Thermal Energy Storage and Mechanical Performance of Crude Glycerol Polyurethane Composite Foams Containing Phase Change Materials and Expandable Graphite.

ABSTRACT: The aim of this study was to enhance the thermal comfort properties of crude glycerol (CG) derived polyurethane foams (PUFs) using phase change materials (PCMs) (2.5⁻10.0% (wt/wt)) to contribute to the reduction of the use of non-renewable resources and increase energy savings. The main challenge when adding PCM to PUFs is to combine the low conductivity of PUFs whilst taking advantage of the heat released/absorbed by PCMs to achieve efficient thermal regulation. The solution considered to overcome this limitation was to use expandable graphite (EG) (0.50⁻1.50% (wt/wt)). The results obtained show that the use of PCMs increased the heterogeneity of the foams cellular structure and that the incorporation of PCMs and EG increased the stiffness of the ensuing composite PUFs acting as filler-reinforcing materials. However, these fillers also caused a substantial increase of the thermal conductivity and density of the ensuing foams which limited their thermal energy storage. Therefore, numerical simulations were carried using a single layer panel and the thermal and physical properties measured to evaluate the behavior of a composite PUF panel with different compositions, and guide future formulations to attain more effective results in respect to temperature buffering and temperature peak delay.

SUBMITTER: Gama NV

PROVIDER: S-EPMC6212961 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effects of Various Types of Expandable Graphite and Blackcurrant Pomace on the Properties of Viscoelastic Polyurethane Foams.

Project description:We investigated the effect of the type and amount of expandable graphite (EG) and blackcurrant pomace (BCP) on the flammability, thermal stability, mechanical properties, physical, and chemical structure of viscoelastic polyurethane foams (VEF). For this purpose, the polyurethane foams containing EG, BCP, and EG with BCP were obtained. The content of EG varied in the range of 3-15 per hundred polyols (php), while the BCP content was 30 php. Based on the obtained results, it was found that the additional introduction of BCPs into EG-containing composites allows for an additive effect in improving the functional properties of viscoelastic polyurethane foams. As a result, the composite containing 30 php of BCP and 15 php of EG with the largest particle size and expanded volume shows the largest change in the studied parameters (hardness (H) = 2.65 kPa (+16.2%), limiting oxygen index (LOI) = 26% (+44.4%), and peak heat release rate (pHRR) = 15.5 kW/m2 (-87.4%)). In addition, this composite was characterized by the highest char yield (m600 = 17.9% (+44.1%)). In turn, the change in mechanical properties is related to a change in the physical and chemical structure of the foams as indicated by scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) analysis.

| S-EPMC8038687 | biostudies-literature

The Synergistic Effect of Ionic Liquid-Modified Expandable Graphite and Intumescent Flame-Retardant on Flame-Retardant Rigid Polyurethane Foams.

Project description:In this study, a nitrogen-phosphorus intumescent flame-retardant 3-(N-diphenyl phosphate) amino propyl triethoxy silane (DPES), the ionic liquid (IL) of 1-butyl-3-methyl-imidazole phosphate, and a phosphorous-containing ionic liquid-modified expandable graphite (IL-EG), were synthesized, and their molecular structures were characterized. The flame-retardant rigid polyurethane foams (RPUFs) were compounded with synergistic flame-retardant IL-EG/DPES to study the effects of the combination IL-EG and DPES on the pore structure, mechanical properties, thermal decomposition behavior and thermal decomposition mechanism of RPUF. The results showed that IL-EG/DPES had good thermal stability, and an excellent expansibility and char yield. The flame-retardant RPUF, modified with IL-EG and DPES at the ratio of 1:1, had a relatively uniform pore size, the highest compressive strength, and an excellent flame-retardant performance due to the form interwoven hydrogen bonds between IL-EG and DPES, as well as the new synergistic flame-retardant coating on the RPUF surface to restrict the transfer of gas or heat into the PU matrix.

| S-EPMC7411720 | biostudies-literature

Viscoelastic Polyurethane Foams for Use as Auxiliary Materials in Orthopedics.

