Effect of Early Age-Curing Methods on Drying Shrinkage of Alkali-Activated Slag Concrete.

ABSTRACT: Drying shrinkage of alkali-activated slag concrete (AASC) is significantly greater than that of concrete made with ordinary Portland cement (OPC). It limits the large-scale application of AASC in field engineering. This study investigates the effect of early age-curing methods, including water curing, curing in elevated-temperature water, and CO2 curing, on drying shrinkage of AASC. Scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric (TG-DTG), and mercury intrusion porosimetry (MIP) were carried out to analyze the composition and microstructure of hydration products, to provide deeper understanding of drying shrinkage of AASC. The results show that water curing decreased drying shrinkage of both C30 and C50 AASC moderately compared to air curing, while it was more effective for C30 AASC. Curing in water of elevated temperature and CO2 curing were very beneficial to mitigate drying shrinkage of AASC. Heat curing decreased drying shrinkage of AASC up to 80%. SEM and TG-DTG results show that denser microstructure formed because of the accelerated hydration, resulting in lower porosity and lower proportion of pores smaller than 25 nm that contributed to the reduction of drying shrinkage. In addition, under high-temperature curing, most autogenous shrinkage of AASC occurred in the first few days because hydration was accelerated. After measurement of drying shrinkage was started, recorded autogenous shrinkage of AASC cured in elevated-temperature water should be much less than that of AASC cured at normal temperature. It is another important reason for the reduction of drying shrinkage. Carbonation occurring in the CO2 curing period led to the decalcification of C-(A)-S-H gel; it coarsened the pore-size distribution and decreased the total porosity. Therefore, drying shrinkage of C30 and C50 AASC was declined by 49% and 53% respectively.

SUBMITTER: Cai Y

PROVIDER: S-EPMC6566924 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of Early Age-Curing Methods on Drying Shrinkage of Alkali-Activated Slag Concrete.

Cai Yuxin Y Yu Linwen L Yang Yong Y Gao Yang Y Yang Changhui C

Materials (Basel, Switzerland) 20190518 10

Drying shrinkage of alkali-activated slag concrete (AASC) is significantly greater than that of concrete made with ordinary Portland cement (OPC). It limits the large-scale application of AASC in field engineering. This study investigates the effect of early age-curing methods, including water curing, curing in elevated-temperature water, and CO<sub>2</sub> curing, on drying shrinkage of AASC. Scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric (TG-DTG), and mercury in ...[more]

PMID: 31109048

Similar Datasets

Project description:Alkali-activated concrete is an eco-friendly construction material that is used to preserve natural resources and promote sustainability in the construction industry. This emerging concrete consists of fine and coarse aggregates and fly ash that constitute the binder when mixed with alkaline activators, such as sodium hydroxide (NaOH) and sodium silicate (Na2SiO3). However, understanding its tension stiffening and crack spacing and width is of critical importance in fulfilling serviceability requirements. Therefore, this research aims to evaluate the tension stiffening and cracking performance of alkali-activated (AA) concrete. The variables considered in this study were compressive strength (fc) and concrete cover-to-bar diameter (Cc/db) ratios. After casting the specimen, they were cured before testing at ambient curing conditions for 180 days to reduce the effects of concrete shrinkage and obtain more realistic cracking results. The results showed that both AA and OPC concrete prisms develop slightly similar axial cracking force and corresponding cracking strain, but OPC concrete prisms exhibited a brittle behavior, resulting in a sudden drop in the load-strain curves at the crack location. In contrast, AA concrete prisms developed more than one crack simultaneously, suggesting a more uniform tensile strength compared to OPC specimens. The tension-stiffening factor (β) of AA concrete exhibited better ductile behavior than OPC concrete due to the strain compatibility between concrete and steel even after crack ignition. It was also observed that increasing the confinement (Cc/db ratio) around the steel bar delays internal crack formation and enhances tension stiffening in AAC. Comparing the experimental crack spacing and width with the values predicted using OPC codes of practice, such as EC2 and ACI 224R, revealed that EC2 tends to underestimate the maximum crack width, while ACI 224R provided better predictions. Thus, models to predict crack spacing and width have been proposed accordingly.

Dataset Information

Effect of Early Age-Curing Methods on Drying Shrinkage of Alkali-Activated Slag Concrete.

Publications

Effect of Early Age-Curing Methods on Drying Shrinkage of Alkali-Activated Slag Concrete.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets