Preparation of Carriers Based on ZnO Nanoparticles Decorated on Graphene Oxide (GO) Nanosheets for Efficient Immobilization of Lipase from Candida rugosa.

ABSTRACT: Herein, a promising carrier, graphene oxide (GO) decorated with ZnO nanoparticles, denoted as GO/ZnO composite, has been designed and constructed. This carrier was characterized by X-ray powder diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy and thermogravimetry. Then, Candida rugosa lipase (CRL) was immobilized onto the GO-based materials via physical adsorption. Our results indicated that the lipase loading amount on the GO/ZnO composites was about 73.52 mg of protein per g. In the activity assay, the novel immobilized lipase GO/ZnO@CRL, exhibited particularly excellent performance in terms of thermostability and reusability. Within 30 min at 50 °C, the free lipase, GO@CRL and ZnO@CRL had respectively lost 64%, 62% and 41% of their initial activity. However, GO/ZnO@CRL still retained its activity of 63% after 180 min at 50 °C. After reuse of the GO/ZnO@CRL 14 times, 90% of the initial activity can be recovered. Meanwhile, the relative activity of GO@CRL and ZnO@CRL was 28% and 23% under uniform conditions. Hence, GO-decorated ZnO nanoparticles may possess great potential as carriers for immobilizing lipase in a wide range of applications.

SUBMITTER: Zhang S

PROVIDER: S-EPMC6152098 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A strategy for the bioconjugation of the enzyme Candida antarctica lipase B onto titania ceramic membranes with varied pore sizes (15, 50, 150, and 300 kDa) was successfully performed. The relationship between the membrane morphology, i.e.,the pore size of the ceramic support, and bioconjugation performance was considered. Owing to the dimension of the enzyme (~33 kDa), the morphology of the ceramics allowed (50, 150, and 300 kDa) or did not allow (15 kDa) the entrance of the enzyme molecules into the porous structure. Such a strategy made it possible to better understand the changes in the material (morphology) and physicochemical features (wettability, adhesiveness, and surface charge) of the samples, which were systematically examined. The silane functionalization and enzyme immobilization were accomplished via the covalent route. The samples were characterized after each stage of the modification, which was very informative from the material point of view. As a consequence of the modification, significant changes in the contact angle, roughness, adhesion, and zeta potential were observed. For instance, for the 50 kDa membrane, the contact angle increased from 29.1 ± 1.5° for the pristine sample to 72.3 ± 1.5° after silane attachment; subsequently, it was reduced to 57.2 ± 1.5° after the enzyme immobilization. Finally, the contact angle of the bioconjugated membrane used in the enzymatic process rose to 92.9 ± 1.5°. By roughness (Sq) controlling, the following amendments were noticed: for the pristine 50 kDa membrane, Sq = 1.87 ± 0.21 µm; after silanization, Sq = 2.33 ± 0.30 µm; after enzyme immobilization, Sq = 2.74 ± 0.26 µm; and eventually, after the enzymatic process, Sq = 2.37 ± 0.27 µm. The adhesion work of the 50 kDa samples was equal to 136.41 ± 2.20 mN m-1 (pristine membrane), 94.93 ± 2.00 mN m-1 (with silane), 112.24 ± 1.90 mN m-1 (with silane and enzyme), and finally, 69.12 ± 1.40 mN m-1 (after the enzymatic process). The materials and physicochemical features changed substantially, particularly after the application of the membrane in the enzymatic process. Moreover, the impact of ceramic material morphology on the zeta potential value is here presented for the first time. With an increase in the ceramic support cut-off, the amount of immobilized lipase rose, but the specific productivity was higher for membranes possessing smaller pores, owing to the higher grafting density. For the enzymatic process, two modes of accomplishment were selected, i.e., stirred-tank and cross-flow. The latter method was characterized by a much higher effectiveness, with a resulting productivity equal to 99.7 and 60.3 µmol h-1 for the 300 and 15 kD membranes, respectively.

Dataset Information

Preparation of Carriers Based on ZnO Nanoparticles Decorated on Graphene Oxide (GO) Nanosheets for Efficient Immobilization of Lipase from Candida rugosa.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets