Surface Property Modification of Silver Nanoparticles with Dopamine-Functionalized Poly(pentafluorostyrene) via RAFT Polymerization.

ABSTRACT: This research aims to synthesize a dopamine-functionalized macromolecular anchor to perform surface modification on the target nanostructures. A molecular anchor, 3,4-dichloro-1-[2-(3,4-dihydroxyphenyl)ethyl]-1H-pyrrole-2,5-dione, was successfully synthesized from dopamine and 2,3-dichloromaleic anhydride. The anchor acted as a linkage to couple the chains of poly(pentafluorostyrene) (PPFS) which were synthesized via reversible addition fragmentation chain transfer (RAFT) polymerization. Modification was successfully performed to silver nanoparticles (AgNPs) by deposition of the dopamine-functionalized coupled PPFS onto the surface of the particles. The modified AgNPs had demonstrated improved dispersibility in organic solvent due to the hydrophobic nature of PPFS. To modify the surface chemistry of the nanoparticles further, thioglucose was grafted onto the structure of the coupled PPFS via thiol-fluoro nucleophilic substitution at the para-position of the pentafluorophenyl groups on the monomer units. The presence of sugar moieties on the coupled PPFS increased its hydrophilicity, which allowed the modified AgNPs to be readily dispersed in aqueous solvent.

SUBMITTER: Fan KW

PROVIDER: S-EPMC6432553 | biostudies-literature | 2016 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A poly(2-(dimethylamino)ethyl methacrylate) (PDMA) chain transfer agent (CTA) is used for the reversible addition-fragmentation chain transfer (RAFT) alcoholic dispersion polymerization of benzyl methacrylate (BzMA) in ethanol at 70 °C. THF GPC analysis indicated a well-controlled polymerization with molecular weight increasing linearly with conversion. GPC traces also showed high blocking efficiency with no homopolymer contamination apparent and Mw/Mn values below 1.35 in all cases. 1H NMR studies confirmed greater than 98% BzMA conversion for a target PBzMA degree of polymerization (DP) of up to 600. The PBzMA block becomes insoluble as it grows, leading to the in situ formation of sterically stabilized diblock copolymer nanoparticles via polymerization-induced self-assembly (PISA). Fixing the mean DP of the PDMA stabilizer block at 94 units and systematically varying the DP of the PBzMA block enabled a series of spherical nanoparticles of tunable diameter to be obtained. These nanoparticles were characterized by TEM, DLS, MALLS, and SAXS, with mean diameters ranging from 35 to 100 nm. The latter technique was particularly informative: data fits to a spherical micelle model enabled calculation of the core diameter, surface area occupied per copolymer chain, and the mean aggregation number (Nagg). The scaling exponent derived from a double-logarithmic plot of core diameter vs PBzMA DP suggests that the conformation of the PBzMA chains is intermediate between the collapsed and fully extended state. This is in good agreement with 1H NMR studies, which suggest that only 5-13% of the BzMA residues of the core-forming chains are solvated. The Nagg values calculated from SAXS and MALLS are in good agreement and scale approximately linearly with PBzMA DP. This suggests that spherical micelles grow in size not only as a result of the increase in copolymer molecular weight during the PISA synthesis but also by exchange of individual copolymer chains between micelles and/or by sphere-sphere fusion events.

Dataset Information

Surface Property Modification of Silver Nanoparticles with Dopamine-Functionalized Poly(pentafluorostyrene) via RAFT Polymerization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets