Facile synthesis of NiCo2S4/CNTs nanocomposites for high-performance supercapacitors.

ABSTRACT: Herein, porous NiCo2S4/CNTs nanocomposites were synthesized via a simple hydrothermal method followed by the sulphurization process using different sulfide sources. By comparing two different sulfur sources, the samples using thioacetamide as sulfide source delivered more remarkable electrochemical performance with a high specific capacitance of 1765 F g-1 at 1 A g-1 and an admirable cycling stability with capacitance retention of 71.7% at a high current density of 10 A g-1 after 5000 cycles in 2 M KOH aqueous electrolyte. Furthermore, an asymmetric supercapacitor (ASC) device was successfully fabricated with the NiCo2S4/CNTs electrode as the positive electrode and graphene as the negative electrode. The device provided a maximum energy density of 29.44 W h kg-1 at a power density of 812 W kg-1. Even at a high power density of 8006 W kg-1, the energy density still reaches 16.68 W h kg-1. Moreover, the ASC presents 89.8% specific capacitance retention after 5000 cycles at 5 A g-1. These results reveal its great potential for supercapacitors in electrochemical energy storage field.

SUBMITTER: Huang Y

PROVIDER: S-EPMC6170541 | biostudies-literature | 2018 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Facile synthesis of hybrid CNTs/NiCo2S4 composite for high performance supercapacitors.

Project description:In this work, a novel carbon nanotubes (CNTs)/NiCo2S4 composite for high performance supercapacitors was prepared via a simple chemical bath deposition combined with a post-anion exchange reaction. The morphologies and phase structures of the composites were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy (Raman), X-ray photoelectron spectroscopy (XPS) and low-temperature sorption of nitrogen (BET). The electro-chemical tests revealed that the CNT/NiCo2S4 composite exhibited high electrochemical performance, because the CNTs were used as a conductive network for the NiCo2S4 hexagonal nanoplates. Compared with pure NiCo2S4 and the mechanically mixed CNTs/NiCo2S4 composite, the CNTs/NiCo2S4 composite electrode material exhibited excellent supercapacitive performance, such as a high specific capacitance up to 1537 F/g (discharge current density of 1 A/g) and an outstanding rate capability of 78.1% retention as the discharge current density increased to 100 A/g. It is therefore expected to be a promising alternative material in the area of energy storage.

| S-EPMC4942691 | biostudies-literature

Facile synthesis of ternary graphene nanocomposites with doped metal oxide and conductive polymers as electrode materials for high performance supercapacitors.

Project description:Supercapacitors (SCs) due to their high energy density, fast charge storage and energy transfer, long charge discharge curves and low costs are very attractive for designing new generation of energy storage devices. In this work we present a simple and scalable synthetic approach to engineer ternary composite as electrode material based on combination of graphene with doped metal oxides (iron oxide) and conductive polymer (polypyrrole) with aims to achieve supercapacitors with very high gravimetric and areal capacitances. In the first step a binary composite with graphene mixed with doped iron oxide (rGO/MeFe2O4) (Me = Mn, Ni) was synthesized using new single step process with NaOH acting as a coprecipitation and GO reducing agent. This rGO/MnFe2O4 composite electrode showed gravimetric capacitance of 147 Fg-1 and areal capacitance of 232 mFcm-2 at scan rate of 5 mVs-1. In the final step a conductive polypyrrole was included to prepare a ternary composite graphene/metal doped iron oxide/polypyrrole (rGO/MnFe2O4/Ppy) electrode. Ternary composite electrode showed significantly improved gravimetric capacitance and areal capacitance of 232 Fg-1 and 395 mFcm-2 respectively indicating synergistic impact of Ppy additives. The method is promising to fabricate advanced electrode materials for high performing supercapacitors combining graphene, doped iron oxide and conductive polymers.

| S-EPMC6461681 | biostudies-literature

Facile synthesis of Al-doped NiO nanosheet arrays for high-performance supercapacitors.

Project description:Electrode material design is the key to the development of asymmetric supercapacitors with high electrochemical performances and stability. In this work, Al-doped NiO nanosheet arrays were synthesized using a facile hydrothermal method followed by a calcination process, and the synthesized arrays exhibited a superior pseudocapacitive performance, including a favourable specific capacitance of 2253 ± 105 F g-1 at a current density of 1 A g-1, larger than that of an undoped NiO electrode (1538 ± 80 F g-1). More importantly, the arrays showed a high-rate capability (75% capacitance retention at 20 A g-1) and a high cycling stability (approx. 99% maintained after 5000 cycles). The above efficient capacitive performance benefits from the large electrochemically active area and enhanced conductivity of the arrays. Furthermore, an assembled asymmetric supercapacitor based on the Al-doped NiO arrays and N-doped multiwalled carbon nanotube ones delivered a high specific capacitance of 192 ± 23 F g-1 at 0.4 A g-1 with a high-energy density of 215 ± 15 Wh kg-1 and power density of 21.6 kW kg-1. Additionally, the asymmetric device exhibited a durable cyclic stability (approx. 100% retention after 5000 cycles). This work with the proposed doping method will be beneficial to the construction of high-performance supercapacitor systems.

| S-EPMC6281943 | biostudies-literature

Facile Synthesis of Nitrogen-Doped Microporous Carbon Spheres for High Performance Symmetric Supercapacitors.

Project description:Nitrogen-doped microporous carbon spheres (NMCSs) are successfully prepared via carbonization and KOH activation of phenol-formaldehyde resin polymer spheres synthesized by a facile and time-saving one-step hydrothermal strategy using triblock copolymer Pluronic F108 as a soft template under the Stöber-like method condition. The influence of the ethanol/water volume ratios and carbonation temperatures on the morphologies, pore structures and electrochemical performances of the prepared NMCSs are investigated systematically. The optimal NMCSs have a large specific surface area of 1517 m2 g- 1 with a pore volume of 0.8 cm3 g- 1. The X-ray photo-electron spectroscopy analysis reveals a suitable nitrogen-doped content of 2.6 at.%. The as-prepared NMCSs used as supercapacitor electrode materials exhibit an outstanding specific capacitance of 416 F g- 1 at a current density of 0.2 A g- 1, also it shows an excellent charge/discharge cycling stability with 96.9% capacitance retention after 10,000 cycles. The constructed symmetric supercapacitors using PVA/KOH as the gel electrolyte can deliver a specific capacitance of 60.6 F g- 1 at current density of 1 A g- 1. A maximum energy density of 21.5 Wh kg- 1 can be achieved at a power density of 800 W kg- 1, and the energy density still maintains 13.3 Wh kg- 1 even at a high power density of 16 kW kg- 1. The results suggest that this work can open up a facile and effective way to synthesize the NMCSs for electrode materials of high performance energy storage devices.

| S-EPMC6172159 | biostudies-literature

Facile Synthesis of Manganese Cobalt Oxide/Nickel Cobalt Oxide Composites for High-Performance Supercapacitors.

Project description:Transition metal oxides (TMOs) with spinel structures have a promising potential as the electrode materials for supercapacitors application owning to its outstanding theoretical capacity, good redox activity, and eco-friendly feature. In this work, MnCo2O4.5@NiCo2O4 nanowire composites for supercapacitors has been successfully fabricated by using a mild hydrothermal approach without any surfactant. The morphology and physicochemical properties of the prepared products can be well-controlled by adjusting experimental parameters of preparation. The double spinel composite exhibits a high specific capacitance of 325 F g-1 (146 C g-1) and 70.5% capacitance retention after 3,000 cycling tests at 1 A g-1.

| S-EPMC6344439 | biostudies-literature

One-step facile synthesis of nickel-chromium layered double hydroxide nanoflakes for high-performance supercapacitors.

Project description:Rational design and synthesis of efficient electrodes with pronounced energy storage properties are crucial for supercapacitors. Herein, we report thin NiCr-layered double hydroxide nanoflakes (NiCr-LDNs) for a high-performance supercapacitor. These fabricated NiCr-LDNs, with various Ni2+/Cr3+ ratios, are one-step controllably synthesized through ultrasonication coupled with mechanical agitation, without hydrothermal treatment or extra exfoliation using organic solvents. Through comparison of different Ni2+/Cr3+ ratios, the Ni2Cr1-LDNs with a 4.7 nm thickness exhibited a superb capacitance performance of 1525 F g-1 at 2 A g-1, which is competitive with most previously reported layered double hydroxide (LDH)-based electrodes. These thin nanoflake structures have the potential to reduce the energy barrier and enhance the capture ability of electrolyte ions. Besides, an asymmetric supercapacitor (ASC) assembled using Ni2Cr1-LDNs achieved a remarkable energy density of 55.22 W h kg-1 at a power density of 400 W kg-1 and maintained high specific capacitance (over 81%), even after 5000 cycles. This work offers an efficient and facile route to fabricating LDH nanoflakes for boosting energy storage capabilities.

| S-EPMC9419058 | biostudies-literature

High-performance symmetric supercapacitors based on carbon nanotube/graphite nanofiber nanocomposites.

Project description:This work reports the nanocomposites of graphitic nanofibers (GNFs) and carbon nanotubes (CNTs) as the electrode material for supercapacitors. The hybrid CNTs/GNFs was prepared via a synthesis route that involved catalytic chemical vapor deposition (CVD) method. The structure and morphology of CNTs/GNFs can be precisely controlled by adjusting the flow rates of reactant gases. The nest shape entanglement of CNTs and GNFs which could not only have high conductivity to facilitate ion transmission, but could also increase surface area for more electrolyte ions access. When assembled in a symmetric two-electrode system, the CNTs/GNFs-based supercapacitor showed a very good cycling stability of 96% after 10 000 charge/discharge cycles. Moreover, CNTs/GNFs-based symmetric device can deliver a maximum specific energy of 72.2 Wh kg-1 at a power density of 686.0 W kg-1. The high performance of the hybrid performance can be attributed to the wheat like GNFs which provide sufficient accessible sites for charge storage, and the CNTs skeleton which provide channels for charge transport.

| S-EPMC5998012 | biostudies-literature

Facile Synthesis of Zn-Co-S Nanostrip Cluster Arrays on Ni Foam for High-Performance Hybrid Supercapacitors.

Project description:Mixed metal sulfides exhibit outstanding electrochemical performance compared to single metal sulfides and mixed metal oxides because of their richer redox reactions and high electronic conductivity. In the present study, Zn-Co-S nanostrip cluster arrays were formed from ZnCo2O4 grown on Ni foam by an anion exchange reaction using a two-step hydrothermal process. Morphological characterization confirmed that the Zn-Co-S nanostrip cluster arrays had grown homogeneously on the skeleton of the 3D Ni foam. The length of the nanostrip was approximately 8 µm, and the width ranged from 600 to 800 nm. The Ni foam-supported Zn-Co-S nanostrip cluster arrays were assessed directly for electrochemical supercapacitor applications. Compared to ZnCo2O4, the Zn-Co-S electrode exhibited a three-fold higher specific capacity of 830 C g-1 at a specific current of 2.0 A g-1. The higher polarizability, lower electro-negativity, and larger size of the S2- ion played an important role in substituting oxygen with sulfur, which enhanced the performance. The Zn-Co-S//AC hybrid device delivered a maximum specific energy of 19.0 Wh kg-1 at a specific power of 514 W kg-1. The remarkable performance of Zn-Co-S nanostrip cluster arrays highlights their potential as a positive electrode for hybrid supercapacitor applications.

| S-EPMC8706522 | biostudies-literature

Facile synthesis of crumpled nitrogen-doped porous carbon nanosheets with ultrahigh surface area for high-performance supercapacitors.

Project description:Porous carbon nanosheets are currently considered excellent electrode materials for high-performance supercapacitors. However, their ease of agglomeration and stacking nature reduce the available surface area and limit the electrolyte ion diffusion and transport, thereby leading to low capacitance and poor rate capability. To solve these problems, we report an adenosine blowing and KOH activation combination strategy to prepare crumpled nitrogen-doped porous carbon nanosheets (CNPCNS), which exhibit much higher specific capacitance and rate capability compared to flat microporous carbon nanosheets. The method is simple and capable of one-step scalable production of CNPCNS with ultrathin crumpled nanosheets, ultrahigh specific surface area (SSA), microporous and mesoporous structure and high heteroatom content. The optimized CNPCNS-800 with a thickness of 1.59 nm has an ultrahigh SSA of 2756 m2 g-1, high mesoporosity of 62.9% and high heteroatom content (2.6 at% for N, 5.4 at% for O). Consequently, CNPCNS-800 presents an excellent capacitance, high rate capability and long cycling stability both in 6 M KOH and EMIMBF4. More importantly, the energy density of the CNPCNS-800-based supercapacitor in EMIMBF4 can reach up to 94.9 W h kg-1 at 875 W kg-1 and is still 61.2 W h kg-1 at 35 kW kg-1.

| S-EPMC10044480 | biostudies-literature

Facile Synthesis of CoSe/Co<sub>3</sub>O<sub>4</sub>-CNTs/NF Composite Electrode for High-Performance Asymmetric Supercapacitor.

Project description:Electrode materials are key factors for supercapacitors to endow them with excellent electrochemical properties. Here, a novel hybrid structure of a CoSe/Co3O4-CNTs binder free composite electrode on nickel foam was prepared via a facile flame method, followed by an electrodeposition process. Benefitting from the synergetic effects of the multicomponent (with low resistances of 1.542 Ω cm2 and a moderate mesoporous size of 3.12 nm) and the enlarged specific surface area of the composite material (77.4 m2 g-1), the CoSe/Co3O4-CNTs composite electrode delivers a high specific capacitance of 2906 F g-1 at 5 mV s-1 with an excellent rate stability. The fabricated CoSe/Co3O4-CNTs/NF//AC ASC exhibits a high energy density of 43.4 Wh kg-1 at 0.8 kW kg-1 and a long cycle life (92.7% capacitance retention after 10,000 cycles).

| S-EPMC9457315 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data