A Universal Stamping Method of Graphene Transfer for Conducting Flexible and Transparent Polymers.

ABSTRACT: Transfer method of chemically vapor deposition graphene is an appealing issue to realize its application as flexible and transparent electrodes. A universal stamping method to transfer as grown graphene from copper onto different flexible and transparent polymers (FTPs) reported here ensures simple, robust, rapid, clean and low-cost. This method relies on coating ethylene vinyl acetate (EVA) onto the as grown graphene, binding EVA coated graphene/Cu with FTPs and delamination by hydrogen bubbling process, which is analogous to the method used by stamping process where ink carries the imprint of the object onto any materials. The fate of the stamping method depends on how strongly the adhesion of EVA coated graphene/Cu with target FTPs. Interestingly, we have found that the thin film of EVA/graphene/Cu can only bind strongly with the FTPs of less than 25?µm in thickness and lower glass transition temperature value to the EVA while wide range of other FTPs are considered upon surface engineering to enhance the binding strength between FTPs and EVA. What's more, the electrical performance was investigated with a demonstration of triboelectric nanogenerators which confirmed the reliability of graphene transfer onto the FTPs and prospect for the development of flexible and transparent electronics.

SUBMITTER: Chandrashekar BN

PROVIDER: S-EPMC6408549 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Stamping Fabrication of Flexible Planar Micro-Supercapacitors Using Porous Graphene Inks.

Project description:High performance, flexibility, safety, and robust integration for micro-supercapacitors (MSCs) are of immense interest for the urgent demand for miniaturized, smart energy-storage devices. However, repetitive photolithography processes in the fabrication of on-chip electronic components including various photoresists, masks, and toxic etchants are often not well-suited for industrial production. Here, a cost-effective stamping strategy is developed for scalable and rapid preparation of graphene-based planar MSCs. Combining stamps with desired shapes and highly conductive graphene inks, flexible MSCs with controlled structures are prepared on arbitrary substrates without any metal current collectors, additives, and polymer binders. The interdigitated MSC exhibits high areal capacitance up to 21.7 mF cm-2 at a current of 0.5 mA and a high power density of 6 mW cm-2 at an energy density of 5 µWh cm-2. Moreover, the MSCs show outstanding cycling performance and remarkable flexibility over 10 000 charge-discharge cycles and 300 bending cycles. In addition, the capacitance and output voltage of the MSCs are easily adjustable through interconnection with well-defined arrangements. The efficient, rapid manufacturing of the graphene-based interdigital MSCs with outstanding flexibility, shape diversity, and high areal capacitance shows great potential in wearable and portable electronics.

| S-EPMC7539196 | biostudies-literature

Pulsed-grown graphene for flexible transparent conductors.

Project description:In the race to find novel transparent conductors for next-generation optoelectronic devices, graphene is supposed to be one of the leading candidates, as it has the potential to satisfy all future requirements. However, the use of graphene as a truly transparent conductor remains a great challenge because its lowest sheet resistance demonstrated so far exceeds that of the commercially available indium tin oxide. The possible cause of low conductivity lies in its intrinsic growth process, which requires further exploration. In this work, I have approached this problem by controlling graphene nucleation during the chemical vapor deposition process as well as by adopting three distinct procedures, including bis(trifluoromethanesulfonyl)amide doping, post annealing, and flattening of graphene films. Additionally, van der Waals stacked graphene layers have been prepared to reduce the sheet resistance effectively. I have demonstrated an efficient and flexible transparent conductor with the extremely low sheet resistance of 40 Ω sq-1, high transparency (T r ∼90%), and high mechanical flexibility, making it suitable for electrode materials in future optoelectronic devices.

| S-EPMC9419159 | biostudies-literature

Polyester-Polysiloxane Hyperbranched Block Polymers for Transparent Flexible Materials.

Project description:Highly transparent flexible silicone elastomers are useful for certain stretchable electronics and various types of smart devices. Polyester-polysiloxane hyperbranched block copolymers are synthesized by ring-opening polymerization of octamethylcyclotetrasiloxane initiated by macromolecular lithium alkoxide. Treatment of these copolymers with tetraethoxysilane and dibutylin dilaurate at room temperature gives the corresponding transparent elastic materials. The transparency of the materials can reach 90% (700-800 nm), and the starting thermal decomposition temperatures of the materials are higher than 330 °C. Very interestingly, though the highest tensile strength of the material prepared is about 0.48 MPa, the elongation at break can reach 778-815%. The results will inspire us to develop highly transparent flexible silicone materials by designing copolymers of silicone materials and hyperbranched polymers.

| S-EPMC7675931 | biostudies-literature

Magnetic assembly of transparent and conducting graphene-based functional composites.

Project description:Innovative methods producing transparent and flexible electrodes are highly sought in modern optoelectronic applications to replace metal oxides, but available solutions suffer from drawbacks such as brittleness, unaffordability and inadequate processability. Here we propose a general, simple strategy to produce hierarchical composites of functionalized graphene in polymeric matrices, exhibiting transparency and electron conductivity. These are obtained through protein-assisted functionalization of graphene with magnetic nanoparticles, followed by magnetic-directed assembly of the graphene within polymeric matrices undergoing sol-gel transitions. By applying rotating magnetic fields or magnetic moulds, both graphene orientation and distribution can be controlled within the composite. Importantly, by using magnetic virtual moulds of predefined meshes, graphene assembly is directed into double-percolating networks, reducing the percolation threshold and enabling combined optical transparency and electrical conductivity not accessible in single-network materials. The resulting composites open new possibilities on the quest of transparent electrodes for photovoltaics, organic light-emitting diodes and stretchable optoelectronic devices.

| S-EPMC4931316 | biostudies-literature

Solution-Processed Transparent Conducting Electrodes for Flexible Organic Solar Cells with 16.61% Efficiency.

Project description:Nonfullerene organic solar cells (OSCs) have achieved breakthrough with pushing the efficiency exceeding 17%. While this shed light on OSC commercialization, high-performance flexible OSCs should be pursued through solution manufacturing. Herein, we report a solution-processed flexible OSC based on a transparent conducting PEDOT:PSS anode doped with trifluoromethanesulfonic acid (CF3SO3H). Through a low-concentration and low-temperature CF3SO3H doping, the conducting polymer anodes exhibited a main sheet resistance of 35 Ω sq-1 (minimum value: 32 Ω sq-1), a raised work function (≈ 5.0 eV), a superior wettability, and a high electrical stability. The high work function minimized the energy level mismatch among the anodes, hole-transporting layers and electron-donors of the active layers, thereby leading to an enhanced carrier extraction. The solution-processed flexible OSCs yielded a record-high efficiency of 16.41% (maximum value: 16.61%). Besides, the flexible OSCs afforded the 1000 cyclic bending tests at the radius of 1.5 mm and the long-time thermal treatments at 85 °C, demonstrating a high flexibility and a good thermal stability.

| S-EPMC8187532 | biostudies-literature

Ultra-smooth glassy graphene thin films for flexible transparent circuits.

Project description:Large-area graphene thin films are prized in flexible and transparent devices. We report on a type of glassy graphene that is in an intermediate state between glassy carbon and graphene and that has high crystallinity but curly lattice planes. A polymer-assisted approach is introduced to grow an ultra-smooth (roughness, <0.7 nm) glassy graphene thin film at the inch scale. Owing to the advantages inherited by the glassy graphene thin film from graphene and glassy carbon, the glassy graphene thin film exhibits conductivity, transparency, and flexibility comparable to those of graphene, as well as glassy carbon-like mechanical and chemical stability. Moreover, glassy graphene-based circuits are fabricated using a laser direct writing approach. The circuits are transferred to flexible substrates and are shown to perform reliably. The glassy graphene thin film should stimulate the application of flexible transparent conductive materials in integrated circuits.

| S-EPMC5262465 | biostudies-literature

Flexible transparent graphene/polymer multilayers for efficient electromagnetic field absorption.

Project description:Thanks to its high electrical conductivity, a graphene plane presents a good shielding efficiency against GHz electromagnetic radiations. Several graphene planes separated by thin polymer spacers add their conductivities arithmetically, because each of them conserves the intrinsic properties of isolated graphene. Maximum absorption of radiations for frequency around 30 GHz is achieved with six separated graphene planes, which is the optimum number. This remarkable result is demonstrated experimentally from electromagnetic measurements performed in the Ka band on a series of multilayers obtained by piling 1, 2, 3... graphene/PMMA units on a silica substrate. Theoretical calculations convincingly explain the observed absorption and transmission data in the GHz domain. It is concluded that graphene/PMMA multilayers can be used as an efficient optically transparent and flexible shielding media.

| S-EPMC4244631 | biostudies-other

Tailored CVD graphene coating as a transparent and flexible gas barrier.

Project description:The chemical vapor deposition (CVD) method to obtain tailored graphene as a transparent and flexible gas barrier has been developed. By separating nucleation step from growth, we could reduce early graphene nucleation density and thus induce better stitching between domain boundaries in the second growth step. Furthermore, two step growth in conjunction with electrochemical polishing of Cu foils achieved large graphene domains and improved graphene quality with minimized defects. The performance of resulting graphene as a gas barrier was superior to the graphene obtained by one-step growth on polished or unpolished Cu foils. The CVD graphene reported here could open up the possibility for exploring graphene-based gas barrier due to the minimized density of defect area.

| S-EPMC4827024 | biostudies-literature

Easily Processable, Highly Transparent and Conducting Thiol-Functionalized Reduced Graphene Oxides Langmuir-Blodgett Films.

Project description:We report synthesis and fabrication of highly thionated reduced graphene oxide and its Langmuir-Blodgett (LB) film without an LB trough. As the synthesized product, mercapto reduced graphene oxide (mRGO) contains high thiol content estimated from XPS, corresponding to a surface coverage of 1.3 SH/nm2. The mRGO LB film shows two electronic transport properties, following Efros-Shklovskii variable-range hopping (VRH) and Mott VRH at low and high temperature, respectively. Optical and band gap of the LB film was estimated from Tauc plot and semi-logarithmic-scale plot of sheet resistance versus temperature to be 0.6 and 0.1 eV, respectively. Additionally, the sheet resistance of the mRGO LB film depends on the quantity of the thiol functional group with the same transmittance at 550 nm (500 kΩ for mRGO, 1.3 MΩ for tRGO with 92% transmittance).

| S-EPMC8124529 | biostudies-literature

Flexible transparent graphene laminates <i>via</i> direct lamination of graphene onto polyethylene naphthalate substrates.

Project description:Graphene, with its excellent electrical, mechanical, and optical properties, has emerged as an exceptional material for flexible and transparent nanoelectronics. Such versatility makes it compelling to find new pathways to lay graphene sheets onto smooth, flexible substrates to create large-scale flexible transparent graphene conductors. Here, we report the realization of flexible transparent graphene laminates by direct adhesion of chemical vapor deposition (CVD) graphene on a polyethylene naphthalate (PEN) substrate, which is an emerging standard for flexible electronics. By systematically optimizing the conditions of a hot-press technique, we have identified that applying optimum temperature and pressure can make graphene directly adhere to flexible PEN substrates without any intermediate layer. The resultant flexible graphene films are transparent, have a standard sheet resistance of 1 kΩ with high bending resilience, and high optical transmittance of 85%. Our direct hot-press method is achieved below the glass transition temperature of the PEN substrate. Furthermore, we demonstrate press-assisted embossing for patterned transfer of graphene, and hence it can serve as a reliable new means for creating universal, transparent conducting patterned films for designing flexible nanoelectronic and optoelectronic components.

| S-EPMC9416925 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data