Characterization of New PEEK/HA Composites with 3D HA Network Fabricated by Extrusion Freeforming.

ABSTRACT: Addition of bioactive materials such as calcium phosphates or Bioglass, and incorporation of porosity into polyetheretherketone (PEEK) has been identified as an effective approach to improve bone-implant interfaces and osseointegration of PEEK-based devices. In this paper, a novel production technique based on the extrusion freeforming method is proposed that yields a bioactive PEEK/hydroxyapatite (PEEK/HA) composite with a unique configuration in which the bioactive phase (i.e., HA) distribution is computer-controlled within a PEEK matrix. The 100% interconnectivity of the HA network in the biocomposite confers an advantage over alternative forms of other microstructural configurations. Moreover, the technique can be employed to produce porous PEEK structures with controlled pore size and distribution, facilitating greater cellular infiltration and biological integration of PEEK composites within patient tissue. The results of unconfined, uniaxial compressive tests on these new PEEK/HA biocomposites with 40% HA under both static and cyclic mode were promising, showing the composites possess yield and compressive strength within the range of human cortical bone suitable for load bearing applications. In addition, preliminary evidence supporting initial biological safety of the new technique developed is demonstrated in this paper. Sufficient cell attachment, sustained viability in contact with the sample over a seven-day period, evidence of cell bridging and matrix deposition all confirmed excellent biocompatibility.

SUBMITTER: Vaezi M

PROVIDER: S-EPMC6273399 | biostudies-literature | 2016 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Characterization of New PEEK/HA Composites with 3D HA Network Fabricated by Extrusion Freeforming.

Vaezi Mohammad M Black Cameron C Gibbs David M R DM Oreffo Richard O C RO Brady Mark M Moshrefi-Torbati Mohamed M Yang Shoufeng S

Molecules (Basel, Switzerland) 20160526 6

Addition of bioactive materials such as calcium phosphates or Bioglass, and incorporation of porosity into polyetheretherketone (PEEK) has been identified as an effective approach to improve bone-implant interfaces and osseointegration of PEEK-based devices. In this paper, a novel production technique based on the extrusion freeforming method is proposed that yields a bioactive PEEK/hydroxyapatite (PEEK/HA) composite with a unique configuration in which the bioactive phase (i.e., HA) distributio ...[more]

PMID: 27240326

Similar Datasets

Project description:The specific objective of this study was to stabilize a simple valid method to prepare pure nanorod hydroxyapatite (HA) mixed with berberine chloride (BER) and Moghat water extract (ME) as composites for incorporation into cellulose acetate (CA) nanofibers to be used as novel bone scaffolds and to determine their efficacy in bone regeneration process In Vitro. Preparation of HA/BER and HA/ME composites were performed by mixing powders using the ball-milling machine. The HA, HA/BER, and HA/ME composites at a concentration of 6.25, 12.5, 25, 50, 100, and 200 mg were mixed with CA solution (13%), then the fiber was formed using electrospinning technique. The properties of the obtained CA fibers were investigated (SEM, TEM, EDX, FTIR, TGA, water uptake, porosity, and mechanical tests). The efficacy of HA and HA composites loaded into CA nanofiber on osteoblast and osteoclast differentiation were measured by tacking ALP, osteocalcin, TRAcP, calcium, and total protein concentration. Moreover, their effects on cell differentiation (CD90 and PARP- ɣ) and death markers (GSK3b, MAPK, Wnt-5 and β-catenin) were evaluated by using ELISA and qPCR. The obtained TEM results indicated that the continuous CA and CA/HA composites electrospun fibers have ultrafine fiber diameters of about 200 nm and uniform distribution of discrete n-HA clusters throughout. In addition, hydrocortisone (HCT) was found to increase the formation of adipocytes and osteoclastic markers CD90 and p38-MAPK which indicated the bone lose process take placed. Treatment with CA loaded with HA, HA/BER or HA/ME decreased CD90, Wnt-5, PARP- ɣ, GSK3b and p38-MAPK associated elevation of osteogenic markers: ALP and osteocalcin. Moreover, HCT overexpressed RANKL and down expressed Osterix gene. Treatment with CA/HA/BER or CA/HA/ME downregulated RANKL and upregulated Osterix associated with a reduction in RANKL/OPG ratio, at p < 0.05. In conclusion, novel CA composite nanofibers (CA/HA/BER and CA/HA/ME) reversed the HCT adverse effect on osteoblast cell death through canonical and non-canonical pathways regulated by Wnt/β-catenin and Wnt/Ca(2+) pathways. Furthermore, our data confirmed that the novel scaffolds create a crosstalk between RUNX-2, RANKL, p38-MAPK, and Wnt signals which positively impact bone regeneration process. Treatment with CA/HA/BER is better compared to the treatment with CA/HA/ME. Nevertheless, both are considered as alternative biomaterial scaffolds with a potential for biomedical applications in the field of bone tissue engineering.

Project description:Additive manufacturing promises to revolutionize manufacturing industries. However, 3D printing of novel build materials is currently limited by constraints inherent to printer designs. In this work, a bench-top powder melt extrusion (PME) 3D printer head was designed and fabricated to print parts directly from powder-based materials rather than filament. The final design of the PME printer head evolved from the Rich Rap Universal Pellet Extruder (RRUPE) design and was realized through an iterative approach. The PME printer was made possible by modifications to the funnel shape, pressure applied to the extrudate by the auger, and hot end structure. Through comparison of parts printed with the PME printer with those from a commercially available fused filament fabrication (FFF) 3D printer using common thermoplastics poly(lactide) (PLA), high impact poly (styrene) (HIPS), and acrylonitrile butadiene styrene (ABS) powders (< 1 mm in diameter), evaluation of the printer performance was performed. For each build material, the PME printed objects show comparable viscoelastic properties by dynamic mechanical analysis (DMA) to those of the FFF objects. However, due to a significant difference in printer resolution between PME (X-Y resolution of 0.8 mm and a Z-layer height calibrated to 0.1 mm) and FFF (X-Y resolution of 0.4 mm and a Z-layer height of 0.18 mm), as well as, an inherently more inconsistent feed of build material for PME than FFF, the resulting print quality, determined by a dimensional analysis and surface roughness comparisons, of the PME printed objects was lower than that of the FFF printed parts based on the print layer uniformity and structure. Further, due to the poorer print resolution and inherent inconsistent build material feed of the PME, the bulk tensile strength and Young's moduli of the objects printed by PME were lower and more inconsistent (49.2 ± 10.7 MPa and 1620 ± 375 MPa, respectively) than those of FFF printed objects (57.7 ± 2.31 MPa and 2160 ± 179 MPa, respectively). Nevertheless, PME print methods promise an opportunity to provide a platform on which it is possible to rapidly prototype a myriad of thermoplastic materials for 3D printing.

Dataset Information

Characterization of New PEEK/HA Composites with 3D HA Network Fabricated by Extrusion Freeforming.

Publications

Characterization of New PEEK/HA Composites with 3D HA Network Fabricated by Extrusion Freeforming.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets