Optimization of Epoxy Resin: An Investigation of Eggshell as a Synergic Filler.

ABSTRACT: Epoxy resin based on bisphenol A diglycidyl ether/anhydride methyl tetrahydrophthalic/2,4,6-tris(dimethylaminomethyl)phenol (DGEBA/MTHPA/DEH 35) was produced by magnetic stirring; chicken eggshell (ES) was added as cure improver. Thermal stability, cure parameters, mechanical properties, and fracture surface were investigated by thermogravimetry (TGA), differential scanning calorimetry (DSC), tensile experiments, and scanning electron microscopy (SEM). In general, the addition of ES slightly decreased the thermal stability, being T0.05 5% lower than that of the reference sample. The cure rate increased with the heating rates, while best results were obtained upon addition of neat membrane (M) from ES. Surprisingly, the mechanical properties were significantly improved with ES as well as with M, being the Young's modulus 18% higher, the tensile strength 50% higher, and the deformation 35% higher than those of epoxy resin. SEM images showed that the synthetic compounds presented a smooth fracture surface, while the compounds with ES and M had a rougher surface with multiplane fractures, suggesting a fracture with higher energy absorption. In conclusion, epoxy/ES composites with better performance were produced, and effective tools are provided to control and attain in the future even better properties with ecological features.

SUBMITTER: Souza JWL

PROVIDER: S-EPMC6540584 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Optimization of Epoxy Resin: An Investigation of Eggshell as a Synergic Filler.

Souza José William de Lima JWL Jaques Nichollas Guimarães NG Popp Matthias M Kolbe Jana J Fook Marcus Vinícius Lia MVL Wellen Renate Maria Ramos RMR

Materials (Basel, Switzerland) 20190508 9

Epoxy resin based on bisphenol A diglycidyl ether/anhydride methyl tetrahydrophthalic/2,4,6-tris(dimethylaminomethyl)phenol (DGEBA/MTHPA/DEH 35) was produced by magnetic stirring; chicken eggshell (ES) was added as cure improver. Thermal stability, cure parameters, mechanical properties, and fracture surface were investigated by thermogravimetry (TGA), differential scanning calorimetry (DSC), tensile experiments, and scanning electron microscopy (SEM). In general, the addition of ES slightly dec ...[more]

PMID: 31071924

Similar Datasets

Project description:Adhesion interaction of epoxy resin with the basal surfaces of h-BN and graphite is investigated with the first-principles density functional theory calculations in conjunction with the dispersion correction. The h-BN/epoxy and graphite/epoxy interfaces play an important role in producing nanocomposite materials with excellent thermal dissipation properties. The epoxy resin structure is simulated by using four kinds of fragmentary models. Their structures are optimized on the h-BN and graphite surfaces after an annealing simulation. The distance between the epoxy fragment and the surface is about 3 Å. At the interface between h-BN and epoxy resin, no H-bonding formation is observed, though one could expect that the active functional groups of epoxy resin, such as hydroxyl (-OH) group, would be involved in a hydrogen-bonding interaction with nitrogen atoms of the h-BN surface. The adhesion energies for the two interfaces are calculated, showing that these two interfaces are characterized by almost the same strength of adhesion interaction. To obtain the adhesion force-separation curve for the two interfaces, the potential energy surface associated with the detachment of the epoxy fragment from the surface is calculated with the help of the nudged elastic band method and then the adhesion force is obtained by using either the Morse-potential approximation or the Hellmann-Feynman force calculation. The results from both methods agree with each other. The maximum adhesion force for the h-BN/epoxy interface is as high as that for the graphite/epoxy interface. To better understand this result, a force-decomposition analysis is carried out, and it has been disclosed that the adhesion forces working at both interfaces mainly come from the dispersion force. The trend of increase in the C 6 parameters used for the dispersion correction for the atoms included in the h-BN or graphite surface is in the order: N < C < B, which reasonably explains why the strengths of the dispersion forces operating at the two interfaces are similar. Also, the electron localization function analysis can explain why the h-BN surface cannot form an H bond with the hydroxyl group in epoxy resin.

Dataset Information

Optimization of Epoxy Resin: An Investigation of Eggshell as a Synergic Filler.

Publications

Optimization of Epoxy Resin: An Investigation of Eggshell as a Synergic Filler.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets