Effect of Microfibrillated Cellulose on Microstructure and Properties of Poly(vinyl alcohol) Foams.

ABSTRACT: Poly(vinyl alcohol) foams, containing different amounts of microfibrillated cellulose, were prepared through an eco-friendly procedure based on high-speed mixing and freeze-drying. The effect of filler amount on cell shape and regularity was studied by scanning electron microscopy (SEM) and the evolution of the microstructure was assessed through dynamic cryo-SEM. Fourier Transformed Infrared Analysis and Differential Scanning Calorimetry measurements revealed the presence of hydrogen bond interaction among cellulosic filler and the matrix. The modulus and compression deflection of neat PVA were significantly improved by increasing the amount of microfibrillated cellulose content with respect to foams realised with pulp cellulose fibers.

SUBMITTER: Gentile G

PROVIDER: S-EPMC6403540 | biostudies-literature | 2018 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of Microfibrillated Cellulose on Microstructure and Properties of Poly(vinyl alcohol) Foams.

Gentile Gennaro G Cocca Mariacristina M Avolio Roberto R Errico Maria Emanuela ME Avella Maurizio M

Polymers 20180724 8

Poly(vinyl alcohol) foams, containing different amounts of microfibrillated cellulose, were prepared through an eco-friendly procedure based on high-speed mixing and freeze-drying. The effect of filler amount on cell shape and regularity was studied by scanning electron microscopy (SEM) and the evolution of the microstructure was assessed through dynamic cryo-SEM. Fourier Transformed Infrared Analysis and Differential Scanning Calorimetry measurements revealed the presence of hydrogen bond inter ...[more]

PMID: 30960738

Similar Datasets

Project description:This study aimed to develop poly (vinyl alcohol) grafted glycidyl methacrylate/cellulose nanofiber (PVA-g-GMA/CNF) injectable hydrogels for meniscus tissue engineering. PVA-g-GMA is an interesting polymer for preparing cross-linking injectable hydrogels with UV radiation, but it has poor mechanical properties and low cell proliferation. In this study, CNF as a reinforcing agent was selected to improve mechanical properties and cell proliferation in PVA-g-GMA injectable hydro-gels. The effect of CNF concentration on hydrogel properties was investigated. Both PVA-g-GMA and PVA-g-GMA hydrogels incorporating 0.3, 0.5, and 0.7% (w/v) CNF can be formed by UV curing at a wavelength of 365 nm, 6 mW/cm2 for 10 min. All hydrogels showed substantial microporosity with interconnected tunnels, and a pore size diameter range of 3-68 µm. In addition, all hydrogels also showed high physicochemical properties, a gel fraction of 81-82%, porosity of 83-94%, water content of 73-87%, and water swelling of 272-652%. The water content and swelling of hydrogels were increased when CNF concentration increased. It is worth noting that the reduction of porosity in the hydrogels occurred with increasing CNF concentration. With increasing CNF concentration from 0.3% to 0.7% (w/v), the compressive strength and compressive modulus of the hydrogels significantly increased from 23 kPa to 127 kPa and 27 kPa to 130 kPa, respectively. All of the hydrogels were seeded with human cartilage stem/progenitor cells (CSPCs) and cultured for 14 days. PVA-g-GMA hydrogels incorporating 0.5% and 0.7% (w/v) CNF demonstrated a higher cell proliferation rate than PVA-g-GMA and PVA-g-GMA hydrogels incorporating 0.3% (w/v) CNF, as confirmed by MTT assay. At optimum formulation, 10%PVA-g-GMA/0.7%CNF injectable hydrogel met tissue engineering requirements, which showed excellent properties and significantly promoted cell proliferation, and has a great potential for meniscus tissue engineering application.

Dataset Information

Effect of Microfibrillated Cellulose on Microstructure and Properties of Poly(vinyl alcohol) Foams.

Publications

Effect of Microfibrillated Cellulose on Microstructure and Properties of Poly(vinyl alcohol) Foams.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets