Type of Primary Nb₅Si₃ and Precipitation of Nb_ss in αNb₅Si₃ in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy.

ABSTRACT: The Nb-silicide-based alloy of near eutectic composition (at.%) Nb-21.1Si-8.3Ti-5.4Mo-4W-0.7Hf (alloy CM1) was studied in the cast and heat-treated (1500 °C/100 h) conditions. The alloy was produced in the form of buttons and bars using three different methods, namely arc-melting, arc-melting and suction casting, and optical floating zone (OFZ) melting. In the former two cases the alloy solidified in water-cooled copper crucibles. Buttons and suction-cast bars of different size, respectively of 10 g and 600 g weight and 6 mm and 8 mm diameter, were produced. The OFZ bars were grown at three different growth rates of 12, 60 and 150 mm/h. It was confirmed that the type of Nb₅Si₃ formed in the cast microstructures depended on the solidification conditions. The primary phase in the alloy CM1 was the βNb₅Si₃. The transformation of βNb₅Si₃ to αNb₅Si₃ had occurred in the as cast large size button and the OFZ bars grown at the three different growth rates, and after the heat treatment of the small size button and the suction-cast bars of the alloy. This transformation was accompanied by subgrain formation in Nb₅Si₃ and the precipitation of Nb_ss in the large size as cast button and only by the precipitation of Nb_ss in the cast OFZ bars. Subgrains and precipitation of Nb_ss in αNb₅Si₃ was observed in the small size button and suction-cast bars after the heat treatment. Subgrains formed in αNb₅Si₃ after the heat treatment of the OFZ bars. The partitioning of solutes and in particular of Mo and Ti was key to this phase transformation. Subgrain formation was not necessary for precipitation of Nb_ss in αNb₅Si₃, but the partitioning of solutes was essential for this precipitation.

SUBMITTER: McCaughey C

PROVIDER: S-EPMC6024954 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Coating system(s) will be required for Nb-silicide based alloys. Alumina forming alloys that are chemically compatible with the Nb-silicide based alloy substrate could be components of such systems. The intermetallic alloys Nb1.45Si2.7Ti2.25Al3.25Hf0.35 (MG5) and Nb1.35Si2.3Ti2.3Al3.7Hf0.35 (MG6) were studied in the cast, heat treated and isothermally oxidised conditions at 800 and 1200 °C to find out if they are αAl₂O₃ scale formers. A (Al/Si)alloy versus Nb/(Ti + Hf)alloy map, which can be considered to be a map for Multi-Principle Element or Complex Concentrated Nb-Ti-Si-Al-Hf alloys, and a [Nb/(Ti + Hf)]Nb5Si3 versus [Nb/(Ti + Hf)]alloy map were constructed making use of the alloy design methodology NICE and data from a previously studied alloy, and were used to select the alloys MG5 and MG6 that were expected (i) not to pest, (ii) to form αAl₂O₃ scale at 1200 °C, (iii) to have no solid solution, (iv) to form only hexagonal Nb₅Si₃ and (v) to have microstructures consisting of hexagonal Nb₅Si₃, Ti₅Si₃, Ti₅Si₄, TiSi silicides, and tri-aluminides and Al rich TiAl. Both alloys met the requirements (i) to (v). The alumina scale was able to self-heal at 1200 °C. Liquation in the alloy MG6 at 1200 °C was linked with the formation of a eutectic like structure and the TiAl aluminide in the cast alloy. Key to the oxidation of the alloys was the formation (i) of "composite" silicide grains in which the Nb₅Si₃ core was surrounded by the Ti₅Si₄ and TiSi silicides, and (ii) of tri-aluminides with high Al/Si ratio, particularly at 1200 °C and very low Nb/Ti ratio forming in-between the "composite" silicide grains. Both alloys met the "standard definition" of high entropy alloys (HEAs). Compared with HEAs with bcc solid solution and intermetallics, the VEC values of both the alloys were outside the range of reported values. The parameters VEC,  and  of Nb-Ti-Si-Al-Hf coating alloys and non-pesting Nb-silicide based alloys were compared and trends were established. Selection of coating alloys with possible "layered" structures was discussed and alloy compositions were proposed.

Dataset Information

Type of Primary Nb₅Si₃ and Precipitation of Nb_ss in αNb₅Si₃ in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Dataset Information

Type of Primary Nb₅Si₃ and Precipitation of Nbss in αNb₅Si₃ in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Type of Primary Nb₅Si₃ and Precipitation of Nb_ss in αNb₅Si₃ in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy.