agents or sensors for various applications of contrast-enhanced ultrasound.

| S-EPMC8469504 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data