Response of hPDLSCs on 3D printed PCL/PLGA composite scaffolds in vitro.

ABSTRACT: Three?dimensional printed (3DP) scaffolds have become an excellent resource in alveolar bone regeneration. However, selecting suitable printable materials remains a challenge. In the present study, 3DP scaffolds were fabricated using three different ratios of poly (??caprolactone) (PCL) and poly?lactic?co?glycolic acid (PLGA), which were 0.1PCL/0.9PLGA, 0.5PCL/0.5PLGA and 0.9PCL/0.1PLGA. The surface characteristics and degradative properties of the scaffolds, and the response of human periodontal ligament stem cells (hPDLSCs) on the scaffolds, were assessed to examine the preferable ratio of PCL and PLGA for alveolar bone regeneration. The results demonstrated that the increased proportion of PLGA markedly accelerated the degradation, smoothed the surface and increased the wettability of the hybrid scaffold. Furthermore, the flow cytometry and Cell Counting Kit?8 assay revealed that the adhesion and proliferation of hPDLSCs were markedlyincreased on the 0.5PCL/0.5PLGA and 0.1PCL/0.9PLGA scaffolds. Additionally, the alkaline phosphatase activity detection and reverse?transcription quantitative polymerase chain reaction demonstrated that the hPDLSCs on the 0.5PCL/0.5PLGA scaffold exhibited the best osteogenic capacity. Consequently, PCL/PLGA composite scaffolds may represent a candidate focus for future bone regeneration studies, and the 0.5PCL/0.5PLGA scaffold demonstrated the best bio?response from the hPDLSCs.

SUBMITTER: Peng C

PROVIDER: S-EPMC6072152 | biostudies-literature | 2018 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Response of hPDLSCs on 3D printed PCL/PLGA composite scaffolds in vitro.

Peng Caixia C Zheng Jinxuan J Chen Dongru D Zhang Xueqin X Deng Lidi L Chen Zhengyuan Z Wu Liping L

Molecular medicine reports 20180525 2

Three‑dimensional printed (3DP) scaffolds have become an excellent resource in alveolar bone regeneration. However, selecting suitable printable materials remains a challenge. In the present study, 3DP scaffolds were fabricated using three different ratios of poly (ε‑caprolactone) (PCL) and poly‑lactic‑co‑glycolic acid (PLGA), which were 0.1PCL/0.9PLGA, 0.5PCL/0.5PLGA and 0.9PCL/0.1PLGA. The surface characteristics and degradative properties of the scaffolds, and the response of human periodonta ...[more]

PMID: 29845276

Similar Datasets

Project description:With advances in bone tissue engineering, various materials and methods have been explored to find a better scaffold that can help in improving bone growth and regeneration. Three-dimensional (3D) printing by fused deposition modeling can produce customized scaffolds from biodegradable polyesters such as polycaprolactone (PCL). Although the fabricated PCL scaffolds exhibited a lack of bioactivity and poor cell attachment on their surfaces, herein, using a simple postfabrication modification method with hydroxyapatite (HA) and bioglasses (BGs), we obtained better cell proliferation and attachment. Biological behavior and osteosupportive capacity of the 3D-printed scaffolds including PCL, PCL/HA, PCL/BG, and PCL/HA/BG were evaluated in this study, while human adipose tissue-derived mesenchymal stem cells (hADSCs) were cultured on the scaffolds. The cell morphology, attachment, and proliferation were investigated using scanning electron microscopy (SEM), 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT) assay, and 4',6-diamidino-2-phenylindole (DAPI) staining. In the next step, the ability of stem cells to differentiate into osteoblasts was evaluated by measuring alkaline phosphatase (ALP) activity, calcium deposition, and bone-related gene and protein expression. In the end, the expression levels of miR-20a, miR-125a, and their target genes were also investigated as positive and negative regulators in osteogenesis pathways. The results showed that the coated scaffolds with bioceramics present a more appropriate surface for cell adhesion and proliferation, as well as efficient potential in inducing osteoconduction and osteointegration compared to PCL alone and control. The PCL/HA/BG scaffold exhibited higher in vitro cell viability and bone formation compared to the other groups, which can be due to the synergistic effect of HA and BG. On the whole, this tricomponent 3D-printing scaffold has a promising prospect for bone tissue engineering applications.

Project description:Gellan gum (GG) was chemically modified with methacrylic moieties to produce a photocrosslinkable biomaterial ink, hereinafter called methacrylated GG (GGMA), with improved physico-chemical properties, mechanical behavior and stability under physiological conditions. Afterwards, GGMA was functionalized by incorporating two different bioactive compounds, a naturally derived eumelanin extracted from the black soldier fly (BSF-Eumel), or hydroxyapatite nanoparticles (HAp), synthesized by the sol-gel method. Different ink formulations based on GGMA (2 and 4% (w/v)), BSF-Eumel, at a selected concentration (0.3125 mg/mL), or HAp (10 and 30% wHAp/wGGMA) were developed and processed by three-dimensional (3D) printing. All the functionalized GGMA-based ink formulations allowed obtaining 3D-printed GGMA-based scaffolds with a well-organized structure. For both bioactive signals, the scaffolds with the highest GGMA concentration (4% (w/v)) and the highest percentage of infill (45%) showed the best performances in terms of morphological and mechanical properties. Indeed, these scaffolds showed a good structural integrity over 28 days. Given the presence of negatively charged groups along the eumelanin backbone, scaffolds consisting of GGMA/BSF-Eumel demonstrated a higher stability. From a mechanical point of view, GGMA/BSF-Eumel scaffolds exhibited values of storage modulus similar to those of GGMA ones, while the inclusion of HAp at 30% (wHAp/wGGMA) led to a storage modulus of 32.5 kPa, 3.5-fold greater than neat GGMA. In vitro studies proved the capability of the bioactivated 3D-printed scaffolds to support 7F2 osteoblast cell growth and differentiation. BSF-Eumel and HAp triggered a different time-dependent physiological response in the osteoblasts. Specifically, while the ink with BSF-Eumel acted as a stimulus towards cell proliferation, reaching the highest value at 14 days, a higher expression of alkaline phosphatase activity was detected for scaffolds consisting of GGMA and HAp. The overall findings demonstrated the possible use of these biomaterial inks for 3D-printed bone tissue-engineered scaffolds.

Project description:BackgroundScaffolds are of great importance in tissue engineering applications as they provide a mechanically supportive environment for cellular activity, which is particularly necessary for hard tissues such as bone. Notably, the mechanical properties of a scaffold vary with differing design parameters such as those related to scaffold height and internal structure. Thus, the present study aimed to explore the relationship between design parameters and mechanical properties of composite polycaprolactone (PCL) and nano-hydroxyapatite (nHAp) scaffolds fabricated by three-dimensional (3D) printing.MethodsWe designed and printed scaffolds with different internal structures (lattice and staggered) and varying heights (4, 6, 8 and 10 layers), and consistent porosity (50%) for the purpose of comparison. Then, we examined the scaffold microstructure (pore size and penetration between layers) using scanning electron microscopy (SEM) and mechanical properties (elastic modulus and yield strength) using compressive testing.ResultsOur results illustrated that the microstructural parameters were related to scaffold design. At higher heights, pore size increased while penetration between layers decreased; thus, mechanical properties were affected. Results of mechanical testing demonstrated that for lattice scaffolds, elastic modulus was similar for 6 vs 4, and 8 vs 4 layers but ~33% lower for 10 layers vs 4 layers. Similarly, yield strength was comparable for 6 vs 4, and 8 vs 4 layers but ~27% lower for 10 layers vs 4 layers. With staggered scaffolds, when compared to 4-layer results, elastic modulus was similar for 6 layers but was ~43% lower for 8 layers and ~38% lower for 10 layers. Staggered scaffolds had ~38%, ~51%, and ~76% lower yield strength when the number of layers were increased from 4 to 6, 8, and 10 layers, respectively. When comparing lattice and staggered scaffolds with the same layer number, elastic modulus was similar, apart from 8-layer scaffolds where the staggered design was ~42% lower than lattice. Yield strength was similar between 4-layer staggered and lattice scaffolds, while staggered scaffolds with 6, 8, and 10 number of layers showed ~43%, ~45%, ~68% lower strength, respectively, than those found in lattice scaffolds with the same layer numbers.ConclusionsMechanical properties of 3D printed scaffolds depended on scaffold height for both lattice and staggered internal structures. Staggered scaffolds had lower mechanical properties than the lattice scaffolds with the same height and were more sensitive to the change in scaffold height. Taken together, lattice scaffolds demonstrated the advantages of more stable mechanical properties over staggered scaffolds. Also, scaffolds with lower height were more promising in terms of mechanical properties compared to scaffolds with greater height.

Dataset Information

Response of hPDLSCs on 3D printed PCL/PLGA composite scaffolds in vitro.

Publications

Response of hPDLSCs on 3D printed PCL/PLGA composite scaffolds in vitro.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets