Metal-organic framework-based CoP/reduced graphene oxide: high-performance bifunctional electrocatalyst for overall water splitting.

ABSTRACT: Efficient and cost-effective electrocatalysts for the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER), especially bifunctional catalysts for overall water splitting, are highly desired. In this work, with rationally designed sandwich-type metal-organic framework/graphene oxide as a template and precursor, a layered CoP/reduced graphene oxide (rGO) composite has been successfully prepared via pyrolysis and a subsequent phosphating process. The resultant CoP/rGO-400 exhibits excellent HER activity in acid solution. More importantly, the catalyst manifests excellent catalytic performances for both the HER and OER in basic solution. Therefore, it can be utilized as a bifunctional catalyst on both the anode and cathode for overall water splitting in basic media, even displaying superior activity to that of the integrated Pt/C and IrO2 catalyst couple.

SUBMITTER: Jiao L

PROVIDER: S-EPMC5964964 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Cobalt Phosphide-Embedded Reduced Graphene Oxide as a Bifunctional Catalyst for Overall Water Splitting.

Project description:It is highly desirable to design high-efficiency stable and low-price catalysts in the electrocatalysis field. Herein, we reported a cobalt phosphide (Co2P)-loaded reduced graphene oxide (rGO) composite catalyst (rGO/Co2P) prepared via the convenient hydrothermal and H2 reduction methods. The rGO/Co2P catalyst reduced at 800 °C (rGO/Co2P-800) shows superior electrocatalytic activities for hydrogen evolution reaction and oxygen evolution reaction in 1.0 M KOH solution, achieving an overpotential of 134 and 378 mV, respectively, at a current density of 10 mA cm-2. Moreover, the catalyst can not only maintain stability for a long time in alkaline solution but also in acid media because of the protection of the rGO layers. The superior performance of this catalyst is attributed to the synergy between the carbon layer and transition-metal phosphides. The Co2P nanoparticles have a high degree of dispersion, which prevents agglomeration, thereby exposing more active sites. Moreover, rGO protects the exposed metal particles while providing more electroconductivity to the material. This work provides an efficient route for the development of bifunctional electrocatalysts with excellent performance and stability, which provides new ideas toward overall water splitting.

| S-EPMC7114733 | biostudies-literature

Thermally reduced mesoporous manganese MOF @reduced graphene oxide nanocomposite as bifunctional electrocatalyst for oxygen reduction and evolution.

Project description:Oxygen electrocatalysis plays a crucial role in harnessing energy from modern renewable energy technologies like fuel cells and metal-air batteries. But high cost and stability issues of noble metal catalysts call for research on tailoring novel metal-organic framework (MOF) based architectures which can bifunctionally catalyze O2 reduction and evolution reactions (ORR & OER). In this work, we report a novel manganese MOF @rGO nanocomposite synthesized using a facile self-templated solvothermal method. The nanocomposite is superior to commercial Pt/C catalyst both in material resource and effectiveness in application. A more positive cathodic peak (E pc = 0.78 V vs. RHE), onset (E onset = 1.09 V vs. RHE) and half wave potentials (E 1/2 = 0.98 V vs. RHE) for the ORR and notable potential to achieve the threshold current density (E @10 mA cm-2 = 1.84 V vs. RHE) for OER are features promising to reduce overpotentials during ORR and OER. Small Tafel slopes, methanol tolerance and acceptable short term stability augment the electrocatalytic properties of the as-prepared nanocomposite. Remarkable electrocatalytic features are attributed to the synergistic effect from the mesoporous 3D framework and transition metal-organic composition. Template directed growth, tunable porosities, novel architecture and excellent electrocatalytic performance of the manganese MOF @rGO nanocomposite make it an excellent candidate for energy applications.

| S-EPMC9055589 | biostudies-literature

Phase-Controlled NiO Nanoparticles on Reduced Graphene Oxide as Electrocatalysts for Overall Water Splitting.

Project description:Efficient water electrolysis is one of the key issues in realizing a clean and renewable energy society based on hydrogen fuel. However, several obstacles remain to be solved for electrochemical water splitting catalysts, which are the high cost of noble metals and the high overpotential of alternative catalysts. Herein, we suggest Ni-based alternative catalysts that have comparable performances with precious metal-based catalysts and could be applied to both cathode and anode by precise phase control of the pristine catalyst. A facile microwave-assisted procedure was used for NiO nanoparticles anchored on reduced graphene oxide (NiO NPs/rGO) with uniform size distribution in ~1.8 nm. Subsequently, the Ni-NiO dual phase of the NPs (A-NiO NPs/rGO) could be obtained via tailored partial reduction of the NiO NPs/rGO. Moreover, we demonstrate from systematic HADDF-EDS and XPS analyses that metallic Ni could be formed in a local area of the NiO NP after the reductive annealing procedure. Indeed, the synergistic catalytic performance of the Ni-NiO phase of the A-NiO NPs/rGO promoted hydrogen evolution reaction activity with an overpotential as 201 mV at 10 mA cm-2, whereas the NiO NPs/rGO showed 353 mV. Meanwhile, the NiO NPs/rGO exhibited the most excellent oxygen evolution reaction performance among all of the Ni-based catalysts, with an overpotential of 369 mV at 10 mA cm-2, indicating that they could be selectively utilized in the overall water splitting. Furthermore, both catalysts retained their activities over 12 h with constant voltage and 1000 cycles under cyclic redox reaction, proving their high durability. Finally, the full cell capability for the overall water electrolysis system was confirmed by observing the generation of hydrogen and oxygen on the surface of the cathode and anode.

| S-EPMC8708175 | biostudies-literature

Accelerating the water splitting kinetics of CoP microcubes anchored on a graphene electrocatalyst by Mn incorporation.

Project description:CoP is considered as an efficient electrocatalyst for the hydrogen evolution reaction (HER) in acidic electrolytes but its performance in alkaline solutions is generally poor because of its slow reaction kinetics, which further limits its application in overall water splitting. Herein, we demonstrate a strategy to greatly accelerate its HER and OER kinetics in alkaline solutions through Mn incorporation. Ternary Mn x Co1-x P microcubes with a tunable Mn/Co ratio strongly anchored on rGO were synthesized using Prussian blue analogues as precursors. The synergy between the high activity of Mn x Co1-x P microcubes and the good conductivity of rGO leads to the superior performance of the hybrid toward water splitting in 1 M KOH. The optimized Mn0.6Co0.4P-rGO electrocatalyst shows high activity and stability towards both the HER and OER with low overpotentials of 54 and 250 mV at 10 mA cm-2, respectively. Furthermore, the water electrolyzer using Mn0.6Co0.4P-rGO as both the cathode and anode only requires a cell voltage as low as 1.55 V to reach a current density of 10 mA cm-2, making Mn0.6Co0.4P-rGO a competitive and cost-effective electrocatalyst for water splitting.

| S-EPMC9473208 | biostudies-literature

Nanostructured Nickel Nitride with Reduced Graphene Oxide Composite Bifunctional Electrocatalysts for an Efficient Water-Urea Splitting.

Project description:A three-dimensional nickel nitride with reduced graphene oxide composite on nickel foam (s-X, where s represents Ni3N/rGO@NF and the annealing temperature X can be 320, 350, or 380) electrode has been fabricated through a facile method. We demonstrate that s-350 has excellent urea oxidation reaction (UOR) activity, with a demanded potential of 1.342 V to reach 10 mA/cm2 and bears high hydrogen evolution reaction (HER) activity. It provides a low overpotential of 124 mV at 10 mA/cm2, which enables the successful construction of its two-electrode alkaline electrolyzer (s-350||s-350) for water-urea splitting. It merely requires a voltage of 1.518 V to obtain 100 mA/cm2 and is 0.145 V lower than that of pure water splitting. This noble metal-free bifunctional electrode is regarded as an inexpensive and effective water-urea electrolysis assisted hydrogen production technology, which is commercially viable.

| S-EPMC6915570 | biostudies-literature

Coordination engineering of iridium nanocluster bifunctional electrocatalyst for highly efficient and pH-universal overall water splitting.

Project description:Water electrolysis offers a promising energy conversion and storage technology for mitigating the global energy and environmental crisis, but there still lack highly efficient and pH-universal electrocatalysts to boost the sluggish kinetics for both cathodic hydrogen evolution reaction (HER) and anodic oxygen evolution reaction (OER). Herein, we report uniformly dispersed iridium nanoclusters embedded on nitrogen and sulfur co-doped graphene as an efficient and robust electrocatalyst for both HER and OER at all pH conditions, reaching a current density of 10 mA cm-2 with only 300, 190 and 220 mV overpotential for overall water splitting in neutral, acidic and alkaline electrolyte, respectively. Based on probing experiments, operando X-ray absorption spectroscopy and theoretical calculations, we attribute the high catalytic activities to the optimum bindings to hydrogen (for HER) and oxygenated intermediate species (for OER) derived from the tunable and favorable electronic state of the iridium sites coordinated with both nitrogen and sulfur.

| S-EPMC7447631 | biostudies-literature

Carved nanoframes of cobalt-iron bimetal phosphide as a bifunctional electrocatalyst for efficient overall water splitting.

Project description:Water electrolysis for hydrogen production has long been regarded as an ideal tactic for renewable energy conversion and storage, but is impeded by the sluggish kinetics of both the hydrogen and oxygen evolution reactions, which are therefore in urgent need for high-performance but low-cost electrocatalysts. Herein, nanoframes of transition metal phosphides (TMPs) with the 3D framework carved open have been demonstrated as highly potent bifunctional catalysts for overall water splitting, reaching the benchmark performance of the Pt/C‖RuO2 couple, and are much superior to their nanocubic counterparts. This excellent water splitting behavior can be attributed to the enlarged active surface area, less obstructed electrolyte infiltration, promoted charge transfer, and facilitated gas release. Further through in-depth activity analysis and post-electrocatalysis characterization, special attention has been paid to the fate and role of phosphorus in the electrocatalytic process, suggesting that despite the chemical instability of the TMPs (especially under OER conditions), excellent electrocatalytic stability can still be achieved through the amorphous bimetallic hydroxides/oxides formed in situ.

| S-EPMC6334264 | biostudies-literature

Metal-organic Framework-driven Porous Cobalt Disulfide Nanoparticles Fabricated by Gaseous Sulfurization as Bifunctional Electrocatalysts for Overall Water Splitting.

Project description:Both high activity and mass production potential are important for bifunctional electrocatalysts for overall water splitting. Catalytic activity enhancement was demonstrated through the formation of CoS2 nanoparticles with mono-phase and extremely porous structures. To fabricate porous structures at the nanometer scale, Co-based metal-organic frameworks (MOFs), namely a cobalt Prussian blue analogue (Co-PBA, Co3[Co(CN)6]2), was used as a porous template for the CoS2. Then, controlled sulfurization annealing converted the Co-PBA to mono-phase CoS2 nanoparticles with ~ 4?nm pores, resulting in a large surface area of 915.6?m2?g-1. The electrocatalysts had high activity for overall water splitting, and the overpotentials of the oxygen evolution reaction and hydrogen evolution reaction under the operating conditions were 298?mV and -196 mV, respectively, at 10?mA?cm-2.

| S-EPMC6925291 | biostudies-literature

Fe-CoP Electrocatalyst Derived from a Bimetallic Prussian Blue Analogue for Large-Current-Density Oxygen Evolution and Overall Water Splitting.

Project description:Industrial application of overall water splitting requires developing readily available, highly efficient, and stable oxygen evolution electrocatalysts that can efficiently drive large current density. This study reports a facile and practical method to fabricate a non-noble metal catalyst by directly growing a Co-Fe Prussian blue analogue on a 3D porous conductive substrate, which is further phosphorized into a bifunctional Fe-doped CoP (Fe-CoP) electrocatalyst. The Fe-CoP/NF (nickel foam) catalyst shows efficient electrocatalytic activity for oxygen evolution reaction, requiring low overpotentials of 190, 295, and 428 mV to achieve 10, 500, and 1000 mA cm-2 current densities in 1.0 m KOH solution. In addition, the Fe-CoP/NF can also function as a highly active electrocatalyst for hydrogen evolution reaction with a low overpotential of 78 mV at 10 mA cm-2 current density in alkaline solution. Thus, the Fe-CoP/NF electrode with meso/macropores can act as both an anode and a cathode to fabricate an electrolyzer for overall water splitting, only requiring a cell voltage of 1.49 V to afford a 10 mA cm-2 current density with remarkable stability. This performance appears to be among the best reported values and is much better than that of the IrO2-Pt/C-based electrolyzer.

| S-EPMC6193147 | biostudies-literature

A Self-Reconstructed Bifunctional Electrocatalyst of Pseudo-Amorphous Nickel Carbide @ Iron Oxide Network for Seawater Splitting.

Project description:Here, a sol-gel method is used to prepare a Prussian blue analogue (NiFe-PBA) precursor with a 2D network, which is further annealed to an Fe3 O4 /NiCx composite (NiFe-PBA-gel-cal), inheriting the ultrahigh specific surface area of the parent structure. When the composite is used as both anode and cathode catalyst for overall water splitting, it requires low voltages of 1.57 and 1.66 V to provide a current density of 100 mA cm-2 in alkaline freshwater and simulated seawater, respectively, exhibiting no obvious attenuation over a 50 h test. Operando Raman spectroscopy and X-ray photoelectron spectroscopy indicate that NiOOH2-x active species containing high-valence Ni3+ /Ni4+ are in situ generated from NiCx during the water oxidation. Density functional theory calculations combined with ligand field theory reveal that the role of high valence states of Ni is to trigger the production of localized O 2p electron holes, acting as electrophilic centers for the activation of redox reactions for oxygen evolution reaction. After hydrogen evolution reaction, a series of ex situ and in situ investigations indicate the reduction from Fe3+ to Fe2+ and the evolution of Ni(OH)2 are the origin of the high activity.

| S-EPMC9131433 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data