Characterizing fretting damage in different test media for cardiovascular device durability testing.

ABSTRACT: In vitro durability tests of cardiovascular devices are often used to evaluate the potential for fretting damage during clinical use. Evaluation of fretting damage is important because severe fretting can concentrate stress and lead to the loss of structural integrity. Most international standards call for the use of phosphate buffered saline (PBS) for such tests although there has been little evidence to date that the use of PBS is appropriate in terms of predicting the amount of fretting damage that would occur in vivo. In order to determine an appropriate test media for in vitro durability tests where fretting damage is being evaluated, we utilized an in vitro test that is relevant to cardiovascular devices both in terms of dimensions and materials (nitinol, cobalt-chromium, and stainless steel) to characterize fretting damage in PBS, deionized water (DIW), and heparinized porcine blood. Overall, tests conducted in blood were found to have increased levels of fretting damage over tests in DIW or PBS, although the magnitude of this difference was smaller than the variability for each test media. Tests conducted in DIW and PBS led to mostly similar amounts of fretting damage with the exception of one material combination where DIW had greatly reduced damage compared to PBS and blood. Differences in fretting damage among materials were also observed with nitinol having less fretting damage than stainless steel or cobalt-chromium. In general, evaluating fretting damage in PBS or DIW may be appropriate although caution should be used when selecting test media and interpreting results given some of the differences observed across different materials.

SUBMITTER: Weaver JD

PROVIDER: S-EPMC6374031 | biostudies-literature | 2018 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Characterizing fretting damage in different test media for cardiovascular device durability testing.

Weaver J D JD Ramirez L L Sivan S S Di Prima M M

Journal of the mechanical behavior of biomedical materials 20180404

In vitro durability tests of cardiovascular devices are often used to evaluate the potential for fretting damage during clinical use. Evaluation of fretting damage is important because severe fretting can concentrate stress and lead to the loss of structural integrity. Most international standards call for the use of phosphate buffered saline (PBS) for such tests although there has been little evidence to date that the use of PBS is appropriate in terms of predicting the amount of fretting damag ...[more]

PMID: 29653383

Similar Datasets

Project description:Thrombus formation in blood-contacting medical devices is a major concern in the medical device industry, limiting the clinical efficacy of these devices. Further, a locally formed clot within the device has the potential to detach from the surface, posing a risk of embolization. Clot embolization from blood-contacting cardiovascular devices can result in serious complications like acute ischemic stroke and myocardial infarction. Therefore, clot embolization associated with device-induced thrombosis can be life-threatening and requires an enhanced fundamental understanding of embolization characteristics to come up with advanced intervention strategies. Therefore, this work aims to investigate the adhesive characteristics of blood clots on common biocompatible materials used in various cardiovascular devices. This study focuses on characterizing the adhesion strength of blood clots on materials such as polytetrafluoroethylene (PTFE), polyurethane (PU), polyether ether ketone (PEEK), nitinol, and titanium, frequently used in medical devices. In addition, the effect of incubation time on clot adhesion is explored. Results from this work demonstrated strongest clot adhesion to titanium with 3 h of incubation resulting in 1.06 ± 0.20 kPa detachment stresses. The clot adhesion strength on titanium was 51.5% higher than PEEK, 35.9% higher than PTFE, 63.1% higher than PU, and 35.4% higher than nitinol. Further, adhesion strength increases with incubation time for all materials. The percentage increase in detachment stress over incubation time (ranging from 30 min to 3 h) for polymers ranged from at least 108.75% (PEEK), 140.74% (PU), to 151.61% (PTFE). Whereas, for metallic surfaces, the percentage rise ranged from 70.21% (nitinol) to 89.28% (titanium). Confocal fluorescence imaging of clot remnants on the material surfaces revealed a well-bounded platelet-fibrin network at the residual region, representing a comparatively higher adhesive region than the non-residual zone of the surface.

Project description:Background: Hepatic knockdown of the proprotein convertase subtilisin/kexin type 9 (PCSK9) gene or the angiopoietin-like 3 (ANGPTL3) gene has been demonstrated to reduce blood low-density lipoprotein cholesterol (LDL-C) levels, and hepatic knockdown of the angiotensinogen (AGT) gene has been demonstrated to reduce blood pressure. Genome editing can productively target each of these three genes in hepatocytes in the liver, offering the possibility of durable “one-and-done” therapies for hypercholesterolemia and hypertension. However, concerns around making permanent gene sequence changes via DNA strand breaks might hinder acceptance of these therapies. Epigenome editing offers an alternative approach to gene inactivation, via silencing of gene expression by methylation of the promoter region, but the long-term durability of epigenome editing remains to be established. Objectives and Results: We assessed the ability of epigenome editing to durably reduce the expression of the human PCSK9, ANGPTL3, and AGT genes in HuH-7 hepatoma cells. Cells treated with the CRISPRoff epigenome editor and PCSK9 guide RNAs were maintained for up to 124 cell doublings and demonstrated durable knockdown of gene expression and increased CpG dinucleotide methylation in the promoter, exon 1, and intron 1 regions. In contrast, cells treated with CRISPRoff and ANGPTL3 guide RNAs experienced only transient knockdown of gene expression. Cells treated with CRISPRoff and AGT guide RNAs also experienced transient knockdown of gene expression; although initially there was increased CpG methylation throughout the early part of the gene, this methylation was geographically heterogeneous—transient in the promoter, and stable in intron 1.Conclusions: This work demonstrates precise and durable gene regulation via methylation, supporting a new therapeutic approach for protection against cardiovascular disease via knockdown of genes such as PCSK9. However, the durability of knockdown with methylation changes is not generalizable across target genes, likely limiting the therapeutic potential of epigenome editing compared to other modalities.

