Nitrogen-Doped Nanoporous Carbon Nanospheroids for Selective Dye Adsorption and Pb(II) Ion Removal from Waste Water.

ABSTRACT: In the presence of melamine and block copolymers, namely, F108, F127, and P123, nitrogen-doped nanoporous carbon nanospheroids (N@CNSs) were synthesized by the hydrothermal process. The F127-modified sample (CNF127) exhibits the maximum Brunauer-Emmett-Teller (BET) surface area of 773.4 m²/g with a pore volume of 0.877 cm³/g. The microstructural study reveals that nanospheroids of size 50-200 nm were aggregated together to form a chainlike structure for all triblock copolymer-modified samples. The X-ray photoelectron spectroscopy study shows the binding energies of 398.33 and 400.7 eV attributed to sp² (C-N=C)- and sp³ (C-N)-hybridized nitrogen-bonded carbons, respectively. The synthesized N@CNS samples showed selective adsorption of organic dye methylene blue (MB) in the presence of methyl orange (MO) as well as Pb(II) ion removal from contaminated water. The adsorptions for MB and Pb(II) ions followed pseudo-first-order and pseudo-second-order kinetic models, respectively. The sample CNF127 showed the highest adsorption of 73 and 99.82 mg/g for MB and Pb(II) adsorptions, respectively. The adsorption capacity for MB of the copolymer-modified samples follows the order CNF127 > CNP123 > CNF108, which corroborated with the mesoporosity as well as nitrogen content of the corresponding samples. The maximum % adsorption of Pb(II) follows the order CNF127 (99.82%) > CNF108 (98.74%) > CNP123 (91.82%), and this trend is attributed to the BET surface area of the corresponding samples. This study demonstrates multicomponent removal of water pollutants, both organic dyes and inorganic toxic metal ions.

SUBMITTER: Kundu S

PROVIDER: S-EPMC6644633 | biostudies-literature | 2018 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nitrogen-Doped Nanoporous Carbon Nanospheroids for Selective Dye Adsorption and Pb(II) Ion Removal from Waste Water.

Kundu Sukanya S Chowdhury Ipsita Hazra IH Naskar Milan Kanti MK

ACS omega 20180824 8

In the presence of melamine and block copolymers, namely, F108, F127, and P123, nitrogen-doped nanoporous carbon nanospheroids (N@CNSs) were synthesized by the hydrothermal process. The F127-modified sample (CNF127) exhibits the maximum Brunauer-Emmett-Teller (BET) surface area of 773.4 m<sup>2</sup>/g with a pore volume of 0.877 cm<sup>3</sup>/g. The microstructural study reveals that nanospheroids of size 50-200 nm were aggregated together to form a chainlike structure for all triblock copolym ...[more]

PMID: 31459117

Similar Datasets

Project description:The current research mainly focuses on transforming low-quality waste into value-added nanomaterials and investigating various ways of utilising them. The hydrothermal preparation of highly fluorescent N-doped carbon dots (N-CDs) was obtained from the carboxymethylcellulose (CMC) of oil palm empty fruit bunches and linear-structured polyethyleneimines (LPEI). Transmission electron microscopy (TEM) analysis showed that the obtained N-CDs had an average size of 3.4 nm. The N-CDs were monodispersed in aqueous solution and were strongly fluorescent under the irradiation of ultra-violet light. A detailed description of the morphology and shape was established using Fourier transform infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS). It was shown that LPEI were successfully tuned the fluorescence (PL) properties of CDs in both the intrinsic and surface electronic structures, and enhanced the quantum yield (QY) up to 44%. The obtained N-CDs exhibited remarkable PL stability, long lifetime and pH-dependence behaviour, with the excitation/emission maxima of 350/465.5 nm. Impressively, PL enhancement and blue-shifted emission could be seen with the dilution of the original N-CDs solution. The obtained N-CDs were further applied as fluorescent probe for the identification of Cu2+ in aqueous media. The mechanism could be attributed to the particularly high thermodynamic affinity of Cu2+ for the N-chelate groups over the surface of N-CDs and the fast metal-to-ligand binding kinetics. The linear relationship between the relative quenching rate and the concentration of Cu2+ were applied between 1-30 µM, with a detection limit of 0.93 µM. The fluorescent probe was successfully applied for the detection of Cu2+ in real water. Moreover, a solid-state film of N-CDs was prepared in the presence of poly (vinyl alcohol) (PVA) polymer and found to be stable even after 72-h of continuous irradiation to UV-lamp. In contrast to the aqueous N-CDs, the composite film showed only an excitation independent property, with enhanced PL QY of around 47%. Due to the strong and stable emission nature of N-CDs in both aqueous and solid conditions, the obtained N-CDs are ideal for reducing the overall preparation costs and applying them for various biological and environmental applications in the future.

Dataset Information

Nitrogen-Doped Nanoporous Carbon Nanospheroids for Selective Dye Adsorption and Pb(II) Ion Removal from Waste Water.

Publications

Nitrogen-Doped Nanoporous Carbon Nanospheroids for Selective Dye Adsorption and Pb(II) Ion Removal from Waste Water.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets