Substrate-Independent, Fast, and Reversible Switching between Underwater Superaerophobicity and Aerophilicity on the Femtosecond Laser-Induced Superhydrophobic Surfaces for Selectively Repelling or Capturing Bubbles in Water.

ABSTRACT: In this paper, the reversible switching between underwater (super-) aerophilicity and superaerophobicity was achieved on various femtosecond (fs) laser-induced superhydrophobic surfaces. A range of materials including Al, stainless steel, Cu, Ni, Si, poly(tetrafluoroethylene), and polydimethylsiloxane were first transformed to superhydrophobic after the formation of surface microstructures through fs laser treatment. These surfaces showed (super-) aerophilicity when immersed in water. In contrast, if the surface was prewetted with ethanol and then dipped into water, the surfaces showed superaerophobicity in water. The underwater aerophilicity of the superhydrophobic substrates could easily recover by drying. The switching between the underwater aerophilicity and superaerophobicity can be fast repeated many cycles and is substrate-independent in stark contrast to common wettability-switchable surfaces based on stimuli-responsive chemistry. Therefore, the as-prepared superhydrophobic surfaces can capture or repel air bubbles in water by selectively switching between underwater superaerophobicity and aerophilicity. Finally, we demonstrated that the underwater bubbles could pass through an underwater aerophilic porous sheet but were intercepted by an underwater superaerophobic porous sheet. The selective passage of the underwater bubbles was achieved by the reversible switching between the underwater aerophilicity and superaerophobicity. We believe that this substrate-independent and fast method of switching air wettability has important applications in controlling air behavior in water.

SUBMITTER: Yong J

PROVIDER: S-EPMC6396345 | biostudies-literature | 2019 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Substrate-Independent, Fast, and Reversible Switching between Underwater Superaerophobicity and Aerophilicity on the Femtosecond Laser-Induced Superhydrophobic Surfaces for Selectively Repelling or Capturing Bubbles in Water.

Yong Jiale J Singh Subhash C SC Zhan Zhibing Z Chen Feng F Guo Chunlei C

ACS applied materials & interfaces 20190213 8

In this paper, the reversible switching between underwater (super-) aerophilicity and superaerophobicity was achieved on various femtosecond (fs) laser-induced superhydrophobic surfaces. A range of materials including Al, stainless steel, Cu, Ni, Si, poly(tetrafluoroethylene), and polydimethylsiloxane were first transformed to superhydrophobic after the formation of surface microstructures through fs laser treatment. These surfaces showed (super-) aerophilicity when immersed in water. In contras ...[more]

PMID: 30698002

Similar Datasets

Project description:Laser-textured surfaces enabling reversible wettability switching and improved optical properties are gaining importance in cutting-edge applications, including self-cleaning interfaces, tunable optical lenses, microfluidics, and lab-on-chip systems. Fabrication of such surfaces by combining nanosecond-laser texturing and low-temperature annealing of titanium Ti-6Al-4V alloy was demonstrated by Lian et al. in ACS Appl. Mater. Inter. 2020, 12 (5), 6573-6580. However, it is difficult to agree with (i) their contradictory explanation of the wettability transition due to low-temperature annealing and (ii) their theoretical description of the optical behavior of the laser-textured titanium surface. This comment provides an alternative view-supported by both experimental results and theoretical investigation-on how the results by Lian et al. could be interpreted more correctly. The annealing experiments clarify that controlled contamination is crucial in obtaining consistent surface wettability alterations after low-temperature annealing. Annealing of laser-textured titanium at 100 °C in contaminated and contaminant-free furnaces leads to completely different wettability transitions. Analysis of the surface chemistry by XPS and ToF-SIMS reveals that (usually overlooked) contamination with hydrophobic polydimethylsiloxane (PDMS) may arise from the silicone components of the furnace. In this case, a homogeneous thin PDMS film over the entire surface results in water repellency (contact angle of 161° and roll-off angle of 15°). In contrast, annealing under the same conditions but in a contaminant-free furnace preserves the initial superhydrophilicity, whereas the annealing at 350 °C turns the hydrophobicity "off". The theoretical calculations of optical properties demonstrate that the laser-induced oxide layer formed during the laser texturing significantly influences the surface optical behavior. Consequently, the interference of light reflected by the air-oxide and the oxide-metal interfaces should not be neglected and enables several advanced approaches to exploit such optical properties.

Dataset Information

Substrate-Independent, Fast, and Reversible Switching between Underwater Superaerophobicity and Aerophilicity on the Femtosecond Laser-Induced Superhydrophobic Surfaces for Selectively Repelling or Capturing Bubbles in Water.

Publications

Substrate-Independent, Fast, and Reversible Switching between Underwater Superaerophobicity and Aerophilicity on the Femtosecond Laser-Induced Superhydrophobic Surfaces for Selectively Repelling or Capturing Bubbles in Water.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets