Annealing Behaviour of Pt and PtNi Nanowires for Proton Exchange Membrane Fuel Cells.

ABSTRACT: PtNi alloy and hybrid structures have shown impressive catalytic activities toward the cathodic oxygen reduction reaction (ORR) in proton exchange membrane fuel cells (PEMFCs). However, such promise does not often translate into improved electrode performances in PEMFC devices. In this contribution, a Ni impregnation and subsequent annealing method, translatable to vertically aligned nanowire gas diffusion electrodes (GDEs), is shown in thin-film rotating disk electrode measurements (TFRDE) to enhance the ORR mass activity of Pt nanowires (NWs) supported on carbon (Pt NWs/C) by around 1.78 times. Physical characterisation results indicate that this improvement can be attributed to a combination of Ni alloying of the nanowires with retention of the morphology, while demonstrating that Ni can also help improve the thermal stability of Pt NWs. These catalysts are then tested in single PEMFCs. Lower power performances are achieved for PtNi NWs/C than Pt NWs/C. A further investigation confirms the different surface behaviour between Pt NWs and PtNi NWs when in contact with electrolyte ionomer in the electrodes in PEMFC operation. Indications are that this interaction exacerbates reactant mass transport limitations not seen with TFRDE measurements.

SUBMITTER: Mardle P

PROVIDER: S-EPMC6120042 | biostudies-literature | 2018 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Nafion-stabilised bimetallic Pt-Cr nanoparticles as electrocatalysts for proton exchange membrane fuel cells (PEMFCs).

Project description:The current study investigated the unique combination of alloying (Pt with Cr) and Nafion stabilisation to reap the benefits of catalyst systems with enhanced catalytic activity and improved durability in PEMFCs. Pt-Cr alloy nanoparticles stabilised with Nafion were chosen in the current study owing to their higher stability in acidic and oxidising media at high temperatures compared to other Pt-transition metal alloys (e.g. Pt-Ni, Pt-Co). Two different precursor?:?reducing agent (1?:?10 and 1?:?20) ratios were used in order to prepare two different alloys, denoted as Pt-Cr 10 and Pt-Cr 20. The Pt-Cr 20 alloy system (with composition Pt80Cr20) demonstrated higher electrocatalytic activity for the oxygen reduction reaction compared to commercial Pt/C (TKK) catalysts. Accelerated stress tests and single cell tests revealed that Nafion stabilised alloy catalyst systems displayed significantly enhanced durability (only ?20% loss of ECSA) compared with Pt/C (50% loss of ECSA) due to improved catalyst-ionomer interaction. Furthermore, the Pt-Cr 20 alloy system demonstrated a current density comparable to that of Pt/C making them promising potential electrocatalysts for proton exchange membrane fuel cells.

| S-EPMC5059791 | biostudies-literature

Polyaniline Based Pt-Electrocatalyst for a Proton Exchanged Membrane Fuel Cell.

Project description:Calcination reduction reaction is used to prepare Pt/EB (emeraldine base)-XC72 (Vulcan carbon black) composites as the cathode material of a proton exchange membrane fuel cell (PEMFC). The EB-XC72 core-shell composite obtained from directly polymerizing aniline on XC72 particles is able to chelate and capture the Pt-ions before calcination. X-ray diffraction spectra demonstrate Pt particles are successfully obtained on the EB-XC72 when the calcined temperature is higher than 600 °C. Micrographs of TEM and SEM illustrate the affluent, Pt nanoparticles are uniformly distributed on EB-XC72 at 800 °C (Pt/EB-XC72/800). More Pt is deposited on Pt/EB-XC72 composite as temperatures are higher than 600 °C. The Pt/EB-XC72/800 catalyst demonstrates typical type of a cyclic voltammograms (C-V) curve of a Pt-catalyst with clear Pt-H oxidation and Pt-O reduction peaks. The highest number of transferred electrons during ORR approaches 3.88 for Pt/EB-XC72/800. The maximum power density of the single cell based on Pt/EB-XC72/800 reaches 550 mW cm-2.

| S-EPMC7182897 | biostudies-literature

Mesoporous Platinum Prepared by Electrodeposition for Ultralow Loading Proton Exchange Membrane Fuel Cells.

Project description:The porosity and utilization of platinum catalysts have a direct impact on their performance within proton exchange membrane fuel cells. It is desirable to identify methods that can prepare these catalysts with the desired features, and that can be widely implemented using existing and industrially scalable techniques. Through the use of electrodeposition processes, fuel cell testing, and electron microscopy analyses before and after fuel cell testing, we report the preparation and performance of mesoporous platinum catalysts for proton exchange membrane fuel cells. We found that these mesoporous platinum catalysts can be prepared in sufficient quantities through techniques that also enable their direct incorporation into membrane electrode assemblies. We also determined that the mesoporous catalysts achieved a high porosity, which was retained after assembly and utilization within fuel cells. In addition, these mesoporous platinum catalysts exhibited an improved platinum mass specific power over catalysts prepared from commercially available platinum nanocatalysts.

| S-EPMC6411755 | biostudies-literature

Proton Transport in Aluminum-Substituted Mesoporous Silica Channel-Embedded High-Temperature Anhydrous Proton-Exchange Membrane Fuel Cells.

Project description:Polymer composite membrane technology is promising for enhancing the performance of membrane electrode assemblies for high-temperature fuel cells. In this study, we developed a novel anhydrous proton-exchange polybenzimidazole (m-PBI) composite membrane using Al-substituted mesoporous silica (Al-MCM-41) as a proton-carrier support. The surface-substituted Al-MCM-41 formed effective proton-transport pathways via its periodic hexagonal channel and improved the proton conductivity. The proton conductivity of an m-PBI filled with 9 wt.% filler was 0.356?S?cm-1 at 160?°C and 0% humidity, representing an increase of 342% compared to that of a pristine m-PBI. Further, the current density at 0.6?V and maximum power density of m-PBI composite membranes were increased to 0.393?A?cm-2 and 0.516?W?cm-2, respectively. The enhanced fuel-cell performance was attributed to the proton-transfer channels and H3PO4 reservoirs formed by the mesopores of the Al-MCM-41 shell. The results indicated that Al-MCM-41 is suitable with respect to the hybrid homologues for enhancing the proton transport of the m-PBI membrane.

| S-EPMC7316861 | biostudies-literature

Chlorobenzene Poisoning and Recovery of Platinum-Based Cathodes in Proton Exchange Membrane Fuel Cells.

Project description:The platinum electrocatalysts found in proton exchange membrane fuel cells are poisoned both reversibly and irreversibly by air pollutants and residual manufacturing contaminants. In this work, the poisoning of a Pt/C PEMFC cathode was probed by a trace of chlorobenzene in the air feed. Chlorobenzene inhibits the oxygen reduction reaction and causes significant cell performance loss. The performance loss is largely restored by neat air operation and potential cycling between 0.08 V and 1.2 V under H2/N2 (anode/cathode). The analysis of emissions, in situ X-ray absorption spectroscopy and electrochemical impedance spectra show the chlorobenzene adsorption/reaction and molecular orientation on Pt surface depend on the electrode potential. At low potentials, chlorobenzene deposits either on top of adsorbed H atoms or on the Pt surface via the benzene ring and is converted to benzene (ca. 0.1 V) or cyclohexane (ca. 0 V) upon Cl removal. At potentials higher than 0.2 V, chlorobenzene binds to Pt via the Cl atom and can be converted to benzene (less than 0.3 V) or desorbed. Cl- is created and remains in the membrane electrode assembly. Cl- binds to the Pt surface much stronger than chlorobenzene, but can slowly be flushed out by liquid water.

| S-EPMC4570834 | biostudies-literature

Zigzag carbon as efficient and stable oxygen reduction electrocatalyst for proton exchange membrane fuel cells.

Project description:Non-precious-metal or metal-free catalysts with stability are desirable but challenging for proton exchange membrane fuel cells. Here we partially unzip a multiwall carbon nanotube to synthesize zigzag-edged graphene nanoribbons with a carbon nanotube backbone for electrocatalysis of oxygen reduction in proton exchange membrane fuel cells. Zigzag carbon exhibits a peak areal power density of 0.161 W cm-2 and a peak mass power density of 520 W g-1, superior to most non-precious-metal electrocatalysts. Notably, the stability of zigzag carbon is improved in comparison with a representative iron-nitrogen-carbon catalyst in a fuel cell with hydrogen/oxygen gases at 0.5 V. Density functional theory calculation coupled with experimentation reveal that a zigzag carbon atom is the most active site for oxygen reduction among several types of carbon defects on graphene nanoribbons in acid electrolyte. This work demonstrates that zigzag carbon is a promising electrocatalyst for low-cost and durable proton exchange membrane fuel cells.

| S-EPMC6145918 | biostudies-literature

Multi-functional anodes boost the transient power and durability of proton exchange membrane fuel cells.

Project description:Proton exchange membrane fuel cells have been regarded as the most promising candidate for fuel cell vehicles and tools. Their broader adaption, however, has been impeded by cost and lifetime. By integrating a thin layer of tungsten oxide within the anode, which serves as a rapid-response hydrogen reservoir, oxygen scavenger, sensor for power demand, and regulator for hydrogen-disassociation reaction, we herein report proton exchange membrane fuel cells with significantly enhanced power performance for transient operation and low humidified conditions, as well as improved durability against adverse operating conditions. Meanwhile, the enhanced power performance minimizes the use of auxiliary energy-storage systems and reduces costs. Scale fabrication of such devices can be readily achieved based on the current fabrication techniques with negligible extra expense. This work provides proton exchange membrane fuel cells with enhanced power performance, improved durability, prolonged lifetime, and reduced cost for automotive and other applications.

| S-EPMC7055244 | biostudies-literature

Rechargeable proton exchange membrane fuel cell containing an intrinsic hydrogen storage polymer.

Project description:Proton exchange membrane fuel cells (PEMFCs) are promising clean energy conversion devices in residential, transportation, and portable applications. Currently, a high-pressure tank is the state-of-the-art mode of hydrogen storage; however, the energy cost, safety, and portability (or volumetric hydrogen storage capacity) presents a major barrier to the widespread dissemination of PEMFCs. Here we show an 'all-polymer type' rechargeable PEMFC (RCFC) that contains a hydrogen-storable polymer (HSP), which is a solid-state organic hydride, as the hydrogen storage media. Use of a gas impermeable SPP-QP (a polyphenylene-based PEM) enhances the operable time, reaching up to ca. 10.2 s mgHSP-1, which is more than a factor of two longer than that (3.90 s mgHSP-1) for a Nafion NRE-212 membrane cell. The RCFCs are cycleable, at least up to 50 cycles. The features of this RCFC system, including safety, ease of handling, and light weight, suggest applications in mobile, light-weight hydrogen-based energy devices.

| S-EPMC9814259 | biostudies-literature

Expert assessments of the cost and expected future performance of proton exchange membrane fuel cells for vehicles.

Project description:Despite decades of development, proton exchange membrane fuel cells (PEMFCs) still lack wide market acceptance in vehicles. To understand the expected trajectories of PEMFC attributes that influence adoption, we conducted an expert elicitation assessment of the current and expected future cost and performance of automotive PEMFCs. We elicited 39 experts' assessments of PEMFC system cost, stack durability, and stack power density under a hypothetical, large-scale production scenario. Experts assessed the median 2017 automotive cost to be $75/kW, stack durability to be 4,000 hours, and stack power density to be 2.5 kW/L. However, experts ranged widely in their assessments. Experts' 2017 best cost assessments ranged from $40 to $500/kW, durability assessments ranged from 1,200 to 12,000 hours, and power density assessments ranged from 0.5 to 4 kW/L. Most respondents expected the 2020 cost to fall short of the 2020 target of the US Department of Energy (DOE). However, most respondents anticipated that the DOE's ultimate target of $30/kW would be met by 2050 and a power density of 3 kW/L would be achieved by 2035. Fifteen experts thought that the DOE's ultimate durability target of 8,000 hours would be met by 2050. In general, experts identified high Pt group metal loading as the most significant barrier to reducing cost. Recommended research and development (R&D) funding was allocated to "catalysts and electrodes," followed in decreasing amount by "fuel cell performance and durability," "membranes and electrolytes," and "testing and technical assessment." Our results could be used to inform public and private R&D decisions and technology roadmaps.

| S-EPMC6421432 | biostudies-literature

Synthesizing 2D MoS2 Nanofins on carbon nanospheres as catalyst support for Proton Exchange Membrane Fuel Cells.

Project description:Highly dense 2D MoS2 fin-like nanostructures on carbon nanospheres were fabricated and formed the main catalyst support structure in the oxygen reduction reaction (ORR) for polymer electrolyte membrane (PEM) fuel cells. These nanofins were observed growing perpendicular to the carbon nanosphere surface in random orientations and high resolution transmission electron microscope confirmed 2D layers. The PEM fuel cell test showed enhanced electrochemical activity with good stability, generating over 8.5?W.mgPt(-1) as compared to standard carbon black of 7.4?W.mgPt(-1) under normal operating conditions. Electrochemical Impedance Spectroscopy confirmed that the performance improvement is highly due to the excellent water management of the MoS2 lamellar network, which facilitates water retention at low current density and flood prevention at high current density. Reliability test further demonstrated that these nanofins are highly stable in the electrochemical reaction and is an excellent ORR catalyst support.

| S-EPMC4908422 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data