Inducing β Phase Crystallinity in Block Copolymers of Vinylidene Fluoride with Methyl Methacrylate or Styrene.

ABSTRACT: Block copolymers of poly(vinylidene fluoride) (PVDF) with either styrene or methyl methacrylate (MMA) were synthesized and analyzed with respect to the type of the crystalline phase occurring. PVDF with iodine end groups (PVDF-I) was prepared by iodine transfer polymerization either in solution with supercritical CO₂ or in emulsion. To activate all iodine end groups Mn₂(CO)₁₀ is employed. Upon UV irradiation Mn(CO)₅ radicals are obtained, which abstract iodine from PVDF-I generating PVDF radicals. Subsequent polymerization with styrene or methyl methacrylate (MMA) yields block copolymers. Size exclusion chromatography and NMR results prove that the entire PVDF-I is converted. XRD, FT-IR, and differential scanning calorimetry (DSC) analyses allow for the identification of crystal phase transformation. It is clearly shown that the original α crystalline phase of PVDF-I is changed to the β crystalline phase in case of the block copolymers. For ratios of the VDF block length to the MMA block length ranging from 1.4 to 5 only β phase material was detected.

SUBMITTER: Golzari N

PROVIDER: S-EPMC6418974 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Nanoconfinement-Induced β-Phase Formation Inside Poly(vinylidene fluoride)-Based Block Copolymers.

Project description:The electroactive properties of poly(vinylidene fluoride) (PVDF) are a direct consequence of its crystalline phases. Although poorly understood, nanostructuring PVDF in confined geometries can drastically change its crystallization behavior. Therefore, we synthesized a variety of PVDF-based triblock copolymers to gain a better understanding of the melt crystallization and explore how crystallization is affected by the morphology and chemical nature of the amorphous block. Differential scanning calorimetry, small-/wide-angle X-ray scattering, and transmission electron microscopy gave us excellent insights into the morphology and the corresponding crystalline phases. We find that crystallization of PVDF inside spherical nanodomains occurs via a homogeneous nucleation mechanism leading to a large undercooling and the formation of the thermodynamically favorable ferroelectric β-phase. On the contrary, when confined crystallization occurs inside a lamellar morphology, or in the case of breakout crystallization, a heterogeneous nucleation process leads to the formation of the nonferroelectric α-phase. Furthermore, favorable melt interactions between both blocks induce crystallization into the polar γ-phase at moderate cooling rates.

| S-EPMC6052937 | biostudies-literature

Phase Transitions in Poly(vinylidene fluoride)/Polymethylene-Based Diblock Copolymers and Blends.

Project description:The crystallization and morphology of two linear diblock copolymers based on polymethylene (PM) and poly(vinylidene fluoride) (PVDF) with compositions PM23-b-PVDF77 and PM38-b-PVDF62 (where the subscripts indicate the relative compositions in wt%) were compared with blends of neat components with identical compositions. The samples were studied by SAXS (Small Angle X-ray Scattering), WAXS (Wide Angle X-ray Scattering), PLOM (Polarized Light Optical Microscopy), TEM (Transmission Electron Microscopy), DSC (Differential Scanning Calorimetry), BDS (broadband dielectric spectroscopy), and FTIR (Fourier Transform Infrared Spectroscopy). The results showed that the blends are immiscible, while the diblock copolymers are miscible in the melt state (or very weakly segregated). The PVDF component crystallization was studied in detail. It was found that the polymorphic structure of PVDF was a strong function of its environment. The number of polymorphs and their amount depended on whether it was on its own as a homopolymer, as a block component in the diblock copolymers or as an immiscible phase in the blends. The cooling rate in non-isothermal crystallization or the crystallization temperature in isothermal tests also induced different polymorphic compositions in the PVDF crystals. As a result, we were able to produce samples with exclusive ferroelectric phases at specific preparation conditions, while others with mixtures of paraelectric and ferroelectric phases.

| S-EPMC8348057 | biostudies-literature

Effective Interaction between Homo- and Heteropolymer Block of Poly(n-butyl acrylate)-b-poly(methyl methacrylate-r-styrene) Diblock Copolymers.

Project description:We investigated the segregation behavior of a molten diblock copolymer, poly(n-butyl acrylate)-b-poly(methyl methacrylate-r-styrene) (PBA-b-P(MMA-r-S)), wherein styrene (S) is incorporated as a comonomer in the second block to modulate the effective interaction between homopolymer and a random copolymer block. The temperature dependence of the effective interaction parameter χeff between n-butyl acrylate (BA) and the average monomer of the MMA-r-S random block was evaluated from small-angle X-ray scattering (SAXS) analysis using the random phase approximation (RPA) approach. The calculated χeff, as a function of the styrene fraction in the random copolymer block, shows a good agreement with the mean-field binary interaction model. This consistency indicates that the effective interaction between component BA and the average monomer of the random copolymer block is smaller than the interactions between pure components (χBA,MMA,χBA,S). The present study suggests that the introduction of a random copolymer block to a block copolymer can effectively reduce the degree of incompatibility of the block copolymer system without altering the constituent species, which may serve as a viable methodology in designing novel thermoplastic elastomers based on triblock or multiblock copolymers.

| S-EPMC10346336 | biostudies-literature

Quaternized Amphiphilic Block Copolymers/Graphene Oxide and a Poly(vinyl alcohol) Coating Layer on Graphene Oxide/Poly(vinylidene fluoride) Electrospun Nanofibers for Superhydrophilic and Antibacterial Properties.

Project description:Poly(vinylidene fluoride) (PVDF) is common polymer for electrospinning, however, its high hydrophobicity is a major drawback, which cause fouling. To introduce hydrophilicity and antibacterial activity, quaternary ammonium-functionalized amphiphilic diblock copolymers were synthesized and blended with a PVDF/graphene oxide (GO) solution, then, electrospun and coated with a hydrophilic polymer, poly(vinyl alcohol) (PVA). The amphiphilic block copolymer, consisting of a hydrophobic poly(methyl methacrylate) block and a hydrophilic poly[N,N-2-(dimethylamino)-ethyl methacrylate) block (PMMA-b-PDMAEMA), was synthesized. Polymeric quaternary ammonium with three different alkyl chain lengths (C2, C4, and C8) were successfully introduced to obtain as q-PMMA-b-PDMAEMA. The q-PMMA-b-PDMAEMA in the nanofiber matrix was confirmed by C=O bands (1734 cm-1) in the Fourier transform infrared spectra. Nano-sized spherical protuberances were distributed on the surface as revealed by field emission scanning and transmission electron microscopies. The PVDF/GO/q-PMMA-b-PDMAEMA@PVA nanofibers has superhydrophilic properties (water contact angle?=?0-20°) and the pure water flux was generally improved by increasing the alkyl chain length. When introducing the longest alkyl chain (C8,OBC), the total fouling ratio was the lowest (49.99%) and the bacteria removal capacities after 60?min were the highest for both Escherichia coli (4.2?×?105 CFU/mg) and Staphylococcus aureus (6.1?×?105 CFU/mg) via growth inhibition and cytoplasmic membrane damage.

| S-EPMC6344507 | biostudies-literature

Tannic Acid-Mediated Aggregate Stabilization of Poly(N-vinylpyrrolidone)-b-poly(oligo (ethylene glycol) methyl ether methacrylate) Double Hydrophilic Block Copolymers.

Project description:The self-assembly of block copolymers in aqueous solution is an important field in modern polymer science that has been extended to double hydrophilic block copolymers (DHBC) in recent years. In here, a significant improvement of the self-assembly process of DHBC in aqueous solution by utilizing a linear-brush macromolecular architecture is presented. The improved self-assembly behavior of poly(N-vinylpyrrolidone)-b-poly(oligo(ethylene glycol) methyl ether methacrylate) (PVP-b-P(OEGMA)) and its concentration dependency is investigated via dynamic light scattering (DLS) (apparent hydrodynamic radii ≈ 100-120 nm). Moreover, the DHBC assemblies can be non-covalently crosslinked with tannic acid via hydrogen bonding, which leads to the formation of small aggregates as well (apparent hydrodynamic radius ≈ 15 nm). Non-covalent crosslinking improves the self-assembly and stabilizes the aggregates upon dilution, reducing the concentration dependency of aggregate self-assembly. Additionally, the non-covalent aggregates can be disassembled in basic media. The presence of aggregates was studied via cryogenic scanning electron microscopy (cryo-SEM) and DLS before and after non-covalent crosslinking. Furthermore, analytical ultracentrifugation of the formed aggregate structures was performed, clearly showing the existence of polymer assemblies, particularly after non-covalent crosslinking. In summary, we report on the completely hydrophilic self-assembled structures in solution formed from fully biocompatible building entities in water.

| S-EPMC6566864 | biostudies-literature

Differential orientation and conformation of surface-bound keratinocyte growth factor on (hydroxyethyl)methacrylate, (hydroxyethyl)methacrylate/methyl methacrylate, and (hydroxyethyl)methacrylate/methacrylic acid hydrogel copolymers.

Project description:The development of hydrogels for protein delivery requires protein-hydrogel interactions that cause minimal disruption of the protein's biological activity. Biological activity can be influenced by factors such as orientational accessibility for receptor binding and conformational changes, and these factors can be influenced by the hydrogel surface chemistry. (Hydroxyethyl)methacrylate (HEMA) hydrogels are of interest as drug delivery vehicles for keratinocyte growth factor (KGF) which is known to promote re-epithelialization in wound healing. The authors report here the surface characterization of three different HEMA hydrogel copolymers and their effects on the orientation and conformation of surface-bound KGF. In this work, they characterize two copolymers in addition to HEMA alone and report how protein orientation and conformation is affected. The first copolymer incorporates methyl methacrylate (MMA), which is known to promote the adsorption of protein to its surface due to its hydrophobicity. The second copolymer incorporates methacrylic acid (MAA), which is known to promote the diffusion of protein into its surface due to its hydrophilicity. They find that KGF at the surface of the HEMA/MMA copolymer appears to be more orientationally accessible and conformationally active than KGF at the surface of the HEMA/MAA copolymer. They also report that KGF at the surface of the HEMA/MAA copolymer becomes conformationally unfolded, likely due to hydrogen bonding. KGF at the surface of these copolymers can be differentiated by Fourier-transform infrared-attenuated total reflectance spectroscopy and time-of-flight secondary ion mass spectrometry in conjunction with principal component analysis. The differences in KGF orientation and conformation between these copolymers may result in different biological responses in future cell-based experiments.

| S-EPMC6905655 | biostudies-literature

Preparation and electroactive phase adjustment of Ag-doped poly(vinylidene fluoride) (PVDF) films.

Project description:The crystallinities of Ag-doped poly(vinylidene fluoride) (PVDF) films were modified by removing Ag+ using a novel washing process, which allowed control of the ratio of γ- and β-phases. The polarity of the composite film without Ag+ removal through the washing process reached 98%, and the β-phase content in the total electroactive phase was increased to 61%, according to Fourier-transform infrared spectroscopy. When Ag+ were removed through a process involving several cycles of washing, filtering, drying, and re-dissolving, the highest ratio of the γ-phase was increased to 67%, 28% higher than that before washing. This showed that Ag+ induced β-phase formation while Ag nanoparticles induced γ-phase formation, and that the ratio of γ- and β-phases in PVDF composite films can be controlled to suit specific applications by this washing process.

| S-EPMC9076169 | biostudies-literature

Bioinspired amphiphilic phosphate block copolymers as non-fluoride materials to prevent dental erosion.

Project description:Inspired by the fact that certain natural proteins, e.g. casein phosphopeptide or amelogenin, are able to prevent tooth erosion (mineral loss) and to enhance tooth remineralization, a synthetic amphiphilic diblock copolymer, containing a hydrophilic methacryloyloxyethyl phosphate block (MOEP) and a hydrophobic methyl methacrylate block (MMA), was designed as a novel non-fluoride agent to prevent tooth erosion under acidic conditions. The structure of the polymer, synthesized by reversible addition-fragment transfer (RAFT) polymerization, was confirmed by gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FTIR), and nuclear magnetic resonance spectroscopy (NMR). While the hydrophilic PMOEP block within the amphiphilic block copolymer strongly binds to the enamel surface, the PMMA block forms a hydrophobic shell to prevent acid attack on tooth enamel, thus preventing/reducing acid erosion. The polymer treatment not only effectively decreased the mineral loss of hydroxyapatite (HAP) by 36-46% compared to the untreated control, but also protected the surface morphology of the enamel specimen following exposure to acid. Additionally, experimental results confirmed that low pH values and high polymer concentrations facilitate polymer binding. Thus, the preliminary data suggests that this new amphiphilic diblock copolymer has the potential to be used as a non-fluoride ingredient for mouth-rinse or toothpaste to prevent/reduce tooth erosion.

| S-EPMC4235796 | biostudies-literature

Fluoride releasing in polymer blends of poly(ethylene oxide) and poly(methyl methacrylate)

Project description: Not available

| S-EPMC10884178 | biostudies-literature

Curing of Poly(styrene-co-methyl methacrylate-co-2-hydroxyethyl methacrylate) Terpolymers in the Presence of Amino Compounds of Different Structures.

Project description:The process of curing the acrylic oligomers for rapid thermal curing coatings in the presence of hexa(methoxymethyl)melamine (HMMM), tetra(butoxymethyl)glycoluril (TBMG), and tetra(methoxymethyl)glycoluril (TMMG) has been studied. When HMMM is used as a hardener, the content of hydroxyl groups in the terpolymer and also the crosslinking agent concentration have little effect on the initial cure rate. It has been established that during the curing of the TMMG composition, the amount of the network polymer and the initial curing rate decrease at short curing times only. It has also been revealed that the use of butoxy groups instead of methoxy groups as blocking agents leads both to a decrease in the initial cure rate and the gel fraction limiting value from 98 to 80%. When it comes to TBMG-containing compositions, a decrease in the part of hydroxyl groups in the copolymer leads to a significant fall in the initial curing rate and also in the gel fraction content. Regardless of the crosslinking agent used, an acceleration of the curing process is observed with an increase in the catalyst content in the compositions.

| S-EPMC10180959 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data