Project description:One of the essential factors in prostheses is their fitting. To assemble a prosthesis with the residual limb, so-called liners are used. Liners used currently are criticized by users for their lack of comfort, causing excessive sweating and skin irritation. The objective of the work was to develop viscoelastic polyurethane foams for use in limb prostheses. As part of the work, foams were produced with different isocyanate indexes (0.6-0.9) and water content (1, 2 and 3 php). The produced foams were characterized by scanning electron microscopy, computer microtomography, infrared spectroscopy, thermogravimetry and differential scanning calorimetry. Measurements also included apparent density, recovery time, rebound elasticity, permanent deformation, compressive stress value and sweat absorption. The results were discussed in the context of modifying the foam recipe. The performance properties of the foams, such as recovery time, hardness, resilience and sweat absorption, indicate that foams that will be suitable for prosthetic applications are foams with a water content of 2 php produced with an isocyanate index of 0.8 and 0.9.

| S-EPMC8746291 | biostudies-literature

Influence of the Characteristics of Expandable Graphite on the Morphology, Thermal Properties, Fire Behaviour and Compression Performance of a Rigid Polyurethane Foam.

Project description:Three types of expandable graphite (EG) differing in particle size and expansion volume, are compared as flame retardant additives to rigid polyurethane foams (RPUFs). In this paper we discuss microstructure, thermal stability, fire behavior, and compression performance. We find that ell size distributions were less homogeneous and cell size was reduced. Furthermore, thermal conductivity increased along with EG loading. Thermogravimetric analysis (TGA) showed that EG only increased residue yield differently. The results indicate that a higher expansion of EG increased the limiting oxygen index (LOI) value, whereas a bigger particle size EG improved the rating of the vertical burning test (UL94). Results from the cone calorimeter test showed that a bigger particle size EG effectively reduced peak of heat release rate (pHRR). Furthermore, a higher expansion, led to a decrease in smoke production (TSP). The combination of both characteristics gives extraordinary results. The physical⁻mechanical characterization of the EG/RPUF foams revealed that their compression performance decreased slightly, mostly due to the effect of a bigger size EG.

| S-EPMC6401788 | biostudies-literature

Graphene-Graphite Polyurethane Composite Based High-Energy Density Flexible Supercapacitors.

Project description:Energy autonomy is critical for wearable and portable systems and to this end storage devices with high-energy density are needed. This work presents high-energy density flexible supercapacitors (SCs), showing three times the energy density than similar type of SCs reported in the literature. The graphene-graphite polyurethane (GPU) composite based SCs have maximum energy and power densities of 10.22 µWh cm-2 and 11.15 mW cm-2, respectively, at a current density of 10 mA cm-2 and operating voltage of 2.25 V (considering the IR drop). The significant gain in the performance of SCs is due to excellent electroactive surface per unit area (surface roughness 97.6 nm) of GPU composite and high electrical conductivity (0.318 S cm-1). The fabricated SCs show stable response for more than 15 000 charging/discharging cycles at current densities of 10 mA cm-2 and operating voltage of 2.5 V (without considering the IR drop). The developed SCs are tested as energy storage devices for wide applications, namely: a) solar-powered energy-packs to operate 84 light-emitting diodes (LEDs) for more than a minute and to drive the actuators of a prosthetic limb; b) powering high-torque motors; and c) wristband for wearable sensors.

| S-EPMC6446598 | biostudies-literature

Silica-Based Aerogel Composites Reinforced with Reticulated Polyurethane Foams: Thermal and Mechanical Properties.

Project description:In this work, silica aerogel composites reinforced with reticulated polyurethane (PU) foams have been manufactured having densities in the range from 117 to 266 kg/m3 and porosities between 85.7 and 92.3%. Two different drying processes were employed (ambient pressure drying and supercritical drying) and a surface modification step was applied to some of the silica formulations. These composites, together with the reference PU foam and the monolithic silica aerogels, were fully characterized in terms of their textural properties, mechanical properties and thermal conductivities. The surface modification with hexamethyldisilazane (HMDZ) proved to improve the cohesion between the reticulated foam and the silica aerogels, giving rise to a continuous network of aerogel reinforced by a polyurethane porous structure. The samples dried under supercritical conditions showed the best interaction between matrixes as well as mechanical and insulating properties. These samples present better mechanical properties than the monolithic aerogels having a higher elastic modulus (from 130 to 450 kPa), a really exceptional flexibility and resilience, and the capacity of being deformed without breaking. Moreover, these silica aerogel-polyurethane foam (Sil-PU) composites showed an excellent insulating capacity, reaching thermal conductivities as low as 14 mW/(m·K).

| S-EPMC9318614 | biostudies-literature

Enhanced Fire Safety of Rigid Polyurethane Foam via Synergistic Effect of Phosphorus/Nitrogen Compounds and Expandable Graphite.

Project description:In order to explore highly efficient flame-retardant rigid polyurethane foam (RPUF), phosphorus/nitrogen compounds and expandable graphite (EG) were successfully incorporated into RPUF by a free one-spot method. The combustion results showed that the fire safety of the RPUF samples was remarkably improved by the addition of phosphoric/nitrogen compounds and EG. With the incorporation of 22.4 wt.% phosphorus/nitrogen compounds and 3.2 wt.% EG, the RPUF composites achieved UL-94 V-0 rating. Besides, the total heat release and total smoke release of RPUF composites were reduced by 29.6% and 32.4% respectively, compared to those of the pure RPUF sample. PO• and PO2• together with nonflammable gaseous products were evolved from phosphoric/nitrogen compounds in the gas phase, which quenched the flammable free radicals in the matrix and diluted the concentration of combustible gaseous products generated from PRUF during combustion. The compact char residues which acted as excellent physical barriers were formed by catalysis of EG and phosphoric/nitrogen compounds in the condense phase. The fire hazard of RPUF was significantly reduced by the synergistic effect of phosphorus-nitrogen compounds and EG. This work provides a promising strategy to enhance the fire safety of RPUF.

| S-EPMC7587603 | biostudies-literature

Biodegradable, Flame-Retardant, and Bio-Based Rigid Polyurethane/Polyisocyanurate Foams for Thermal Insulation Application.

Project description:This article raised the issue of studies on the use of new bio-polyol based on white mustard seed oil and 2,2'-thiodiethanol (3-thiapentane-1,5-diol) for the synthesis of rigid polyurethane/polyisocyanurate (RPU/PIR) foams. For this purpose, new formulations of polyurethane materials were prepared. Formulations contained bio-polyol content from 0 to 0.4 chemical equivalents of hydroxyl groups. An industrial flame retardant, tri(2-chloro-1-methylethyl) phosphate (Antiblaze TCMP), was added to half of the formulations. Basic foaming process parameters and functional properties, such as apparent density, compressive strength, brittleness, absorbability and water absorption, aging resistance, thermal conductivity coefficient λ, structure of materials, and flammability were examined. The susceptibility of the foams to biodegradation in soil was also examined. The increase in the bio-polyol content caused a slight increase in processing times. Also, it was noted that the use of bio-polyol had a positive effect on the functional properties of obtained RPU/PIR foams. Foams modified by bio-polyol based on mustard seed oil showed lower apparent density, brittleness, compressive strength, and absorbability and water absorption, as well as thermal conductivity, compared to the reference (unmodified) foams. Furthermore, the obtained materials were more resistant to aging and more susceptible to biodegradation.

| S-EPMC6918136 | biostudies-literature

Enhanced performance and interfacial investigation of mineral-based composite phase change materials for thermal energy storage.

Project description:A novel mineral-based composite phase change materials (PCMs) was prepared via vacuum impregnation method assisted with microwave-acid treatment of the graphite (G) and bentonite (B) mixture. Graphite and microwave-acid treated bentonite mixture (GBm) had more loading capacity and higher crystallinity of stearic acid (SA) in the SA/GBm composite. The SA/GBm composite showed an enhanced thermal storage capacity, latent heats for melting and freezing (84.64 and 84.14 J/g) was higher than those of SA/B sample (48.43 and 47.13 J/g, respectively). Addition of graphite was beneficial to the enhancement in thermal conductivity of the SA/GBm composite, which could reach 0.77 W/m K, 31% higher than SA/B and 196% than pure SA. Furthermore, atomic-level interfaces between SA and support surfaces were depicted, and the mechanism of enhanced thermal storage properties was in detail investigated.

| S-EPMC3664896 | biostudies-other