Ultrahigh Performance of Nanoengineered Graphene-Based Natural Jute Fiber Composites.

ABSTRACT: Natural fibers composites are considered as a sustainable alternative to synthetic composites due to their environmental and economic benefits. However, they suffer from poor mechanical and interfacial properties due to a random fiber orientation and weak fiber-matrix interface. Here we report nanoengineered graphene-based natural jute fiber preforms with a new fiber architecture (NFA) which significantly improves their mechanical properties and performances. Our graphene-based NFA of jute fiber preform enhances the Young modulus of jute-epoxy composites by ?324% and tensile strength by ?110% more than untreated jute fiber composites, by arranging fibers in a parallel direction through individualization and nanosurface engineering with graphene derivatives. This could potentially lead to manufacturing of high-performance natural alternatives to synthetic composites in various stiffness-driven applications.

SUBMITTER: Sarker F

PROVIDER: S-EPMC6566500 | biostudies-literature | 2019 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Ultrahigh Performance of Nanoengineered Graphene-Based Natural Jute Fiber Composites.

Sarker Forkan F Potluri Prasad P Afroj Shaila S Koncherry Vivek V Novoselov Kostya S KS Karim Nazmul N

ACS applied materials & interfaces 20190530 23

Natural fibers composites are considered as a sustainable alternative to synthetic composites due to their environmental and economic benefits. However, they suffer from poor mechanical and interfacial properties due to a random fiber orientation and weak fiber-matrix interface. Here we report nanoengineered graphene-based natural jute fiber preforms with a new fiber architecture (NFA) which significantly improves their mechanical properties and performances. Our graphene-based NFA of jute fiber ...[more]

PMID: 31063352

Similar Datasets

Project description:A very low dosage of graphene oxide (GO) can enhance the mechanical durability of cement composites, but the reinforcing enhancement is highly dependent on the uniform dispersion of graphene in the matrix. Carboxylic groups at GO nanosheets have a decisive effect on GO aggregation in an alkaline cement solution because they have a strong complexation ability with aqueous Ca2+ released by cement hydration and subsequently crosslinks the adjacent graphene sheets, causing the immediate coagulation of GO. The available methods of homogeneously dispersing GO in a cement slurry cannot completely eliminate this carboxylic-crosslinking-induced GO coagulation. In this study, many hydroxyl groups were introduced onto the edge and planar nanosheets to prepare water-soluble hydroxylated graphene (HO-G) by facile ball milling. The structure of HO-G was thoroughly characterized in detail, and its dispersion behavior in pure water and Ca(OH)2 was extensively investigated. These results showed that the prepared HO-G exhibited good hydrophilicity and excellent colloidal dispersion ability against high pH and Ca2+ ions compared to GO. The effect of HO-G on the workability, mechanical strength, and chloride penetrability of a cement mortar was further studied. At a content of 0.03% by cement mass, HO-G provided 28.62 and 21.19% enhancements of compressive strength and 3.85 and 7.89% enhancements of flexural strength at 3 and 28 days, respectively, while the non-steady-state migration coefficient decreased by 31.51% compared to the reference mortar. Compared to GO, a lower dosage of HO-G exhibited a similar reinforcing effect to cement composites with little adverse impact on the fluidity of the fresh cement slurry. Moreover, the addition of HO-G could refine the pore structure, accelerate the hydration process of cement to some degree, and generate more hydration products so that the structure of the cement mortar was densified. Considering its environmentally friendly preparation, HO-G, as a promising reinforcing nanofiller, could provide a new solution to develop nanoengineered cement composites.

Project description:This work developed novel jute-yarn, non-crimp, unidirectional (UD) preforms and their composites, with three different types of warp jute yarns of varying linear densities and twists in the dry UD preforms, in order to present a possible solution to the detrimental effects of higher yarn twists and crimp at the warp-weft yarn interlacements of traditional, woven, preform-based composites on their mechanical properties. In the developed UD preforms, warp jute yarns were placed in parallel by using a wooden picture-frame pin board, with the minimal number of glass weft yarns to avoid crimp at the warp-weft yarns interlacements, which can significantly enhance the load-bearing ability of UD composites compared to traditional, woven, preform composites. It was found that an optimal combination of jute warp yarn linear densities and twists in the UD preforms is important to achieve the best possible mechanical properties of newly developed UD composites, because it encourages a proper polymer-matrix impregnation on jute fibres, leading to excellent fibre-matrix interface bonding. Composites made from the 25 lb/spindle jute warp yarn linear density (UD25) exhibited higher tensile and flexural properties than other UD composites (UD20, UD30). All the UD composites showed a much better performance compared to the traditional woven preform composites (W20), which were obviously related to the higher crimp and yarn interlacements, less load-carrying capacity, and poor fiber-matrix interfaces of W20 composites. UD25 composites exhibited a significant enhancement in tensile modulus by ~232% and strength by ~146%; flexural modulus by 138.5% and strength by 145% compared to W20 composites. This reveals that newly developed, non-crimp, UD preform composites can effectively replace the traditional woven composites in lightweight, load-bearing, complex-shaped composite applications, and hence, this warrants further investigations of the developed composites, especially on long-term and dynamic-loading mechanical characterizations.

Dataset Information

Ultrahigh Performance of Nanoengineered Graphene-Based Natural Jute Fiber Composites.

Publications

Ultrahigh Performance of Nanoengineered Graphene-Based Natural Jute Fiber Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets