Carboxymethyl Chitosan and Its Hydrophobically Modified Derivative as pH-Switchable Emulsifiers.

ABSTRACT: The emulsification properties of carboxymethyl chitosan (CMChi) and hydrophobically modified carboxymethyl chitosan (h-CMChi) were studied as a function of pH and dodecane/water ratio. The pH was varied between 6-10, and the oil/water ratio between 0.1-2.0. In CMChi solution, the emulsion stability increased as the pH was lowered from 10 to 7, and the phase inversion was shifted from oil/water ratio 1.0 to 1.8, respectively. The system behaved differently in pH 6 due to the aggregation of CMChi and the formation of nanoparticles (?200-300 nm). No phase inversion was observed and the maximum amount of emulsified oil was reached at oil/water ratio 1.2. The h-CMChi showed similar behavior as a function of pH but, due to hydrophobic modification, the phase inversion was shifted to higher values in pH 7-10. In pH 6, the behavior was similar, but the maximum amount of emulsified oil was higher compared to CMChi. The amount of adsorbed particles correlated with the emulsified amount of oil. Reversible emulsification of dodecane was demonstrated by pH adjustment using CMChi and h-CMChi solutions. The formed emulsions were gel-like, suggesting particle-particle interaction.

SUBMITTER: Kalliola S

PROVIDER: S-EPMC6150725 | biostudies-literature | 2018 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:This study investigates the swelling of grafted polycationic brushes as a function of pH and anion type. The brushes are chitosan (CH) and chitosans with 27% and 51% degree of substitution (DS) of quaternary ammonium salt, denoted as CH-Q(25) and CH-Q(50), respectively. The water content and swelling behaviors are monitored using in situ quartz-crystal microbalance with dissipation (QCM-D). The pH varies from ~3.5 to 8.5, and the counter anion types include chloride, acetate, and citrate. At fixed pH, the water content and brush swelling increase as the DS increases. Whereas the CH-Q(50) brush layer shows symmetric swelling with a minimum near pH = 4.5, the swelling of CH and CH-Q(25) is relatively constant as pH decreases from 8.2 to 5.5, and then begins to increase near pH 4. These studies indicate that the symmetric swelling of CH-Q(50) is likely attributed to increasing protonation of primary amines for pH values below pH 6.5 and the quaternary ammonium salts above pH 6.5. At pH 4, the swelling of the CH brush increases upon exchanging the smaller chloridewith a bulkier acetate anion, which is less effective at screening intra/inter molecular repulsion. In contrast, upon exchanging the acetate with trifunctional citrate, CH and CH-Q(25) brushes collapse by 53 and 42%, respectively, because the citrate forms ionic cross-links. To test antibacterial properties, silicon oxide, CH and CH-Q(50) brush layers are exposed to 10(7)-10(8) cfu/ml of S. aureus for two days at 37 °C and exposed to stepped shear stresses in 2 min intervals. Whereas an S. aureus biofilm adheres strongly to silicon oxide and CH for stresses up to 12 dyne/cm(2), biofilms on CH-Q(50) detach at a relatively low shear stress, 1.5 dyne/cm(2). Due to their high degree of swelling that can be tuned via pH, counterion size and type, chitosan and quaternary modified chitosans have potential as responsive coatings for applications including MEMS/NEMS devices and drug eluting implants.

Dataset Information

Carboxymethyl Chitosan and Its Hydrophobically Modified Derivative as pH-Switchable Emulsifiers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets