Optimizing Blended Collagen-Fibrin Hydrogels for Cardiac Tissue Engineering with Human iPSC-derived Cardiomyocytes.

ABSTRACT: Natural polymer hydrogels are used ubiquitously as scaffold materials for cardiac tissue engineering as well as for soft tissue engineering more broadly because of FDA approval, minimal immunogenicity, and well-defined physiological clearance pathways. However, the relationships between natural polymer hydrogels and resident cell populations in directing the development of engineered tissues are poorly defined. This interaction is of particular concern for tissues prepared with iPSC-derived cell populations, in which population purity and batch-to-batch variability become additional critical factors to consider. Herein, the design space for a blended fibrin and collagen scaffold is characterized for applications in creating engineered myocardium with human iPSC-derived cardiomyocytes. Stiffness values of the acellular hydrogel formulations approach those of native myocardium in compression, but deviate significantly in tension when compared to rat myocardium in both transverse and longitudinal fiber orientations. A response surface methodology approach to understanding the relationship between collagen concentration, fibrin concentration, seeding density, and cardiac purity found a statistically significant predictive model across three repeated studies that confirms that all of these factors contribute to tissue compaction. In these constructs, increased fibrin concentration and seeding density were each associated with increased compaction, while increased collagen concentration was associated with decreased compaction. Both the lowest (24.4% cTnT⁺) and highest (60.2% cTnT⁺) cardiomyocyte purities evaluated were associated with decreased compaction, whereas the greatest compaction was predicted to occur in constructs prepared with a 40-50% cTnT⁺ population. Constructs prepared with purified cardiomyocytes (≥75.5% cTnT⁺) compacted and formed syncytia well, although increased fibrin concentration in these groups was associated with decreased compaction, a reversal of the trend observed in unpurified cardiomyocytes. This study demonstrates an analytical approach to understanding cell-scaffold interactions in engineered tissues and provides a foundation for the development of more sophisticated and customized scaffold platforms for human cardiac tissue engineering.

SUBMITTER: Kaiser NJ

PROVIDER: S-EPMC6372981 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Myocardial infarction (MI) causes significant cell loss and damage to myocardium. Cell-based therapies for treatment of MI aim to remuscularize the resultant scar tissue, but the majority of transplanted cells do not survive or integrate with the host tissue. Scaffolds can improve cell retention following construct implantation, but often do little to enhance host-graft integration and/or show limited biodegradation. Fibrin is an ideal biomaterial for cardiac tissue engineering as it is a natural, biodegradable polymer that can induce neovascularization, promote cell attachment, and has tunable mechanical properties. Here we describe a novel, high-density microtemplated fibrin scaffold seeded with a tri-cell mixture of cardiomyocytes, endothelial cells (ECs), and fibroblasts to mimic native cardiac tissue in structure and cellular composition to improve cell retention and promote integration with the host tissue. Scaffolds were designed with uniform architecture of parallel 60 ?m microchannels surrounded by an interconnected microporous network of 27-?m-diameter pores and mechanical stiffness comparable to native cardiac tissues (70-90kPa). Scaffold degradation was controlled with the addition of Factor XIII (FXIII) and/or protease inhibitor (aprotinin). Unmodified scaffolds had a fast degradation profile both in vitro (19.9%±3.9% stiffness retention after 10 days) and in vivo. Scaffolds treated with FXIII showed an intermediate degradation profile in vitro (45.8%±5.9%), while scaffolds treated with aprotinin or both FXIII and aprotinin showed significantly slowed degradation in vitro (60.9%±5.2% and 76.4%±7.6%, respectively, p<0.05). Acellular aprotinin scaffold myocardial implants showed decreased collagen deposition after 7 days. Unmodified and aprotinin implants could not be located by 14 days, while 2 of 8 FXIII implants were found, but were significantly degraded. Constructs supported seeded cell survival and organization in vitro, promoting EC-lined lumen structure formation in construct channels and colocalization of viable ECs and cardiomyocytes. In addition, constructs promoted extracellular matrix deposition by seeded cells, as shown by collagen staining within construct channels and by significant increases in construct stiffness over 10 days in vitro (209%±32%, p<0.05). The data suggest our fibrin scaffolds are ideally designed to promote graft cell survival and organization, thus improving chances of promoting construct integration with the host tissue upon implantation.

Project description:Fibrin has been used clinically for wound coverings, surgical glues, and cell delivery because of its affordability, cytocompatibility, and ability to modulate angiogenesis and inflammation. However, its rapid degradation rate has limited its usefulness as a scaffold for 3D cell culture and tissue engineering. Previous studies have sought to slow the degradation rate of fibrin with the addition of proteolysis inhibitors or synthetic crosslinkers that require multiple functionalization or polymerization steps. These strategies are difficult to implement in vivo and introduce increased complexity, both of which hinder the use of fibrin in research and medicine. Previously, we demonstrated that additional crosslinking of fibrin gels using bifunctionalized poly(ethylene glycol)-n-hydroxysuccinimide (PEG-NHS) slows the degradation rate of fibrin. In this study, we aimed to further improve the longevity of these PEG-fibrin gels such that they could be used for tissue engineering in vitro or in situ without the need for proteolysis inhibitors. It is well documented that increasing the salinity of fibrin precursor solutions affects the resulting gel morphology. Here, we investigated whether this altered morphology influences the fibrin degradation rate. Increasing the final sodium chloride (NaCl) concentration from 145 mM (physiologic level) to 250 mM resulted in fine, transparent high-salt (HS) fibrin gels that degrade 2-3 times slower than coarse, opaque physiologic-salt (PS) fibrin gels both in vitro (when treated with proteases and when seeded with amniotic fluid stem cells) and in vivo (when injected subcutaneously into mice). Increased salt concentrations did not affect the viability of encapsulated cells, the ability of encapsulated endothelial cells to form rudimentary capillary networks, or the ability of the gels to maintain induced pluripotent stem cells. Finally, when implanted subcutaneously, PS gels degraded completely within one week while HS gels remained stable and maintained viability of seeded dermal fibroblasts. To our knowledge, this is the simplest method reported for the fabrication of fibrin gels with tunable degradation properties and will be useful for implementing fibrin gels in a wide range of research and clinical applications.