Cu/Cu2O nanocomposite films as a p-type modified layer for efficient perovskite solar cells.

ABSTRACT: Cu/Cu2O films grown by ion beam sputtering were used as p-type modified layers to improve the efficiency and stability of perovskite solar cells (PSCs) with an n-i-p heterojunction structure. The ratio of Cu to Cu2O in the films can be tuned by the oxygen flow ratio (O2/(O2 + Ar)) during the sputtering of copper. Auger electron spectroscopy was performed to determine the elemental composition and chemical state of Cu in the films. Ultraviolet photoelectron spectroscopy and photoluminescence spectroscopy revealed that the valence band maximum of the p-type Cu/Cu2O matches well with the perovskite. The Cu/Cu2O film not only acts as a p-type modified layer but also plays the role of an electron blocking buffer layer. By introducing the p-type Cu/Cu2O films between the low-mobility hole transport material, spiro-OMeTAD, and the Ag electrode in the PSCs, the device durability and power conversion efficiency (PCE) were effectively improved as compared to the reference devices without the Cu/Cu2O interlayer. The enhanced PCE is mainly attributed to the high hole mobility of the p-type Cu/Cu2O film. Additionally, the Cu/Cu2O film serves as a protective layer against the penetration of humidity and Ag into the perovskite active layer.

SUBMITTER: Chen YJ

PROVIDER: S-EPMC5955939 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

MDACl2-Modified SnO2 Film for Efficient Planar Perovskite Solar Cells.

Project description:The electron transport layer (ETL) with excellent charge extraction and transport ability is one of the key components of high-performance perovskite solar cells (PSCs). SnO2 has been considered as a more promising ETL for the future commercialization of PSCs due to its excellent photoelectric properties and easy processing. Herein, we propose a facile and effective ETL modification strategy based on the incorporation of methylenediammonium dichloride (MDACl2) into the SnO2 precursor colloidal solution. The effects of MDACl2 incorporation on charge transport, defect passivation, perovskite crystallization, and PSC performance are systematically investigated. First, the surface defects of the SnO2 film are effectively passivated, resulting in the increased conductivity of the SnO2 film, which is conducive to electron extraction and transport. Second, the MDACl2 modification contributes to the formation of high-quality perovskite films with improved crystallinity and reduced defect density. Furthermore, a more suitable energy level alignment is achieved at the ETL/perovskite interface, which facilitates the charge transport due to the lower energy barrier. Consequently, the MDACl2-modified PSCs exhibit a champion efficiency of 22.30% compared with 19.62% of the control device, and the device stability is also significantly improved.

| S-EPMC10056177 | biostudies-literature

Low-Temperature Ionic Layer Adsorption and Reaction Grown Anatase TiO2 Nanocrystalline Films for Efficient Perovskite Solar Cell and Gas Sensor Applications.

Project description:A low-temperature (90 °C) and directly grown anatase titanium dioxide (TiO2) nanocrystalline film using successive ionic layer adsorption and reaction (SILAR) for perovskite solar cell and gas sensor applications. TiO2 nanocrystalline electron transfer layer (ETL) improves the power conversion efficiency (PCE) of perovskite solar cells due to faster charge transport kinetics as well as slower charge recombination process. The optimized TiO2 nanocrystalline ETL (15 L) demonstrates as high as ~10% PCE with a short circuit current density of 18.0 mA/cm2, open circuit voltage of 0.81 V and fill factor of 66.3% in perovskite solar cells. Furthermore, room-temperature ammonia sensing characteristics of TiO2 nanocrystalline film (25 L) were demonstrated for various concentration levels of ammonia in dry air conditions. A high room-temperature response of 80% was achieved at 100 ppm of ammonia with rapid response and recovery signatures of 30 and 85 s, and nearly fifteen days stability, respectively. The response of the sensor to other gases such as formaldehyde, petrol, ethanol acetone, and ammonia etc, indicated a high selectivity towards volatile organic compounds of ammonia gas. The room temperature operation, with high selectivity, repeatability and fast transition times, suggests potentially useful in flexible and cost-effective production in optoelectrochemical device technology.

| S-EPMC6054626 | biostudies-literature

Surface engineering of perovskite films for efficient solar cells.

Project description:It is critical to prepare smooth and dense perovskite films for the fabrication of high efficiency perovskite solar cells. However, solution casting process often results in films with pinhole formation and incomplete surface coverage. Herein, we demonstrate a fast and efficient vacuum deposition method to optimize the surface morphology of solution-based perovskite films. The obtained planar devices exhibit an average power conversion efficiency (PCE) of 13.42% with a standard deviation of?±2.15% and best efficiency of 15.57%. Furthermore, the devices also show excellent stability of over 30 days with a slight degradation <9% when stored under ambient conditions. We also investigated the effect of vacuum deposition thickness on the electron transportation and overall performance of the devices. This work provides a versatile approach to prepare high-quality perovskite films and paves a way for high-performance and stable perovskite photovoltaic devices.

| S-EPMC5670249 | biostudies-literature

MgO Nanoparticle Modified Anode for Highly Efficient SnO2-Based Planar Perovskite Solar Cells.

Project description:Reducing the energy loss and retarding the carrier recombination at the interface are crucial to improve the performance of the perovskite solar cell (PSCs). However, little is known about the recombination mechanism at the interface of anode and SnO2 electron transfer layer (ETL). In this work, an ultrathin wide bandgap dielectric MgO nanolayer is incorporated between SnO2:F (FTO) electrode and SnO2 ETL of planar PSCs, realizing enhanced electron transporting and hole blocking properties. With the use of this electrode modifier, a power conversion efficiency of 18.23% is demonstrated, an 11% increment compared with that without MgO modifier. These improvements are attributed to the better properties of MgO-modified FTO/SnO2 as compared to FTO/SnO2, such as smoother surface, less FTO surface defects due to MgO passivation, and suppressed electron-hole recombinations. Also, MgO nanolayer with lower valance band minimum level played a better role in hole blocking. When FTO is replaced with Sn-doped In2O3 (ITO), a higher power conversion efficiency of 18.82% is demonstrated. As a result, the device with the MgO hole-blocking layer exhibits a remarkable improvement of all J-V parameters. This work presents a new direction to improve the performance of the PSCs based on SnO2 ETL by transparent conductive electrode surface modification.

| S-EPMC5604382 | biostudies-literature

Ultrathin Hole Extraction Layer for Efficient Inverted Perovskite Solar Cells.

Project description:Inverted perovskite solar cells (PSCs) incorporating poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT) as the hole transport/extraction layer have been broadly investigated in recent years. However, most PSCs which incorporate PEDOT as the hole transport layer (HTL) suffer from lower device performance stemming from reduced photocurrent and low open-circuit voltage around 0.95 V. Here, we report an ultrathin PEDOT layer as the HTL for efficient inverted structure PSCs. The transparency, conductivity, and resulting film morphology were studied and compared with traditional architectures and thicker PEDOT layers. The PSC device incorporating an ultrathin PEDOT layer shows significant improvement in short-circuit current density (J SC), open-circuit voltage (V OC), and power conversion efficiency. Because ultrathin PEDOT layers can be easily obtained by dilution, this study suggests a simple way to improve the PSC performance and provide a route to further reduce the fabrication complexity and cost of PSCs.

| S-EPMC6644352 | biostudies-literature

Ti3C2Tx-Modified PEDOT:PSS Hole-Transport Layer for Inverted Perovskite Solar Cells.

Project description:PedotPSS is a commonly used hole-transport layer (HTL) in inverted perovskite solar cells (PSCs) due to its compatibility with low-temperature solution processing. However, it possesses lower conductivity than other conductive polymers and metal oxides, along with surface defects, limiting its photovoltaic performance. In this study, we introduced two-dimensional Ti3C2Tx (MXene) as an additive in the PEDOT:PSS HTL with varying doping concentrations (i.e., 0, 0.03, 0.05, and 0.1 wt.%) to tune the electrical conductivity of PEDOT:PSS and to modify the properties of the perovskite film atop it. We noted that the grain size of the CH3NH3PbI3 (MAPI3) perovskite layer grown over an optimal concentration of MXene (0.03 wt.%)-doped PEDOT:PSS increased from 250 nm to 400 nm, reducing charge recombination due to fewer grain boundaries. Ultraviolet photoelectron spectroscopy (UPS) revealed increased work function (WF) from 4.43 eV to 4.99 eV with 0.03 wt.% MXene doping, making the extraction of holes easier due to a more favorable energy level alignment with the perovskite. Quantum chemical investigations based on density functional theory (DFT) were conducted at the ωB97XD/6-311++G(d,p) level of theory to provide more insight into the stability, bonding nature, and optoelectronic properties of the PEDOT:PSS-MXene system. The theoretical investigations revealed that the doping of PEDOT:PSS with Ti3C2Tx could cause a significant effect on the electronic properties of the HTL, as experimentally demonstrated by an increase in the electrical conductivity. Finally, the inverted PSCs employing 0.03 wt.% MXene-doped PEDOT:PSS showed an average power conversion efficiency (PCE) of 15.1%, up from 12.5% for a reference PSC employing a pristine PEDOT:PSS HTL. The champion device with a 0.03 wt.% MXene-PEDOT:PSS HTL achieved 15.5% PCE.

| S-EPMC9655112 | biostudies-literature

Efficient Carbon-Based CsPbBr3 Inorganic Perovskite Solar Cells by Using Cu-Phthalocyanine as Hole Transport Material.

Project description:Metal halide perovskite solar cells (PSCs) have attracted extensive research interest for next-generation solution-processed photovoltaic devices because of their high solar-to-electric power conversion efficiency (PCE) and low fabrication cost. Although the world's best PSC successfully achieves a considerable PCE of over 20% within a very limited timeframe after intensive efforts, the stability, high cost, and up-scaling of PSCs still remain issues. Recently, inorganic perovskite material, CsPbBr3, is emerging as a promising photo-sensitizer with excellent durability and thermal stability, but the efficiency is still embarrassing. In this work, we intend to address these issues by exploiting CsPbBr3 as light absorber, accompanied by using Cu-phthalocyanine (CuPc) as hole transport material (HTM) and carbon as counter electrode. The optimal device acquires a decent PCE of 6.21%, over 60% higher than those of the HTM-free devices. The systematic characterization and analysis reveal a more effective charge transfer process and a suppressed charge recombination in PSCs after introducing CuPc as hole transfer layer. More importantly, our devices exhibit an outstanding durability and a promising thermal stability, making it rather meaningful in future fabrication and application of PSCs.

| S-EPMC6199080 | biostudies-literature

Efficient and Air-Stable Planar Perovskite Solar Cells Formed on Graphene-Oxide-Modified PEDOT:PSS Hole Transport Layer.

Project description:As a hole transport layer, PEDOT:PSS usually limits the stability and efficiency of perovskite solar cells (PSCs) due to its hygroscopic nature and inability to block electrons. Here, a graphene-oxide (GO)-modified PEDOT:PSS hole transport layer was fabricated by spin-coating a GO solution onto the PEDOT:PSS surface. PSCs fabricated on a GO-modified PEDOT:PSS layer exhibited a power conversion efficiency (PCE) of 15.34%, which is higher than 11.90% of PSCs with the PEDOT:PSS layer. Furthermore, the stability of the PSCs was significantly improved, with the PCE remaining at 83.5% of the initial PCE values after aging for 39 days in air. The hygroscopic PSS material at the PEDOT:PSS surface was partly removed during spin-coating with the GO solution, which improves the moisture resistance and decreases the contact barrier between the hole transport layer and perovskite layer. The scattered distribution of the GO at the PEDOT:PSS surface exhibits superior wettability, which helps to form a high-quality perovskite layer with better crystallinity and fewer pin holes. Furthermore, the hole extraction selectivity of the GO further inhibits the carrier recombination at the interface between the perovskite and PEDOT:PSS layers. Therefore, the cooperative interactions of these factors greatly improve the light absorption of the perovskite layer, the carrier transport and collection abilities of the PSCs, and especially the stability of the cells.

| S-EPMC6199037 | biostudies-literature

Low-temperature solution-processed SnO2 electron transport layer modified by oxygen plasma for planar perovskite solar cells.

Project description:SnO2 has attracted significant attention as an electron transport layer (ETL) because of its wide optical bandgap, electron mobility, and transparency. However, the annealing temperature of 180 °C-200 °C, as reported by several studies, for the fabrication of SnO2 ETL limits its application for flexible devices. Herein, we demonstrated that the low-temperature deposition of SnO2 ETL and further surface modification with oxygen plasma enhances its efficiency from 2.3% to 15.30%. Oxygen plasma treatment improves the wettability of the low-temperature processed SnO2 ETL that results in a larger perovskite grain size. Hence, oxygen plasma treatment effectively improves the efficiency of perovskite solar cells at a low temperature and is compatible with flexible applications.

| S-EPMC8981385 | biostudies-literature

Spacer layer design for efficient fully printable mesoscopic perovskite solar cells.

Project description:The spacer layer is a key component of fully printable mesoscopic perovskite solar cells, but its precise characteristics are far from being understood in relation to the device design. In the present work, we perform a detailed systematic study on the effects of spacer parameters, such as size of building blocks, layer thickness, etc., on properties of the perovskite filler, insulating ability and performance of fully printable mesoscopic perovskite solar cells by combining the techniques of time-resolved photoluminescence, high-resolution TEM, insulating resistance measurements, impedance spectroscopy and J-V characteristics. Drawing on the deep understanding from these studies, we formulate key principles, which are anticipated to guide the design of the advanced spacer layer for fully printable mesoscopic perovskite solar cells.

| S-EPMC9072001 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data