Inkjet Printable and Self-Curable Disperse Dyes/P(St-BA-MAA) Nanosphere Inks for Both Hydrophilic and Hydrophobic Fabrics.

ABSTRACT: Low-water-soluble disperse dyes possess a broad color gamut and good durability, but they need chemical or physical modification before being used in inks and can only be applied to several kinds of hydrophobic fabrics. In this work, disperse dyes/P(St-BA-MAA) nanospheres (known as DPN) absorbed by sodium nitrilotriacetate (known as NTA@DPN) were prepared and applied into ink formulations, which exhibited high dye fixation, long-term stability and self-curable ability without addition of any binder. Transmission electron microscopy (TEM) images showed the nanospheres have homogeneous core-shell spherical shape and the average diameter increased by 20.6 nm after coloration. X-ray diffraction (XRD), Fourier transform infrared spectrum (FTIR), and differential scanning calorimetry (DSC) measurements illustrated the interaction between dyes and nanospheres and indicated that the colored nanospheres contained both dye molecules and crystalline dyes. The Zeta potential and particle size measurements demonstrated that the dispersion stability was improved when sodium nitrilotriacetate (NTA) was absorbed onto DPN. The rheological behavior of the NTA@DPN inks was Newtonian and desired droplet formation was achieved at the viscosity of 4.23 mPa·s. Both hydrophilic cotton and hydrophobic polyester fabrics were cationic modified before used, which had an excellent image quality and desired rubbing fastness after inkjet printing. Scanning electron microscope (SEM) images showed NTA@DPN formed stable deposits on the surface of modified fibers and could self-cure to form continuous film coating on the fiber surface after being baked at 150 °C without addition of any binder.

SUBMITTER: Song Y

PROVIDER: S-EPMC6401999 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Inkjet Printable Polydimethylsiloxane for All-Inkjet-Printed Multilayered Soft Electrical Applications.

Project description:In recent years, additive manufacturing of polydimethylsiloxane (PDMS) has gained interest for the development of soft electronics. To build complex electrical devices, fabrication of multilayered structures is required. We propose here a straightforward digital printing fabrication process of silicone rubber-based, multilayered electronics. An inkjet-printable PDMS solution was developed for the digital patterning of elastomeric structures. The silicone ink was used together with a highly conductive silver nanoparticle (Ag NP) ink for the fabrication of all-inkjet-printed multilayered electrical devices. The application of the multilayered circuit board was successful. The sheet resistances were below 0.3 ?/?, and the conductive layer thickness was less than 1 ?m. The electrical insulation between the conductive layers was done by printing a 20-25 ?m-thick dielectric PDMS layer selectively on top of the bottommost conductive layer.

| S-EPMC7145287 | biostudies-literature

Direct-Writable and Thermally One-Step Curable "Water-Stained" Epoxy Composite Inks.

Project description:In this study, a simple method for preparing direct-writable and thermally one-step curable epoxy composite inks was proposed. Specifically, colloidal inks containing a mixture of ordinary epoxy resin and anhydride-type hardener with the suspended alumina microplates, as exemplary fillers, are "stained" with small amounts of water. This increases the elasticity of the ink via the interparticle capillary attraction and promotes curing of the epoxy matrix in low-temperature ranges, causing the three-dimensional (3D) printed ink to avoid structural disruption during one-step thermal curing without the tedious pre-curing step. The proposed mechanisms for the shape retention of thermally cured water-stained inks were discussed with thorough analyses using shear rheometry, DSC, FTIR, and SEM. Results of the computer-vision numerical analysis of the SEM images reveal that the particles in water-stained inks are oriented more in the vertical direction than those in water-free samples, corroborating the proposed mechanisms. The suggested concept is extremely simple and does not require any additional cost to the one required for the preparation of the common epoxy-filler composites, which is thus expected to be well-exploited in various applications where 3D printing of epoxy-based formulations is necessary.

| S-EPMC9573494 | biostudies-literature

Design and tailoring of inks for inkjet patterning of metal oxides.

Project description:Inkjet printing has become a promising, efficient, inexpensive, scalable technique for materials deposition, mask-less and digital patterning in many device applications. Meanwhile, the ink preparation remains a challenge especially for printing functional oxide materials. Based on the principles of inkjet printing (especially relevant for piezoelectric drop-on-demand inkjet printer) and the process of the conversion of liquid ink into solid thin films of oxide materials, we present two approaches to the design and tailoring of inks: (i) oxide particle suspensions (e.g. SiO2, TiO2, Fe3O4) and (ii) metal-acetates precursor solutions for directly printing oxide thin films (e.g. ZnO, MgO, ITO and so forth). The solution inks are stable and produce tunable oxide films with high density and smooth surface. For some of the inks containing multi-type acetates with possible phase separation even before calcinations, we have developed a chelating procedure in order to tailor the films into single-phase homogeneity. The work lays a foundation for inkjet printing of oxides films for functional applications in electronic, photonic and energy devices.

| S-EPMC7211876 | biostudies-literature

Synthesis, characterization, and application of novel aryldiazenyl disperse dyes on polyester fabrics.

