Mechanical properties of magnetic gels containing rod-like composite particles.

ABSTRACT: Magnetic gels (ferrogels) are heterogeneous systems structured at the nanoscale that contains magnetic particles dispersed in three-dimensional networks of polymer chains. In the present work, the magnetic particles were synthesized with a core-shell structure, consisting of sepiolite particles covered by magnetite nanoparticles. These composite particles had a rod-like shape with a high aspect ratio. The obtained sepiolite-magnetite particles showed a high enough susceptibility and saturation magnetization. The magneto-rheological (MR) properties, and the intensity of the MR effect, of aqueous suspensions of the synthesized particles were studied. The particles, functionalized by adsorption of alginate molecules, were imbedded in alginate hydrogels to get homogeneous soft materials. The particles were linked to the polymer chains as the knots in a network and dominated in a great extent the mechanical properties of the materials. After determining the optimal compositions of the ferrogels, their viscoelastic properties were measured in the absence/presence of magnetic fields. The results pointed out that the MR effect provided by the clay-magnetite particles was considerably more intense than those achieved in ferrogels that contain spherical magnetic microparticles. Therefore, the imbedding of rod-shaped magnetic particles in hydrogels allows controlling the mechanical properties in a wider range than in conventional ferrogels. This article is part of the theme issue 'Heterogeneous materials: metastable and non-ergodic internal structures'.

SUBMITTER: Abrougui MM

PROVIDER: S-EPMC6460065 | biostudies-literature | 2019 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Mechanical properties of magnetic gels containing rod-like composite particles.

Abrougui Mariem M MM Lopez-Lopez Modesto T MT Duran Juan D G JDG

Philosophical transactions. Series A, Mathematical, physical, and engineering sciences 20190401 2143

Magnetic gels (ferrogels) are heterogeneous systems structured at the nanoscale that contains magnetic particles dispersed in three-dimensional networks of polymer chains. In the present work, the magnetic particles were synthesized with a core-shell structure, consisting of sepiolite particles covered by magnetite nanoparticles. These composite particles had a rod-like shape with a high aspect ratio. The obtained sepiolite-magnetite particles showed a high enough susceptibility and saturation m ...[more]

PMID: 30827211

Similar Datasets

Project description:Objective:To compare the elastic modulus, flexural strength, and hardness of an experimental resin based composite (RBC) with and without containing silver nanoparticles (AgNPs) and bioactive glass (BAG) with a commercially available RBC. Methods:This study was conducted, during the period August 2016-May 2018, at the Department of Dental Materials, Peshawar Dental College, Peshawar (Pakistan) and Department of Chemistry, University of Montreal, Canada. Test specimens made in the commercial RBC acted as Group-1 (G1). An experimental RBC containing 70 wt % filler content was synthesized. It was first used as such to prepare test specimens to act as the experimental control group (G2). This RBC was then modified by adding various amounts of BAG (5%, 10% and 15%) and a fixed amount of 0.009% AgNPs to use the so modified RBCs for preparing the test specimens to belong to three groups (G3, G4 & G5). The AgNPs had been synthesized in situ by reduction of salt during photo-polymerization. Flexural strength (FS), elastic modulus (EM) and Vickers hardness were determined using universal testing machine and hardness tester respectively. Data were analyzed using one-way ANOVA and Tukey post-hoc test. Results:Except for G3 restorations showing significantly lower mean FS value, the FS for those in the other groups were not significantly different (p>0.05). Elastic modulus of the experimental RBC restorations was though higher than those of the others but the difference was statistically insignificant (p>0.05). Reduced Vickers hardness values were documented for the restorations in the G4 and G5 compared to those in the G3 but again the difference was insignificant (p>0.05). Flexural strength and hardness values of the test specimens in the experimental RBCs were significantly lower than those made in the commercial hybrid RBC (p<0.05). Conclusion:BAG and AgNPs addition to the experimental RBC in the mentioned concentration adversely affected the tested mechanical properties.

Project description:Cellularized collagen gels are a common model in tissue engineering, but the relationship between the microstructure and bulk mechanical properties is only partially understood. Multiphoton microscopy (MPM) is an ideal non-invasive tool for examining collagen microstructure, cellularity and crosslink content in these gels. In order to identify robust image parameters that characterize microstructural determinants of the bulk elastic modulus, we performed serial MPM and mechanical tests on acellular and cellularized (normal human lung fibroblasts) collagen hydrogels, before and after glutaraldehyde crosslinking. Following gel contraction over 16 days, cellularized collagen gel content approached that of native connective tissues (?200 mg ml?¹). Young's modulus (E) measurements from acellular collagen gels (range 0.5-12 kPa) exhibited a power-law concentration dependence (range 3-9 mg ml?¹) with exponents from 2.1 to 2.2, similar to other semiflexible biopolymer networks such as fibrin and actin. In contrast, cellularized collagen gel stiffness (range 0.5-27 kPa) produced concentration-dependent exponents of 0.7 uncrosslinked and 1.1 crosslinked (range ?5-200 mg ml?¹). The variation in E of cellularized collagen hydrogels can be explained by a power-law dependence on robust image parameters: either the second harmonic generation (SHG) and two-photon fluorescence (TPF) (matrix component) skewness (R²=0.75, exponents of -1.0 and -0.6, respectively); or alternatively the SHG and TPF (matrix component) speckle contrast (R²=0.83, exponents of -0.7 and -1.8, respectively). Image parameters based on the cellular component of TPF signal did not improve the fits. The concentration dependence of E suggests enhanced stress relaxation in cellularized vs. acellular gels. SHG and TPF image skewness and speckle contrast from cellularized collagen gels can predict E by capturing mechanically relevant information on collagen fiber, cell and crosslink density.

Dataset Information

Mechanical properties of magnetic gels containing rod-like composite particles.

Publications

Mechanical properties of magnetic gels containing rod-like composite particles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets