Linearly polarized photoluminescence of InGaN quantum disks embedded in GaN nanorods.

ABSTRACT: We have investigated the emission from InGaN/GaN quantum disks grown on the tip of GaN nanorods. The emission at 3.21?eV from the InGaN quantum disk doesn't show a Stark shift, and it is linearly polarized when excited perpendicular to the growth direction. The degree of linear polarization is about 39.3% due to the anisotropy of the nanostructures. In order to characterize a single nanostructure, the quantum disks were dispersed on a SiO2 substrate patterned with a metal reference grid. By rotating the excitation polarization angle from parallel to perpendicular relative to the nanorods, the variation of overall PL for the 3.21?eV peak was recorded and it clearly showed the degree of linear polarization (DLP) of 51.5%.

SUBMITTER: Park Y

PROVIDER: S-EPMC5970171 | biostudies-literature | 2018 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Linearly polarized photoluminescence of InGaN quantum disks embedded in GaN nanorods.

Park Youngsin Y Chan Christopher C S CCS Nuttall Luke L Puchtler Tim J TJ Taylor Robert A RA Kim Nammee N Jo Yongcheol Y Im Hyunsik H

Scientific reports 20180525 1

We have investigated the emission from InGaN/GaN quantum disks grown on the tip of GaN nanorods. The emission at 3.21 eV from the InGaN quantum disk doesn't show a Stark shift, and it is linearly polarized when excited perpendicular to the growth direction. The degree of linear polarization is about 39.3% due to the anisotropy of the nanostructures. In order to characterize a single nanostructure, the quantum disks were dispersed on a SiO<sub>2</sub> substrate patterned with a metal reference gr ...[more]

PMID: 29802300

Similar Datasets

Highly polarized photoluminescence from c-plane InGaN/GaN multiple quantum wells on stripe-shaped cavity-engineered sapphire substrate.

Project description:Highly polarized photoluminescence (PL) from c-plane InGaN/GaN multiple quantum wells (MQWs) grown on stripe-shaped cavity-engineered sapphire substrate (SCES) was realized. The polarization ratio was as high as 0.74 at room temperature. High-resolution X-ray reciprocal space mapping measurements revealed that the InGaN quantum wells on GaN/SCES template were under considerable anisotropic in-plane strain states of -1.178% and -1.921% along the directions perpendicular and parallel to the stripe-pattern, respectively. The anisotropic strain states were attributed to the anisotropic alignment of cavity-incorporated sapphire nano-membranes, which accommodated both anisotropic elastic relaxation in the InGaN quantum well plane as well as the graded elastic relaxation along the vertical direction in the GaN template adjacent to the InGaN/GaN MQWs. The partial strain relaxation in the InGaN wells also contributed to reduction of quantum confined Stark effect, resulting in four times higher PL intensity than InGaN/GaN MQWs on planar sapphire substrate. From theoretical calculations based on k∙p perturbation theory, it was found that fundamental origin of the polarized optical emission was strain-induced modification of valence band structures of the InGaN/GaN MQWs on the SCES. This study will allow us to realize light emitting diodes with highly polarized emission with conventional c-plane sapphire substrates by strain-induced valence band modification.

| S-EPMC6547675 | biostudies-literature

A novel model on time-resolved photoluminescence measurements of polar InGaN/GaN multi-quantum-well structures.

Project description:Based on carrier rate equation, a new model is proposed to explain the non-exponential nature of time-resolved photoluminescence (TRPL) decay curves in the polar InGaN/GaN multi-quantum-well structures. From the study of TRPL curves at different temperatures, it is found that both radiative and non-radiative recombination coefficients vary from low temperature to room temperature. The variation of the coefficients is compatible with the carrier density of states distribution as well as the carrier localization process. These results suggest that there is a novel method to calculate the internal quantum efficiency, which is a complement to the traditional one based on temperature dependent photoluminescence measurement.

| S-EPMC5361181 | biostudies-literature

Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

Project description:GaN nanorods (NRds) with axial InGaN/GaN MQWs insertions are synthesized by an original cost-effective and large-scale nanoimprint-lithography process from an InGaN/GaN MQWs layer grown on c-sapphire substrates. By design, such NRds exhibit a single emission due to the c-axis MQWs. A systematic study of the emission of the NRds by time-resolved luminescence (TR-PL) and power dependence PL shows a diameter-controlled luminescence without significant degradation of the recombination rate thanks to the diameter-controlled strain tuning and QSCE. A blueshift up to 0.26 eV from 2.28 to 2.54 eV (543 nm to 488 nm) is observed for 3.2 nm thick InGaN/GaN QWs with an In composition of 19% when the NRds radius is reduced from 650 to 80 nm. The results are consistent with a 1-D based strain relaxation model. By combining state of the art knowledge of c-axis growth and the strong strain relieving capability of NRds, this process enables multiple and independent single-color emission from a single uniform InGaN/GaN MQWs layer in a single patterning step, then solving color mixing issue in InGaN based nanorods LED devices.

| S-EPMC7990954 | biostudies-literature

3D fluorescence confocal microscopy of InGaN/GaN multiple quantum well nanorods from a light absorption perspective.

Project description:A nanostructure of In0.18Ga0.82N/GaN multiple quantum well (MQW) nanorods (NRs) was fabricated using top-down etching with self-organized nickel (Ni) nanoparticles as masks on the wafer. The optical properties of In0.18Ga0.82N/GaN MQW NRs were discussed by experiment and theory from a light absorption perspective. Three-dimensional (3D) optical images of NRs were successfully obtained by confocal laser scanning microscopy (CLSM) for physical observation of the optical phenomenon of InGaN/GaN MQW NRs. Moreover, optical simulations were performed by COMSOL Multiphysics via the three-dimensional finite-element method to explore the influences of NR geometrical parameters on optical absorption. The simulated results demonstrate that the absorption of NRs is higher than that of the film due to the waveguide properties of NRs resulting from their higher refractive index than embedding medium and higher aspect ratio than bulk. In addition, an increase in the diameter results in a red-shift of the absorption peak position of In0.18Ga0.82N/GaN MQW NRs. The smaller pitch enhances the near-field coupling of the nanorods and broadens the absorption peak. These results clearly illustrate the optical properties of In0.18Ga0.82N/GaN MQW NRs from the perspective of 3D confocal laser scanning microscopy. This work is promising for the applications of III-V optoelectronic devices.

| S-EPMC9417793 | biostudies-literature

Photoluminescence studies of a perceived white light emission from a monolithic InGaN/GaN quantum well structure.

Project description:In this work we demonstrate by photoluminescence studies white light emission from a monolithic InGaN/GaN single quantum well structure grown by metal organic chemical vapour deposition. As-grown and thermally annealed samples at high temperature (1000 °C, 1100 °C and 1200 °C) and high pressure (1.1 GPa) were analysed by spectroscopic techniques, and the annealing effect on the photoluminescence is deeply explored. Under laser excitation of 3.8 eV at room temperature, the as-grown structure exhibits two main emission bands: a yellow band peaked at 2.14 eV and a blue band peaked at 2.8 eV resulting in white light perception. Interestingly, the stability of the white light is preserved after annealing at the lowest temperature (1000 °C), but suppressed for higher temperatures due to a deterioration of the blue quantum well emission. Moreover, the control of the yellow/blue bands intensity ratio, responsible for the white colour coordinate temperatures, could be achieved after annealing at 1000 °C. The room temperature white emission is studied as a function of incident power density, and the correlated colour temperature values are found to be in the warm white range: 3260-4000 K.

| S-EPMC4559898 | biostudies-other

Intersubband Transition in GaN/InGaN Multiple Quantum Wells.

Project description:Utilizing the growth temperature controlled epitaxy, high quality GaN/In0.15Ga0.85N multiple quantum wells designed for intersubband transition (ISBT) as novel candidates in III-nitride infrared device applications have been experimentally realized for the first time. Photo-absorption originated from the ISBT has been successfully observed at infrared regime covering the 3-5 μm atmosphere window, where the central absorption wavelength is modulated by adjusting the quantum well width. With increasing the quantum well thickness, the ISBT center wave length blue shifts at thickness less than 2.8 nm and then redshifts with further increase of the well thickness. The non-monotonic trend is most likely due to the polarization induced asymmetric shape of the quantum wells.

| S-EPMC4473535 | biostudies-other

2D-GaN/AlN Multiple Quantum Disks/Quantum Well Heterostructures for High-Power Electron-Beam Pumped UVC Emitters.

Project description:This article describes GaN/AlN heterostructures for ultraviolet-C (UVC) emitters with multiple (up to 400 periods) two-dimensional (2D)-quantum disk/quantum well structures with the same GaN nominal thicknesses of 1.5 and 16 ML-thick AlN barrier layers, which were grown by plasma-assisted molecular-beam epitaxy in a wide range of gallium and activated nitrogen flux ratios (Ga/N2*) on c-sapphire substrates. An increase in the Ga/N2* ratio from 1.1 to 2.2 made it possible to change the 2D-topography of the structures due to a transition from the mixed spiral and 2D-nucleation growth to a purely spiral growth. As a result, the emission energy (wavelength) could be varied from 5.21 eV (238 nm) to 4.68 eV (265 nm) owing to the correspondingly increased carrier localization energy. Using electron-beam pumping with a maximum pulse current of 2 A at an electron energy of 12.5 keV, a maximum output optical power of 50 W was achieved for the 265 nm structure, while the structure emitting at 238 nm demonstrated a power of 10 W.

| S-EPMC10059987 | biostudies-literature

State-of-the-art and prospects for intense red radiation from core-shell InGaN/GaN nanorods.

Project description:Core-shell nanorods (NRs) with InGaN/GaN quantum wells (QWs) are promising for monolithic white light-emitting diodes and multi-color displays. Such applications, however, are still a challenge because intensity of the red band is too weak compared with blue and green. To clarify this problem, we measured photoluminescence of different NRs, depending on power and temperature, as well as with time resolution. These studies have shown that dominant emission bands come from nonpolar and semipolar QWs, while a broad yellow-red band arises mainly from defects in the GaN core. An emission from polar QWs located at the NR tip is indistinguishable against the background of defect-related luminescence. Our calculations of electromagnetic field distribution inside the NRs show a low density of photon states at the tip, which additionally suppresses the radiation of polar QWs. We propose placing polar QWs inside a cylindrical part of the core, where the density of photon states is higher and the well area is much larger. Such a hybrid design, in which the excess of blue radiation from shell QWs is converted to red radiation in core wells, can help solve the urgent problem of red light for many applications of NRs.

| S-EPMC7643183 | biostudies-literature

Study on spin and optical polarization in a coupled InGaN/GaN quantum well and quantum dots structure.

Project description:The spin and optical polarization based on a coupled InGaN/GaN quantum well (QW) and quantum dots (QDs) structure is investigated. In this structure, spin-electrons can be temporarily stored in QW, and spin injection from the QW into QDs via spin-conserved tunneling is enabled. Spin relaxation can be suppressed owing to the small energy difference between the initial state in the QW and the final states in the QDs. Photoluminescence (PL) and time-resolved photoluminescence (TRPL) measurements are carried out on optical spin-injection and -detection. Owing to the coupled structure, spin-conserved tunneling mechanism plays a significant role in preventing spin relaxation process. As a result, a higher circular polarization degree (CPD) (~49.1%) is achieved compared with conventional single layer of QDs structure. Moreover, spin relaxation time is also extended to about 2.43 ns due to the weaker state-filling effect. This coupled structure is believed an appropriate candidate for realization of spin-polarized light source.

| S-EPMC5069675 | biostudies-literature

Carrier localization in In-rich InGaN/GaN multiple quantum wells for green light-emitting diodes.

Project description:Carrier localization phenomena in indium-rich InGaN/GaN multiple quantum wells (MQWs) grown on sapphire and GaN substrates were investigated. Temperature-dependent photoluminescence (PL) spectroscopy, ultraviolet near-field scanning optical microscopy (NSOM), and confocal time-resolved PL (TRPL) spectroscopy were employed to verify the correlation between carrier localization and crystal quality. From the spatially resolved PL measurements, we observed that the distribution and shape of luminescent clusters, which were known as an outcome of the carrier localization, are strongly affected by the crystalline quality. Spectroscopic analysis of the NSOM signal shows that carrier localization of MQWs with low crystalline quality is different from that of MQWs with high crystalline quality. This interrelation between carrier localization and crystal quality is well supported by confocal TRPL results.

| S-EPMC4366764 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data