Thermo-Responsive Starch-g-(PAM-co-PNIPAM): Controlled Synthesis and Effect of Molecular Components on Solution Rheology.

ABSTRACT: A series of highly branched random copolymers of acrylamide (AM) and N-isopropylacrylamide (NIPAM) have been prepared from a waxy potato starch-based macroinitiator by aqueous Cu⁰-mediated living radical polymerization (Cu⁰-mediated LRP). The NIPAM intake in the copolymer was varied between 0% and 50 mol % to evaluate the influence of chain composition on the aqueous rheological properties as well as their low critical solution temperature (LCST). The viscosity of the copolymer was found to increase with the NIPAM intake and an LCST can be observed when the NIPAM content is high enough (e.g., 50 mol %). In addition, thermo-thickening behavior was observed at a low shear rate (γ ≤ 10 s^-1) and higher NIPAM content was found to shift the onset of thermo-thickening behavior to a lower temperature. However, the absolute increase in viscosity values is reduced with the NIPAM intake. Besides this, an interesting significant thermo-thickening behavior was also observed on highly branched starch-g-polyacrylamide at high temperatures (>80 °C), which has not been previously reported. Rheology tests also revealed a good salt-resistant property in copolymers with low NIPAM content (e.g., <25 mol %). Considering the viscosity profile in saline as compared to that in pure water, this NIPAM intake seems to represent an optimum balance of viscosity and salt-resistance performance.

SUBMITTER: Fan Y

PROVIDER: S-EPMC6414930 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Boron Nitride Nanosheets/PNIPAM Hydrogels with Improved Thermo-Responsive Performance.

Project description:Thermo-responsive hydrogel is an important smart material. However, its slow thermal response rate limits the scope of its applications. Boron nitride nanosheet-reinforced thermos-responsive hydrogels, which can be controlled by heating, were fabricated by in situ polymerization of N-isopropylacrylamide in the presence of boron nitride nanosheets. The hydrogels exhibit excellent thermo-responsiveness and much enhanced thermal response rate than that of pure poly(N-isopropylacrylamide) hydrogels. Interestingly, the hydrogels can be driven to move in aqueous solution by heating. Importantly, the composite hydrogel is hydrophilic at a temperature below lower critical solution temperature (LCST), while it is hydrophobic at a temperature above LCST. Therefore, it can be used for quick absorption and release of dyes and oils from water. All these properties demonstrate the potential of hydrogel composites for water purification and treatment.

| S-EPMC6073573 | biostudies-literature

Thermo-responsive adsorption-desorption of perfluoroorganics from water using PNIPAm hydrogels and pore functionalized membranes.

Project description:Perfluorochemicals (PFCs) are emerging contaminants in various water sources. Responsive polymers provide a new avenue for PFC adsorption/desorption from water. Poly-N-isopropylacrylamide's (PNIPAm's) temperature-responsive behavior and hydrophilic/hydrophobic transition is leveraged for reversible adsorption and desorption of PFCs. Adsorption of PFOA (perfluoro-octanoic acid) onto PNIPAm hydrogels yielded Freundlich distribution coefficients (Kd) of 0.073 L/g at 35 °C (above LCST) and 0.026 L/g at 22°C. Kinetic studies yielded second order rate constants (k2) of 0.012 g/mg/h for adsorption and 12.6 g/mg/h for desorption, with initial rates of 28 mg/g/h and 41 mg/g/h, respectively. Interaction parameters of PNIPAm's functional groups in its different conformational states, as well as the hydrophobic fluorinated carbon tails and hydrophilic head groups of PFOA are used to describe relative adsorption. Polyvinylidene difluoride (PVDF) provides a robust membrane structure for the commercial viability of polymeric adsorbents. Temperature swing adsorption of PFOA using PNIPAm functionalized PVDF membrane pores showed consistent adsorption and desorption capacity over 5 cycles. PFOA desorption percentage of 60% was obtained in pure water at temperatures below PNIPAm's lower critical solution temperature (LCST) while 13% desorption was obtained at temperatures above the LCST, thus showing the importance of the LCST on desorption performance.

| S-EPMC7039651 | biostudies-literature

Synthesis of Thermo-Responsive Monofunctionalized Diblock Copolymer Worms

Project description: Not available

| S-EPMC10708438 | biostudies-literature

Alginate-g-PNIPAM-Based Thermo/Shear-Responsive Injectable Hydrogels: Tailoring the Rheological Properties by Adjusting the LCST of the Grafting Chains.

Project description:Graft copolymers of alginate backbone and N-isopropylacrylamide/N-tert-butylacrylamide random copolymer, P(NIPAMx-co-NtBAMy), side chains (stickers) with various NtBAM content were designed and explored in aqueous media. Self-assembling thermoresponsive hydrogels are formed upon heating, in all cases, through the hydrophobic association of the P(NIPAMx-co-NtBAMy) sticky pendant chains. The rheological properties of the formulations depend remarkably on the NtBAM hydrophobic content, which regulates the lower critical solution temperature (LCST) and, in turn, the stickers' thermo-responsiveness. The gelation point, Tgel, was shifted to lower temperatures from 38 to 20 °C by enriching the PNIPAM chains with 20 mol % NtBAM, shifting accordingly to the gelation temperature window. The consequences of the Tgel shift to the hydrogels' rheological properties are significant at room and body temperature. For instance, at 37 °C, the storage modulus increases about two orders of magnitude and the terminal relaxation time increase about 10 orders of magnitude by enriching the stickers with 20 mol % hydrophobic moieties. Two main thermo-induced behaviors were revealed, characterized by a sol-gel and a weak gel-stiff gel transition for the copolymer with stickers of low (0.6 mol %) and high (14, 20 mol %) NtBAM content, respectively. The first type of hydrogels is easily injectable, while for the second one, the injectability is provided by shear-thinning effects. The influence of the type of media (phosphate buffer (PB), phosphate-buffered saline (PBS), Dulbecco's modified Eagle's medium (DMEM)) on the hydrogel properties was also explored and discussed. The 4 wt % NaALG-g-P(NIPAM80-co-NtBAM20)/DMEM formulation showed excellent shear-induced injectability at room temperature and instantaneous thermo-induced gel stiffening at body temperature, rendering it a good candidate for cell transplantation potential applications.

| S-EPMC8067843 | biostudies-literature

Cassava Starch-Based Thermo-Responsive Pb(II)-Imprinted Material: Preparation and Adsorption Performance on Pb(II).

Project description:Heavy metal pollution is currently an increasing threat to the ecological environment, and the development of novel absorbents with remarkable adsorption performance and cost-effectiveness are highly desired. In this study, a cassava starch-based Pb(II)-imprinted thermo-responsive hydrogel (CPIT) had been prepared by using cassava starch as the bio-substrate, N-isopropyl acrylamide (NIPAM) as the thermo-responsive monomer, and Pb(II) as the template ions. Later, a variety of modern techniques including FTIR, DSC, SEM, and TGA were employed to comprehensively analyze the characteristic functional groups, thermo-responsibility, morphology, and thermal stability of CPIT. The obtained material exhibited superior performance in adsorption of Pb(II) and its maximum adsorption capacity was high-up to 114.6 mg/g under optimized conditions. Notably, the subsequent desorption (regeneration) process was fairly convenient by simply rinsing with cold deionized water and the highest desorption efficiency could be achieved as 93.8%. More importantly, the adsorption capacity of regenerated CPIT still maintained 88.2% of the value of starting material even after 10 recyclings. In addition, the excellence of CPIT in selective adsorption of Pb(II) should also be highlighted as its superior adsorption ability (97.9 mg/g) over the other seven interfering metal ions.

| S-EPMC8963116 | biostudies-literature

Glass and Jamming Rheology in Soft Particles Made of PNIPAM and Polyacrylic Acid.

Project description:The phase behaviour of soft colloids has attracted great attention due to the large variety of new phenomenologies emerging from their ability to pack at very high volume fractions. Here we report rheological measurements on interpenetrated polymer network microgels composed of poly(N-isopropylacrylamide) (PNIPAM) and polyacrylic acid (PAAc) at fixed PAAc content as a function of weight concentration. We found three different rheological regimes characteristic of three different states: a Newtonian shear-thinning fluid, an attractive glass characterized by a yield stress, and a jamming state. We discuss the possible molecular mechanisms driving the formation of these states.

| S-EPMC8070831 | biostudies-literature

Core-Shell Structure Design of Hollow Mesoporous Silica Nanospheres Based on Thermo-Sensitive PNIPAM and pH-Responsive Catechol-Fe<sup>3+</sup> Complex.

Project description:A kind of core-shell hybrid nanoparticle comprised of a hollow mesoporous silica nanoparticles (HMS) core and a copolymer shell bearing N-(3,4-dihydroxyphenethyl) methacrylamide (DMA) and N-isopropylacrylamide (NIPAM) as responsive moieties was prepared. Moreover, the factors that could impact the surface morphology and hierarchical porous structure were discussed. In the presence of Fe3+, catechol-Fe3+ complexes were formed to achieve pH-responsive polymer shell, combining with thermal-sensitiveness of poly(N-isopropylacrylamide). Doxorubicin (DOX) was applied as a model drug and the behaviors of its loading/release behaviors were investigated to prove the idea. The results exhibited a significant drug loading capacity of 8.6% and embed efficiency of 94.6% under 1 mg ml-1 DOX/PBS solution. In fact, the loading capacity of drug can be easily improved to as high as 28.0% by increasing the DOX concentration. The vitro cytotoxicity assay also indicated that the as-prepared nanoparticles have no significant cytotoxicity on RAW 264.7 cells. The in vitro experiment showed that the cumulative release of DOX was obviously dependent on the temperature and pH values. This pH/temperature-sensitive hollow mesoporous silica nanosphere is expected to have potential applications in controlled drug release.

| S-EPMC6918372 | biostudies-literature

Synthesis of Thermo-Responsive Polymer via Radical (Co)polymerization of N,N-Dimethyl-α-(hydroxymethyl)acrylamide with N,N-Diethylacrylamide.

Project description:α-Functionalized acrylamides have not been considered as an effective monomer design due to their poor polymerizability, although the analogues, α-functionalized acrylates, are attractive monomers of which polymers exhibit characteristic properties. In this article, we report the first example of radical polymerization of α-functionalized N,N-disubstituted acrylamide affording thermo-responsive hydrophilic polymers. N,N-dimethyl-α-(hydroxymethyl)acrylamide (DMαHAA) was (co)polymerized with N,N-diethylacrylamide (DEAA). Although the homopolymerization did not afford a polymeric product, the copolymerizations with various feed ratios yielded a series of the copolymers containing 0%⁻65% of DMαHAA units. The obtained copolymers exhibited a lower critical solution temperature (LCST) in water; the cloud points (Tcs) were linearly elevated as the contents of DMαHAA units from 32 to 64 °C, indicating that DMαHAA functioned as a more hydrophilic monomer than DEAA. The linear relationship between Tc and DMαHAA content suggests that the homopolymer, poly(DMαHAA), should have Tc at ca. 80 °C, although it is not available by direct radical homopolymerization.

| S-EPMC6431880 | biostudies-literature

Dual Stimuli-Responsive P(NIPAAm-co-SPA) Copolymers: Synthesis and Response in Solution and in Films.

Project description:We present the synthesis and solution properties of dual stimuli-responsive poly(N-isopropylacrylamide-co-spiropyran acrylate) (P(NIPAAm-co-SPA)) copolymers of varying composition prepared via nitroxide-mediated copolymerization. The resulting copolymers feature molar masses from 40,000 to 100,000 g/mol according to static light scattering and an SPA content of up to 5.3%. The latter was determined by ¹H NMR spectroscopy and UV⁻Vis spectroscopy. These materials exhibit reversible response upon irradiation in polymeric films for a minimum of three cycles; their response in solution to both light and temperature was also investigated in an aqueous TRIS buffer (pH 8). Irradiation was carried out using LED setups with wavelengths of 365 and 590 nm. In aqueous solution, a custom-made setup using a fiber-coupled 200 W Hg(Xe) lamp with 340 and 540 nm filters was used and additional heating of the copolymer solutions during irradiation allowed to study influence of the presence of either the spiropyran or merocyanine form on the cloud point temperature. Hereby, it was found that increasing the SPA content leads to a more pronounced difference between both states and decreasing cloud points in general.

| S-EPMC6403943 | biostudies-literature

Rheology and tribology of starch + κ-carrageenan mixtures.

Project description:In this study, we investigated the rheological and tribological properties of biopolymer mixtures of gelatinized corn starches (0.5 - 10.0 wt%) and κ-carrageenan (κC) (0.05 - 1.0 wt%). Two different starch samples were used. The first starch (CS1), despite extensive heating and shearing contained "ghost" granules, while the second starch (CS2) had no visible ghost granules after the same gelatinization process as CS1. Apparent viscosity measurements demonstrated that κC + CS1 mixtures were shear thinning liquids, with viscosity values being lower than the corresponding weight average of the values of the individual equilibrium phases at shear rates < 50 s-1 . Tribological results revealed that κC ≥ 0.5 wt% was required to observe any decrease in friction coefficients in the mixed lubrication regime. Starch (CS1) showed an unusual behavior at ≥ 5 wt%, where the friction coefficient decreased not only in the mixed regime but also in the boundary regime, probably due to the presence of the "ghost" granules, as the latter became entrained in the contact region. The CS1 + κC mixtures showed significantly lower friction coefficients than that of pure CS1 and κC in the mixed regime. However, the CS2 + κC mixture (i.e., containing no ghost granules) showed similar behavior to pure κC in the mixed regime, while lower friction coefficients than that of the pure CS2 and κC in the boundary regime. These findings illustrate new opportunities for designing biopolymer mixtures with tunable lubrication performance, via optimizing the concentrations of the individual biopolymers and the gelatinization state of the starch.

| S-EPMC7894308 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data