Project description:Azo dyes are widely used for dyeing polyester fabrics but require optimization of properties like color strength and fastness. Fourteen novel disperse azo dyes were synthesized from 2,3-naphthalenediol and aniline derivatives to examine their potential for polyester dyeing. The dyes were prepared via diazotization and coupling reactions and characterized using FT-IR, UV-Vis, 1H NMR, 13C NMR, and elemental analysis. Furthermore, several techniques were employed to study the azo-hydrazone tautomerism, including UV-Vis spectroscopy, NMR spectroscopy, and computational methods. DFT computations revealed hydrazone tautomers were more stable than azo tautomers. The prepared azo dyes were applied on polyester fabrics at 2% depth using a high temperature pressure technique in water utilizing DYEWELL-002 as a dispersing agent. The color shading of dyed polyester samples ranged from peach amber to apple of my eye, depending on the coupler moieties. The fastness properties, assessed using a grey scale of dyed polyester fabrics, indicated very good to excellent grades for most dyes. Additionally, measurements of color strength (K/S), dye exhaustion (%E), as well as colorimetric colors CILAB of dyed polyester fabrics values, were measured and discussed in terms of the effect of substituents. The findings provide new insights into structure-performance relationships to design optimized disperse dyes for polyester coloration. Overall, the synthesized aryldiazenyl dyes are promising candidates for dyeing polyester fabrics across a spectrum of shades with good fastness properties.

| S-EPMC10700463 | biostudies-literature

Hexagonal Boron Nitride-Enhanced Optically Transparent Polymer Dielectric Inks for Printable Electronics.

Project description:Solution-processable thin-film dielectrics represent an important material family for large-area, fully-printed electronics. Yet, in recent years, it has seen only limited development, and has mostly remained confined to pure polymers. Although it is possible to achieve excellent printability, these polymers have low (≈2-5) dielectric constants (ε r ). There have been recent attempts to use solution-processed 2D hexagonal boron nitride (h-BN) as an alternative. However, the deposited h-BN flakes create porous thin-films, compromising their mechanical integrity, substrate adhesion, and susceptibility to moisture. These challenges are addressed by developing a "one-pot" formulation of polyurethane (PU)-based inks with h-BN nano-fillers. The approach enables coating of pinhole-free, flexible PU+h-BN dielectric thin-films. The h-BN dispersion concentration is optimized with respect to exfoliation yield, optical transparency, and thin-film uniformity. A maximum ε r ≈ 7.57 is achieved, a two-fold increase over pure PU, with only 0.7 vol% h-BN in the dielectric thin-film. A high optical transparency of ≈78.0% (≈0.65% variation) is measured across a 25 cm2 area for a 10 μm thick dielectric. The dielectric property of the composite is also consistent, with a measured areal capacitance variation of <8% across 64 printed capacitors. The formulation represents an optically transparent, flexible thin-film, with enhanced dielectric constant for printed electronics.

| S-EPMC7405982 | biostudies-literature

Development and Characterizations of Novel Aqueous-Based Ceramic Inks for Inkjet Printing.

Project description:Stable rheological properties of ceramic ink are a key requirement for inkjet printing (IJP), which should be satisfied in terms of the Reynolds and Weber numbers. In this paper, the reverse microemulsion was introduced for the synthesis of monodispersed nanosized ceramic powders, and the average size was less than 100 nm. A comparison of two different dispersants, i.e., polyacrylic ammonium (PAANH4) and polyacrylic aid (PAA), revealed that the former exerted a good dispersion effect on the ceramic ink. The sedimentation ratio, zeta potential, surface tension, viscosity, and density of the inks were measured, and the Reynolds and Weber numbers, as well as Z value, were calculated. A stable, homogeneous, and high solid loading (20 wt%) ceramic ink could be achieved after aging for a period of 72 h. Finally, the ceramic inks showed the desired printable property in the inkjet printing process. Combining inkjet printing technology with a sintering process, Ni-Mn-O films have the potential to monitor temperature and humidity parameters for intelligent wearable devices.

| S-EPMC9821278 | biostudies-literature

Performance of Washing-Free Printing of Disperse Dye Inks: Influence of Water-Borne Polymers.

Project description:Dye-containing wastewater discharge from the textile industry poses a serious pollution hazard that can be overcome by eliminating the washing step following the dyeing process. To study the washing-free printing of disperse dye ink, a number of water-borne polymers were selected and added to the ink, and the properties of the inks were discussed. By optimizing the ink formulation, printed fabrics with high color strength and color fastness were produced. The effects of the addition of polyvinylpyrrolidone (PVP), polyvinyl alcohol (PVA), and polyethylene glycol (PEG) on the ink jetting performance and printing performance were intensively investigated. The migration-diffusion-fixation behavior of disperse dyes in inks on the polyester fiber was explored. The disperse dye ink with 0.075 wt.% PVA exhibited the strongest migration-diffusion effect. The PVA ink exhibited excellent jetting performance and printing color fastness, and the printing color strength was better than that of the PVP and PEG ink. The addition of PVA increased the difference between the solubility parameter of the disperse dyes and ink system, which improved the migration of disperse dyes from the ink system to the polyester fabric. Meanwhile, PVA could form a protective layer on printed fabrics because of its excellent film-forming properties at room temperature. The washing-free inkjet printing method developed in this study provides a theoretical basis for screening water-borne polymers and an environmentally friendly pathway for the printing of textiles.

| S-EPMC9610862 | biostudies-literature

Silver nanoparticle conductive inks: synthesis, characterization, and fabrication of inkjet-printed flexible electrodes.

Project description:Flexible electronics can be developed with a low-cost and simple fabrication process while being environmentally friendly. Conductive silver inks have been the most applied material in flexible substrates. This study evaluated the performance of different conductive ink formulations using silver nanoparticles by studying the material properties, the inkjet printing process, and application based on electrical impedance spectroscopy using a buffer solution. Silver nanoparticles synthesis was carried out through chemical reduction of silver nitrate; then, seven conductive ink formulations were produced. Properties such as resistivity, viscosity, surface tension, adhesion, inkjet printability of the inks, and electrical impedance of the printed electrodes were investigated. Curing temperature directly influenced the electrical properties of the inks. The resistivity obtained varied from 3.3?×?100 to 5.6?×?10-06 ?.cm. Viscosity ranged from 3.7 to 7.4 mPa.s, which is suitable for inkjet printing fabrication. By using a buffer solution as an analyte, the printed electrode pairs presented electrical impedance lower than 200 ? for all the proposed designs, demonstrating the potential of the formulated inks for utilization in flexible electronic devices for biological sensing applications.

| S-EPMC7264204 | biostudies-literature

Photocurable Bioink for the Inkjet 3D Pharming of Hydrophilic Drugs.

Project description:Novel strategies are required to manufacture customized oral solid dosage forms for personalized medicine applications. 3D Pharming, the direct printing of pharmaceutical tablets, is an attractive strategy, since it allows for the rapid production of solid dosage forms containing custom drug dosages. This study reports on the design and characterization of a biocompatible photocurable pharmaceutical polymer for inkjet 3D printing that is suitable for hydrophilic active pharmaceutical ingredients (API). Specifically, hyaluronic acid was functionalized with norbornene moieties that, in the presence of poly(ethylene) glycol dithiol, Eosin Y as a photoinitiator, and a visible light source, undergoes a rapid step-growth polymerization reaction through thiol-ene chemistry. The engineered bioink was loaded with Ropinirole HCL, dispensed through a piezoelectric nozzle onto a blank preform tablet, and polymerized. Drug release analysis of the tablet resulted in 60% release within 15 min of tablet dissolution. The study confirms the potential of inkjet printing for the rapid production of tablets through the deposition of a photocurable bioink designed for hydrophilic APIs.

| S-EPMC5590429 | biostudies-literature

Novel Monosulfonated Azo Dyes: Design, Synthesis, and Application as Disperse Dyes on Polyester Fabrics.

Project description:This study synthesizes and characterizes a series of disperse dyes based on azo Schiff bases, compounds 8-10. Their structures were identified using various analytical techniques, such as FT-IR, 1H/13C NMR, and mass spectrometry. The study's primary objective was to investigate the behavior of disperse dyes 8-10 when used for dyeing polyester fabrics under different conditions, including variations in time, temperature, shade, and pH. The polyester fabric was chosen for this research due to its wide usage and popularity in the textile industry. By examining the effect of temperature and time on the dyeing process, it was observed that increasing the dyeing temperature from low to high (ranging from 90 to 120 °C) and extending the dyeing time from 10 to 30 min resulted in higher K/S values for the polyester samples dyed with disperse dyes. Additionally, dyes 9 and 10 exhibited the most excellent K/S values among the tested dyes. Furthermore, the study found that dye 8 showed the best dyeing performance as the pH of the dye bath increased to 6.

| S-EPMC10785301 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data