Project description:BackgroundHepatic knockdown of the proprotein convertase subtilisin/kexin type 9 ( PCSK9 ) gene or the angiopoietin-like 3 ( ANGPTL3 ) gene has been demonstrated to reduce blood low-density lipoprotein cholesterol (LDL-C) levels, and hepatic knockdown of the angiotensinogen ( AGT ) gene has been demonstrated to reduce blood pressure. Genome editing can productively target each of these three genes in hepatocytes in the liver, offering the possibility of durable "one-and-done" therapies for hypercholesterolemia and hypertension. However, concerns around making permanent gene sequence changes via DNA strand breaks might hinder acceptance of these therapies. Epigenome editing offers an alternative approach to gene inactivation, via silencing of gene expression by methylation of the promoter region, but the long-term durability of epigenome editing remains to be established.MethodsWe assessed the ability of epigenome editing to durably reduce the expression of the human PCSK9, ANGPTL3 , and AGT genes in HuH-7 hepatoma cells. Using the CRISPRoff epigenome editor, we identified guide RNAs that produced efficient gene knockdown immediately after transfection. We assessed the durability of gene expression and methylation changes through serial cell passages.ResultsCells treated with CRISPRoff and PCSK9 guide RNAs were maintained for up to 124 cell doublings and demonstrated durable knockdown of gene expression and increased CpG dinucleotide methylation in the promoter, exon 1, and intron 1 regions. In contrast, cells treated with CRISPRoff and ANGPTL3 guide RNAs experienced only transient knockdown of gene expression. Cells treated with CRISPRoff and AGT guide RNAs also experienced transient knockdown of gene expression; although initially there was increased CpG methylation throughout the early part of the gene, this methylation was geographically heterogeneous-transient in the promoter, and stable in intron 1.ConclusionsThis work demonstrates precise and durable gene regulation via methylation, supporting a new therapeutic approach for protection against cardiovascular disease via knockdown of genes such as PCSK9 . However, the durability of knockdown with methylation changes is not generalizable across target genes, likely limiting the therapeutic potential of epigenome editing compared to other modalities.

Project description:BackgroundThe durability of Long Lasting Insecticidal Nets (LLINs) in field conditions is of great importance for malaria prevention and control efforts; however, the physical integrity of the net fabric is not well understood making it challenging to determine overall effectiveness of nets as they age. The 2011 World Health Organization Pesticide Evaluation Scheme (WHOPES) guidelines provide a simple, standardized method using a proportional hole index (PHI) for assessing net damage with the intent to provide national malaria control programs with guidelines to assess the useful life of LLINS and estimate the rate of replacement.MethodsWe evaluated the utility of the PHI measure using 409 LLINs collected over three years in Nampula Province, Mozambique following a mass distribution campaign in 2008. For each LLIN the diameter and distance from the bottom of the net were recorded for every hole. Holes were classified into four size categories and a PHI was calculated following WHOPES guidelines. We investigate how the size, shape, and location of holes influence the PHI. The areas of the WHOPES defined categories were compared to circular and elliptical areas based on approximate shape and actual measured axes of each hole and the PHI was compared to cumulative damaged surface area of the LLIN.ResultsThe damaged area of small, medium, large, and extra-large holes was overestimated using the WHOPES categories compared to elliptical areas using the actual measured axes. Similar results were found when comparing to circular areas except for extra-large holes which were underestimated. (Wilcoxon signed rank test of differences p< 0.0001 for all sizes). Approximating holes as circular overestimated hole surface area by 1.5 to 2 times or more. There was a significant difference in the mean number of holes < 0.5 cm by brand and there were more holes of all sizes on the bottom of nets than the top. For a range of hypothetical PHI thresholds used to designate a "failed LLIN", roughly 75 to 80% of failed LLINs were detected by considering large and extra-large holes alone, but sensitivity varied by brand.ConclusionsFuture studies may refine the PHI to better approximate overall damaged surface area. Furthermore, research is needed to identify whether or not appropriate PHI thresholds can be used to deem a net no longer protective. Once a cutoff is selected, simpler methods of determining the effective lifespan of LLINs can help guide replacement strategies for malaria control programs.

Dataset Information

Characterizing fretting damage in different test media for cardiovascular device durability testing.

Publications

Characterizing fretting damage in different test media for cardiovascular device durability testing.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets