Porosity and Pore Size Distribution of Native and Delignified Beech Wood Determined by Mercury Intrusion Porosimetry.

ABSTRACT: The complex hierarchical structures of biological materials in combination with outstanding property profiles are great sources of inspiration for material scientists. Based on these characteristic features, the structure of wood has been increasingly exploited to fabricate novel hierarchical and functional materials. With delignification treatments, the density and chemistry of wood can be altered, resulting in hierarchical cellulose scaffolds with enhanced porosity for the fabrication of novel hybrid materials. In the present study, focusing on acidic delignification of beech wood and its influence on porosity, we report on a structural characterization and qualitative assessment of the cellulose scaffolds using mercury intrusion porosimetry (MIP). To account for the effect of water removal from the hygroscopic structure, different drying methods-e.g., standard oven and freeze-drying-were applied. While native beech wood is characterized by the presence of macro, meso and micro pores, delignification altered the porosity, increasing the importance of the macropores in the pore size distribution. Furthermore, we showed that the final porosity obtained in the material is strongly dependent on the applied drying process. Samples delignified under harsh conditions at high temperature (mass loss of ~35%) show a 13% higher porosity after freeze-drying compared to oven-dried samples. The obtained results contribute to a better understanding of the impact of the delignification and drying processes on the porosity of cellulose scaffolds, which is of high relevance for subsequent modification and functionalization treatments.

SUBMITTER: Vitas S

PROVIDER: S-EPMC6385036 | biostudies-literature | 2019 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Porosity and Pore Size Distribution of Native and Delignified Beech Wood Determined by Mercury Intrusion Porosimetry.

Vitas Selin S Segmehl Jana S JS Burgert Ingo I Cabane Etienne E

Materials (Basel, Switzerland) 20190129 3

The complex hierarchical structures of biological materials in combination with outstanding property profiles are great sources of inspiration for material scientists. Based on these characteristic features, the structure of wood has been increasingly exploited to fabricate novel hierarchical and functional materials. With delignification treatments, the density and chemistry of wood can be altered, resulting in hierarchical cellulose scaffolds with enhanced porosity for the fabrication of novel ...[more]

PMID: 30700052

Similar Datasets

Project description:3D printed scaffolds can be used, for example, in medical applications for simulating body tissues or for manufacturing prostheses. However, it is difficult to print porous structures of specific porosity and pore size values with fused deposition modelling (FDM) technology. The present paper provides a methodology to design porous structures to be printed. First, a model is defined with some theoretical parallel planes, which are bounded within a geometrical figure, for example a disk. Each plane has randomly distributed points on it. Then, the points are joined with lines. Finally, the lines are given a certain volume and the structure is obtained. The porosity of the structure depends on three geometrical variables: the distance between parallel layers, the number of columns on each layer and the radius of the columns. In order to obtain mathematical models to relate the variables with three responses, the porosity, the mean of pore diameter and the variance of pore diameter of the structures, design of experiments with three-level factorial analysis was used. Finally, multiobjective optimization was carried out by means of the desirability function method. In order to favour fixation of the structures by osseointegration, porosity range between 0.5 and 0.75, mean of pore size between 0.1 and 0.3 mm, and variance of pore size between 0.000 and 0.010 mm² were selected. Results showed that the optimal solution consists of a structure with a height between layers of 0.72 mm, 3.65 points per mm² and a radius of 0.15 mm. It was observed that, given fixed height and radius values, the three responses decrease with the number of points per surface unit. The increase of the radius of the columns implies the decrease of the porosity and of the mean of pore size. The decrease of the height between layers leads to a sharper decrease of both the porosity and the mean of pore size. In order to compare calculated and experimental values, scaffolds were printed in polylactic acid (PLA) with FDM technology. Porosity and pore size were measured with X-ray tomography. Average value of measured porosity was 0.594, while calculated porosity was 0.537. Average value of measured mean of pore size was 0.372 mm, while calculated value was 0.434 mm. Average value of variance of pore size was 0.048 mm², higher than the calculated one of 0.008 mm². In addition, both round and elongated pores were observed in the printed structures. The current methodology allows designing structures with different requirements for porosity and pore size. In addition, it can be applied to other responses. It will be very useful in medical applications such as the simulation of body tissues or the manufacture of prostheses.

Dataset Information

Porosity and Pore Size Distribution of Native and Delignified Beech Wood Determined by Mercury Intrusion Porosimetry.

Publications

Porosity and Pore Size Distribution of Native and Delignified Beech Wood Determined by Mercury Intrusion Porosimetry.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets