Poly(glycerol sebacate)-Based Polyester-Polyether Copolymers and Their Semi-Interpenetrated Networks with Thermoplastic Poly(ester-ether) Elastomers: Preparation and Properties.

ABSTRACT: Poly(glycerol sebacate) (PGS), produced from renewable monomers such as sebacic acid and glycerol, has been explored extensively for various biomedical applications. However, relatively less attention has been paid to explore PGS as sustainable materials in applications such as elastomers and rigid plastics, primarily because of serious deficiencies in physical properties of PGS. Here, we present two new approaches for enhancing the properties of PGS; (i) synthesizing block copolymers of PGS with poly(tetramethylene oxide)glycol (PTMO) and (ii) preparing a blend of PGS-b-PTMO with a poly(ester-ether) thermoplastic elastomer. The consequence of molar ratio (hard and soft segments) and M n of soft segment on tensile properties of the material was investigated. The PGS-b-PTMO with 25:75 mole ratios of hard and soft segments and having a medium M n soft segment (5350 g mol-1) exhibits an appreciable increase in percentage of elongation that is from 32% for PGS to 737%. Blends of PGS-b-PTMO and a thermoplastic polyester elastomer, Hytrel 3078, form a semi-interpenetrated polymer network, which exhibits increased tensile strength to 2.11 MPa and percentage of elongation to 2574. An elongation of such magnitude is unprecedented in the literature for predominantly aliphatic polyesters and demonstrates that the simple polyester can be tailored for superior performance.

SUBMITTER: Wilson R

PROVIDER: S-EPMC6312632 | biostudies-literature | 2018 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Poly(glycerol sebacate)-Based Polyester-Polyether Copolymers and Their Semi-Interpenetrated Networks with Thermoplastic Poly(ester-ether) Elastomers: Preparation and Properties.

Wilson Runcy R Divakaran Anumon V AV S Kiran K Varyambath Anuraj A Kumaran Alaganandam A Sivaram Swaminathan S Ragupathy Lakshminarayanan L

ACS omega 20181228 12

Poly(glycerol sebacate) (PGS), produced from renewable monomers such as sebacic acid and glycerol, has been explored extensively for various biomedical applications. However, relatively less attention has been paid to explore PGS as sustainable materials in applications such as elastomers and rigid plastics, primarily because of serious deficiencies in physical properties of PGS. Here, we present two new approaches for enhancing the properties of PGS; (i) synthesizing block copolymers of PGS wit ...[more]

PMID: 30613821

Similar Datasets

Project description:Thermoplastic elastomers benefit from high elasticity and straightforward (re)processability; they are widely used across a multitude of sectors. Currently, the majority derive from oil, do not degrade or undergo chemical recycling. Here a new series of ABA triblock polyesters are synthesized and show high-performances as degradable thermoplastic elastomers; their composition is poly(cyclohexene-alt-phthalate)-b-poly(ε-decalactone)-b-poly(cyclohexene-alt-phthalate) {PE-PDL-PE}. The synthesis is accomplished using a zinc(ii)/magnesium(ii) catalyst, in a one-pot procedure where ε-decalactone ring-opening polymerization yielding dihydroxyl telechelic poly(ε-decalatone) (PDL, soft-block) occurs first and, then, addition of phthalic anhydride/cyclohexene oxide ring-opening copolymerization delivers semi-aromatic polyester (PE, hard-block) end-blocks. The block compositions are straightforward to control, from the initial monomer stoichiometry, and conversions are high (85-98%). Two series of polyesters are prepared: (1) TBPE-1 to TBPE-5 feature an equivalent hard-block volume fraction (f hard = 0.4) and variable molar masses 40-100 kg mol-1; (2) TBPE-5 to TBPE-9 feature equivalent molar masses (∼100 kg mol-1) and variable hard-block volume fractions (0.12 < f hard < 0.4). Polymers are characterized using spectroscopies, size-exclusion chromatography (SEC), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA). They are amorphous, with two glass transition temperatures (∼-51 °C for PDL; +138 °C for PE), and block phase separation is confirmed using small angle X-ray scattering (SAXS). Tensile mechanical performances reveal thermoplastic elastomers (f hard < 0.4 and N > 1300) with linear stress-strain relationships, high ultimate tensile strengths (σ b = 1-5 MPa), very high elongations at break (ε b = 1000-1900%) and excellent elastic recoveries (98%). There is a wide operating temperature range (-51 to +138 °C), an operable processing temperature range (+100 to +200 °C) and excellent thermal stability (T d,5% ∼ 300 °C). The polymers are stable in aqueous environments, at room temperature, but are hydrolyzed upon gentle heating (60 °C) and treatment with an organic acid (para-toluene sulfonic acid) or a common lipase (Novozyme® 51032). The new block polyesters show significant potential as sustainable thermoplastic elastomers with better properties than well-known styrenic block copolymers or polylactide-derived elastomers. The straightforward synthesis allows for other commercially available and/or bio-derived lactones, epoxides and anhydrides to be developed in the future.

Project description:Thermoplastic elastomers (TPEs) that are closed-loop recyclable are needed in a circular material economy, but many current materials degrade during recycling, and almost all are pervasive hydrocarbons. Here, well-controlled block polyester TPEs featuring regularly placed sodium/lithium carboxylate side chains are described. They show significantly higher tensile strengths than unfunctionalized analogues, with high elasticity and elastic recovery. The materials are prepared using controlled polymerizations, exploiting a single catalyst that switches between different polymerization cycles. ABA block polyesters of high molar mass (60-100 kg mol-1; 21 wt % A-block) are constructed using the ring-opening polymerization of ε-decalactone (derived from castor oil; B-block), followed by the alternating ring-opening copolymerization of phthalic anhydride with 4-vinyl-cyclohexene oxide (A-blocks). The polyesters undergo efficient functionalization to install regularly placed carboxylic acids onto the A blocks. Reacting the polymers with sodium or lithium hydroxide controls the extent of ionization (0-100%); ionized polymers show a higher tensile strength (20 MPa), elasticity (>2000%), and elastic recovery (>80%). In one case, sodium functionalization results in 35× higher stress at break than the carboxylic acid polymer; in all cases, changing the quantity of sodium tunes the properties. A leading sample, 2-COONa75 (M n 100 kg mol-1, 75% sodium), shows a wide operating temperature range (-52 to 129 °C) and is recycled (×3) by hot-pressing at 200 °C, without the loss of mechanical properties. Both the efficient synthesis of ABA block polymers and precision ionization in perfectly alternating monomer sequences are concepts that can be generalized to many other monomers, functional groups, and metals. These materials are partly bioderived and have degradable ester backbone chemistries, deliver useful properties, and allow for thermal reprocessing; these features are attractive as future sustainable TPEs.

Dataset Information

Poly(glycerol sebacate)-Based Polyester-Polyether Copolymers and Their Semi-Interpenetrated Networks with Thermoplastic Poly(ester-ether) Elastomers: Preparation and Properties.

Publications

Poly(glycerol sebacate)-Based Polyester-Polyether Copolymers and Their Semi-Interpenetrated Networks with Thermoplastic Poly(ester-ether) Elastomers: Preparation and Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets