Zn-alloy provides a novel platform for mechanically stable bioresorbable vascular stents.

ABSTRACT: Metallic Zn alloys have recently gained interest as potential candidates for developing platforms of bioresorbable vascular stents (BVS). Previous studies revealed that Mg alloys used for BVS can degrade too early, whereas PLLA materials may fail to provide effective scaffolding properties. Here we report on results of a new bioresorbable, metallic stent made from a Zn-Ag alloy studied in a porcine animal model of thrombosis and restenosis. While the tensile strength (MPa) of Zn-3Ag was higher than that of PLLA and resembled Mg's (WE43), fracture elongation (%) of Zn-3Ag was much greater (18-fold) than the PLLA's or Mg alloy's (WE43). Zn-3Ag exposed to HAoSMC culture medium for 30 days revealed degradation elements consisting of Zn, O, N, C, P, and Na at a 6 nm surface depth. Platelet adhesion rates and blood biocompatibility did not differ between Zn-3Ag, PLLA, Mg (WE43), and non-resorbable Nitinol (NiTi) stent materials. Balloon-expandable Zn-3Ag alloy BVS implanted into iliofemoral arteries of 15 juvenile domestic pigs were easily visible fluoroscopically at implantation, and their bioresorption was readily detectable via X-ray over time. Histologically, arteries with Zn-3Ag BVS were completely endothelialized, covered with neointima, and were patent at 1, 3, and 6 months follow-up with no signs of stent thrombosis. Zn-3Ag alloy appears to be a promising material platform for the fabrication of a new generation of bioresorbable vascular stents.

SUBMITTER: Hehrlein C

PROVIDER: S-EPMC6314592 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Zn-alloy provides a novel platform for mechanically stable bioresorbable vascular stents.

Hehrlein Christoph C Schorch Björn B Kress Nadia N Arab Amina A von Zur Mühlen Constantin C Bode Christoph C Epting Thomas T Haberstroh Jörg J Mey Lilly L Schwarzbach Hans H Kinscherf Ralf R Stachniss Vitus V Schiestel Stefanie S Kovacs Adalbert A Fischer Harald H Nennig Ernst E

PloS one 20190102 1

Metallic Zn alloys have recently gained interest as potential candidates for developing platforms of bioresorbable vascular stents (BVS). Previous studies revealed that Mg alloys used for BVS can degrade too early, whereas PLLA materials may fail to provide effective scaffolding properties. Here we report on results of a new bioresorbable, metallic stent made from a Zn-Ag alloy studied in a porcine animal model of thrombosis and restenosis. While the tensile strength (MPa) of Zn-3Ag was higher t ...[more]

PMID: 30601854

Similar Datasets

Project description:BackgroundBioresorbable vascular scaffolds (BVS) were designed to reduce the rate of late adverse events observed in conventional drug-eluting stents (DES) by dissolving once they have restored lasting patency.ObjectivesCompare the safety and efficacy of BVS versus DES in patients receiving percutaneous coronary intervention for coronary artery disease across a complete range of randomised controlled trial (RCT) follow-up intervals.MethodsA systematic review and meta-analysis was performed using Preferred Reporting Items for Systematic Reviews and Meta-Analyses guidelines. MEDLINE, EMBASE and Web of Science were searched from inception through 5 January 2022 for RCTs comparing the clinical outcomes of BVS versus DES. The primary safety outcome was stent/scaffold thrombosis (ST), and the primary efficacy outcome was target lesion failure (TLF: composite of cardiac death, target vessel myocardial infarction (TVMI) and ischaemia-driven target lesion revascularisation (ID-TLR)). Secondary outcomes were patient-oriented composite endpoint (combining all-death, all-MI and all-revascularisation), its individual components and those of TLF. Studies were appraised using Cochrane's Risk of Bias tool and meta-analysis was performed using RevMan V.5.4.Results11 919 patients were randomised to receive either BVS (n=6438) or DES (n=5481) across 17 trials (differing follow-up intervals from 3 months to 5 years). BVS demonstrated increased risk of ST across all timepoints (peaking at 2 years with risk ratio (RR): 3.47; 95% CI 1.80 to 6.70; p=0.0002). Similarly, they showed increased risk of TLF (peaking at 3 years, RR: 1.35; 95% CI 1.07 to 1.70; p=0.01) resulting from high rates of TVMI and ID-TLR. Though improvements were observed after device dissolution (5-year follow-up), these were non-significant. All other outcomes were statistically equivalent. Applicability to all BVS is limited by 91% of the BVS group receiving Abbott's Absorb.ConclusionThis meta-analysis demonstrates that current BVS are inferior to contemporary DES throughout the first 5 years at minimum.

Dataset Information

Zn-alloy provides a novel platform for mechanically stable bioresorbable vascular stents.

Publications

Zn-alloy provides a novel platform for mechanically stable bioresorbable vascular stents.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets