Role of membrane pore polymerization conditions for pH responsive behavior, catalytic metal nanoparticle synthesis, and PCB degradation.

ABSTRACT: This article describes the effects of changing monomer and cross-linker concentrations on the mass gain, water permeability, Pd-Fe nanoparticle (NP) loading, and the rate of degradation of 3,3',4,4',5-pentachlorobiphenyl (PCB 126) of pore functionalized polyvinylidene fluoride (PVDF) membranes. In this study, monomer (acrylic acid (AA)) and cross-linker (N, N'- methylene-bis (acrylamide)) concentrations were varied from 10 to 20 wt% of polymer solution and 0.5-2 mol% of monomer concentration, respectively. Results showed that responsive behavior of membrane could be tuned in terms of water permeability over a range of 270-1 L m-2 h-1 bar-1, which is a function of water pH. The NP size on the membrane surface was found in the range of 16-23 nm. With increasing cross-linker density the percentage of smaller NPs (< 10 nm) increases due to smaller mesh size formation during in-situ polymerization of membrane. NP loading was found to vary from 0.21 to 0.94 mg per cm2 of membrane area depending on the variation of available carboxyl groups in membrane pore domain. The NPs functionalized membranes were then tested for use as a platform for the degradation of PCB 126. The observed batch reaction rate (Kobs) for PCB 126 degradation for per mg of catalyst loading was found 0.08-0.1 h-1. Degradation study in convective flow mode shows 98.6% PCB 126 is degraded at a residence time of 46.2 s. The corresponding surface area normalized reaction rate (K sa ) is found about two times higher than K sa of batch degradation; suggesting elimination of the effect of diffusion resistance for degradation of PCB 126 in convective flow mode operation. These Pd-Fe-PAA-PVDF membranes and nanoparticles are characterized by TGA, contact angle measurement, surface zeta potential, XRD, SEM, XPS, FIB, TEM and other techniques reveal the details about the membrane surface, pores and nanoparticles size, shape and size-distribution. Statistical analysis based on experimental results allows us to depict responsive behavior of functionalized membrane. In our best knowledge this paper first time reports detail study on responsive behavior of pore functionalized membrane in terms of permeability, NPs size, metal loading and its effect on PCB 126 degradation in a quantified approach.

SUBMITTER: Islam MS

PROVIDER: S-EPMC6358284 | biostudies-literature | 2018 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Role of membrane pore polymerization conditions for pH responsive behavior, catalytic metal nanoparticle synthesis, and PCB degradation.

Islam Md Saiful MS Hernández Sebastián S Wan Hongyi H Ormsbee Lindell L Bhattacharyya Dibakar D

Journal of membrane science 20180323

This article describes the effects of changing monomer and cross-linker concentrations on the mass gain, water permeability, Pd-Fe nanoparticle (NP) loading, and the rate of degradation of 3,3',4,4',5-pentachlorobiphenyl (PCB 126) of pore functionalized polyvinylidene fluoride (PVDF) membranes. In this study, monomer (acrylic acid (AA)) and cross-linker (N, N'- methylene-bis (acrylamide)) concentrations were varied from 10 to 20 wt% of polymer solution and 0.5-2 mol% of monomer concentration, re ...[more]

PMID: 30718939

Similar Datasets

Project description:We previously developed a pH-responsive copper-doxorubicin (CuDox) cargo in lysolipid-based temperature-sensitive liposomes (LTSLs). The CuDox complex is released from the particle by elevated temperature; however, full release of doxorubicin from CuDox requires a reduced pH, such as that expected in lysosomes. The primary goal of this study is to evaluate the cellular uptake and intracellular trafficking of the drug-metal complex in comparison with intact liposomes and free drug. We found that the CuDox complex was efficiently internalized by mammary carcinoma cells after release from LTSLs. Intracellular doxorubicin and copper were 6-fold and 5-fold greater, respectively, after a 0.5h incubation with the released CuDox complex, as compared to incubation with intact liposomes containing the complex. Total cellular doxorubicin fluorescence was similar following CuDox and free doxorubicin incubation. Imaging and mass spectrometry assays indicated that the CuDox complex was initially internalized intact but breaks down over time within cells, with intracellular copper decreasing more rapidly than intracellular doxorubicin. Doxorubicin fluorescence was reduced when complexed with copper, and nuclear fluorescence was reduced when cells were incubated with the CuDox complex as compared with free doxorubicin. Therapeutic efficacy, which typically results from intercalation of doxorubicin with DNA, was equivalent for the CuDox complex and free doxorubicin and was superior to that of liposomal doxorubicin formulations. Taken together, the results suggest that quenched CuDox reaches the nucleus and remains efficacious. In order to design protocols for the use of these temperature-sensitive particles in cancer treatment, the timing of hyperthermia relative to drug administration must be examined. When cells were heated to 42°C prior to the addition of free doxorubicin, nuclear drug accumulation increased by 1.8-fold in cancer cells after 5h, and cytotoxicity increased 1.4-fold in both cancer and endothelial cells. Endothelial cytotoxicity was similarly augmented with mild hyperthermia applied prior to treatment with released CuDox. In summary, we find that the drug-metal complex formed in temperature-sensitive particles can be internalized by cancer and endothelial cells resulting in therapeutic efficacy that is similar to free doxorubicin, and this efficacy can be enhanced by elevated temperature.

Project description:Protein subunit vaccines offer important potential advantages over live vaccine vectors but generally elicit weaker and shorter-lived cellular immune responses. Here we investigate the use of pH-responsive, endosomolytic polymer nanoparticles that were originally developed for RNA delivery as vaccine delivery vehicles for enhancing cellular and humoral immune responses. Micellar nanoparticles were assembled from amphiphilic diblock copolymers composed of an ampholytic core-forming block and a redesigned polycationic corona block doped with thiol-reactive pyridyl disulfide groups to enable dual-delivery of antigens and immunostimulatory CpG oligodeoxynucleotide (CpG ODN) adjuvants. Polymers assembled into 23 nm particles with simultaneous packaging of CpG ODN and a thiolated protein antigen, ovalbumin (ova). Conjugation of ova to nanoparticles significantly enhanced antigen cross-presentation in vitro relative to free ova or an unconjugated, physical mixture of the parent compounds. Subcutaneous vaccination of mice with ova-nanoparticle conjugates elicited a significantly higher CD8(+) T cell response (0.5% IFN-γ(+) of CD8(+)) compared to mice vaccinated with free ova or a physical mixture of the two components. Significantly, immunization with ova-nanoparticle conjugates electrostatically complexed with CpG ODN (dual-delivery) enhanced CD8(+) T cell responses (3.4% IFN-γ(+) of CD8(+)) 7-, 18-, and 8-fold relative to immunization with conjugates, ova administered with free CpG, or a formulation containing free ova and CpG complexed to micelles, respectively. Similarly, dual-delivery carriers significantly increased CD4(+)IFN-γ(+) (Th1) responses and elicited a balanced IgG1/IgG2c antibody response. Intradermal administration further augmented cellular immune responses, with dual-delivery carriers inducing ∼7% antigen-specific CD8(+) T cells. This work demonstrates the ability of pH-responsive, endosomolytic nanoparticles to actively promote antigen cross-presentation and augment cellular and humoral immune responses via dual-delivery of protein antigens and CpG ODN. Hence, pH-responsive polymeric nanoparticles offer promise as a delivery platform for protein subunit vaccines.

Project description:Nanosized zeolitic imidazolate framework particles (ZIF-8 nanoparticles [NPs]) have strong potential as effective carriers for both in vivo and in vitro protein drug delivery. Synthesis of ZIF-8 and stability of protein encapsulation within ZIF-8 are affected by several factors, notably the metal ion source and molar ratio. To systematically investigate these factors, we investigated such effects using BSA as a model test protein to synthesize BSA@ZIF-8 NPs at various metal-to-ligand (M:L) ratios. SEM, FTIR, XRD, and DLS were applied to characterize the morphology and structure of BSA@ZIF-8 NPs and their effects on protein loading capacity. Degradation kinetics and protein release behavior of BSA@ZIF-8 NPs were evaluated at pH 5.0 (to simulate the tumor environment) and pH 7.4 (to mimic the blood environment). Our objective was to define optimal combinations of the high protein loading rate and rapid release under varying pH conditions, and we found that (i) the yield of BSA@ZIF-8 NPs decreased as the M:L ratio increased, but the protein content increased. This highlights the need to strike a balance between cost-effectiveness and practicality when selecting ZIF-8 NPs with different molar ratios for protein-based drug formulation. (ii) BSA@ZIF-8 NPs exhibited cruciate flower-like shapes when synthesized using Zn(NO3)2 as the zinc precursor at M:L ratios of 1:16 or 1:20. In all other cases, the NPs displayed a regular rhombic dodecahedral structure. Notably, the release behavior of the NPs did not differ significantly between these morphologies. (iii) When Zn(OAc)2 was used as the zinc precursor, the synthesized ZIF-8 NPs exhibited a smaller size compared to the Zn(NO3)2-derived ZIF-8 NPs. (iv) The release rate and amount of BSA protein were higher at pH 5.0 compared to pH 7.4. (v) Among the different formulations, BSA@ZIF-8 with an M:L ratio of 1:16 at pH 5.0 was observed to have a shorter time to reach a plateau (0.5 h) and higher protein release, making it suitable for locally rapid administration in a tumor environment. BSA@ZIF-8 prepared from Zn(OAc)2 at an M:L ratio of 1:140 showed the slower release of BSA protein over a 24-h period, indicating its suitability for sustained release delivery. In conclusion, our findings provide a useful basis for the practical application of ZIF-8 NPs in protein-based drug delivery systems.

Dataset Information

Role of membrane pore polymerization conditions for pH responsive behavior, catalytic metal nanoparticle synthesis, and PCB degradation.

Publications

Role of membrane pore polymerization conditions for pH responsive behavior, catalytic metal nanoparticle synthesis, and PCB degradation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets