Effect of Very High Charge Density and Monomer Constitution on the Synthesis and Properties of Cationic Polyelectrolytes.

ABSTRACT: The free-radical homopolymerization of 1,3-bis(N,N,N-trimethylammonium)-2-propylmethacrylate dichloride (di-M) and 1,3-bis(N,N,N-trimethylammonium)-2-propylacrylate dichloride (di-A) in aqueous solution yields cationic polyelectrolytes (PEL) with theoretical/structural charge spacing of only ?0.12 nm. The high charge density causes condensation of ?82% of the chloride counterions. The high level of counterion condensation reduces the ionic strength in the polymerizing batch when the monomer molecules connect to PEL chains. This has the consequence that the hydrodynamic and excluded volume of the PEL molecules will change. Studies of the free radical polymerization revealed non-ideal polymerization kinetics already at low conversion and additionally autoacceleration above a certain monomer concentration and conversion. Similar autoacceleration was not observed for monomers yielding PEL with charge spacing of 0.25 or 0.5 nm. Coulomb interactions, monomer association, steric effects, and specific features of the monomer constitution have been evaluated concerning their contributions to the concentration dependence and conversion dependence of kinetic parameters. The different backbone constitutions of di-M and di-A not only influence the polymerization kinetics but also equip poly(di-M) with higher hydrolytic stability. The experimental results confirm the impact of electrochemical parameters and the necessity to reconsider their inclusion in kinetic models.

SUBMITTER: Ahmadloo H

PROVIDER: S-EPMC6432479 | biostudies-literature | 2016 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of Very High Charge Density and Monomer Constitution on the Synthesis and Properties of Cationic Polyelectrolytes.

Ahmadloo Hamideh H Losada Ricardo R Wandrey Christine C

Polymers 20160616 6

The free-radical homopolymerization of 1,3-bis(<i>N,N,N</i>-trimethylammonium)-2-propylmethacrylate dichloride (di-M) and 1,3-bis(<i>N,N,N</i>-trimethylammonium)-2-propylacrylate dichloride (di-A) in aqueous solution yields cationic polyelectrolytes (PEL) with theoretical/structural charge spacing of only ≈0.12 nm. The high charge density causes condensation of ≈82% of the chloride counterions. The high level of counterion condensation reduces the ionic strength in the polymerizing batch when th ...[more]

PMID: 30979329

Similar Datasets

Project description:Three anionic fluorene-based alternating conjugated polyelectrolytes (CPEs) have been synthesized that have 9,9-bis(4-phenoxy-butylsulfonate) fluorene-2,7-diyl and 1,4-phenylene (PBS-PFP), 4,4'-biphenylene (PBS-PFP2), or 4,4″-p-terphenylene (PBS-PFP3) groups, and the effect of the length of the oligophenylene spacer on their aggregation and photophysics has been studied. All form metastable dispersions in water, but can be solubilized using methanol, acetonitrile, or dioxane as cosolvents. This leads to increases in their emission intensities and blue shifts in fluorescence maxima due to break-up of aggregates. In addition, the emission maximum shifts to the blue and the loss of vibronic structure are observed when the number of phenylene rings is increased. Debsity Functional Theory (DFT) calculations suggest that this is due to increasing conformational flexibility as the number of phenylene rings increases. This is supported by increasing amplitude in the fast component in the fluorescence decay. The nonionic surfactant n-dodecylpentaoxyethylene glycol ether (C12E₅) also breaks up aggregates, as seen by changes in fluorescence intensity and maximum. However, the loss in vibrational structure is less pronounced in this case, possibly due to a more rigid environment in the mixed surfactant-CPE aggregates. Further information on the aggregates formed with C12E₅ was obtained by electrical conductivity measurements, which showed an initial increase in specific conductivity upon addition of surfactants, while at higher surfactant/CPE molar ratios a plateau was observed. The specific conductance in the plateau region decreased in the order PBS-PFP3 < PBS-PFP2 < PBS-PFP, in agreement with the change in charge density on the CPE. The reverse process of aggregate formation has been studied by injecting small volumes of solutions of CPEs dissolved at the molecular level in a good solvent system (50% methanol-water) into the poor solvent, water. Aggregation was monitored by changes in both fluorescence and light scattering. The rate of aggregation increases with hydrophobicity and concentration of sodium chloride but is only weakly dependent on temperature.

Project description:This work addresses the role of charge regulation (CR) and the associated fluctuations in the conformational and mechanical properties of weak polyelectrolytes. Due to CR, changes in the pH-value modifies the average macromolecular charge and conformational equilibria. A second effect is that, for a given average charge per site, fluctuations can alter the intensity of the interactions by means of correlation between binding sites. We investigate both effects by means of Monte Carlo simulations at constant pH-value, so that the charge is a fluctuating quantity. Once the average charge per site is available, we turn off the fluctuations by assigning the same average charge to every site. A constant charge MC simulation is then performed. We make use of a model which accounts for the main fundamental aspects of a linear flexible polyelectrolyte that is, proton binding, angle internal rotation, bond stretching and bending. Steric excluded volume and differentiated treatment for short-range and long-range interactions are also included. This model can be regarded as a kind of "minimal" in the sense that it contains a minimum number of parameters but still preserving the atomistic detail. It is shown that, if fluctuations are activated, gauche state bond probabilities increase and the persistence length decreases, so that the polymer becomes more folded. Macromolecular stretching is also analyzed in presence of CR (the charge depends on the applied force) and without CR (the charge is fixed to the value at zero force). The analysis of the low force scaling behavior concludes that Pincus exponent becomes pH-dependent. Both, with and without CR, a transition from 1/2 at high pH-values (phantom chain) to 3/5 at low pH-values (Pincus regime) is observed. Finally, the intermediate force stretching regime is investigated. It is found that CR induces a moderate influence in the force-extension curves and persistence length (which in this force regime becomes force-dependent). It is thus concluded that the effect of CR on the stretching curves is mainly due to the changes in the average charge at zero force. It is also found that, for the cases studied, the effect of steric excluded volume is almost irrelevant compared to electrostatic interactions.

Dataset Information

Effect of Very High Charge Density and Monomer Constitution on the Synthesis and Properties of Cationic Polyelectrolytes.

Publications

Effect of Very High Charge Density and Monomer Constitution on the Synthesis and Properties of Cationic Polyelectrolytes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets