Development of TiO2-SiO2 Photocatalysts Having a Microhoneycomb Structure by the Ice Templating Method.

ABSTRACT: Immobilization of TiO2-based photocatalysts usually suffers from lowered surface area and mass transfer limitation compared with their suspended counterpart. In this work, TiO2-SiO2 monolithic photocatalysts having straight macropores, called microhoneycombs, were synthesized. The obtained samples had straight macropores with a diameter in the range of 15-40 ?m formed by walls having a thickness up to 5 ?m. The samples also contain micropores and small mesopores inside their walls, which contribute to high surface areas of more than 500 m2 g-1. Synthesized photocatalysts were tested in a continuous flow system using the decolorization of methylene blue as a model reaction. It was found that the unique morphology of the samples can be used to promote the uniform distribution of the target fluid while reducing the pressure drop across the photocatalyst to less than a hundredth compared with a packed bed system. In addition, calcination at 600-800 °C improved the strength and photocatalytic activity of the monoliths while preserving the high surface area of the samples.

SUBMITTER: Urkasame K

PROVIDER: S-EPMC6644808 | biostudies-literature | 2018 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Development of TiO2-SiO2 Photocatalysts Having a Microhoneycomb Structure by the Ice Templating Method.

Urkasame Kasama K Yoshida Seiichiro S Takanohashi Taihei T Iwamura Shinichiroh S Ogino Isao I Mukai Shin R SR

ACS omega 20181029 10

Immobilization of TiO2-based photocatalysts usually suffers from lowered surface area and mass transfer limitation compared with their suspended counterpart. In this work, TiO2-SiO2 monolithic photocatalysts having straight macropores, called microhoneycombs, were synthesized. The obtained samples had straight macropores with a diameter in the range of 15-40 μm formed by walls having a thickness up to 5 μm. The samples also contain micropores and small mesopores ...[more]

PMID: 31458118

Similar Datasets

Project description:SiO2@TiO2 core-shell nanoparticles were successfully synthesized via a simple, reproducible, and low-cost method and tested for methylene blue adsorption and UV photodegradation, with a view to their application in wastewater treatment. The monodisperse SiO2 core was obtained by the classical Stöber method and then coated with a thin layer of TiO2, followed by calcination or hydrothermal treatments. The properties of SiO2@TiO2 core-shell NPs resulted from the synergy between the photocatalytic properties of TiO2 and the adsorptive properties of SiO2. The synthesized NPs were characterized using FT-IR spectroscopy, HR-TEM, FE-SEM, and EDS. Zeta potential, specific surface area, and porosity were also determined. The results show that the synthesized SiO2@TiO2 NPs that are hydrothermally treated have similar behaviors and properties regardless of the hydrothermal treatment type and synthesis scale and better performance compared to the SiO2@TiO2 calcined and TiO2 reference samples. The generation of reactive species was determined by EPR, and the photocatalytic activity was evaluated by the methylene blue (MB) removal in aqueous solution under UV light. Hydrothermally treated SiO2@TiO2 showed the highest adsorption capacity and photocatalytic removal of almost 100% of MB after 15 min in UV light, 55 and 89% higher compared to SiO2 and TiO2 reference samples, respectively, while the SiO2@TiO2 calcined sample showed 80%. It was also observed that the SiO2-containing samples showed a considerable adsorption capacity compared to the TiO2 reference sample, which improved the MB removal. These results demonstrate the efficient synergy effect between SiO2 and TiO2, which enhances both the adsorption and photocatalytic properties of the nanomaterial. A possible photocatalytic mechanism was also proposed. Also noteworthy is that the performance of the upscaled HT1 sample was similar to one of the lab-scale synthesized samples, demonstrating the potentiality of this synthesis methodology in producing candidate nanomaterials for the removal of contaminants from wastewater.

Project description:In this article, the TiO2/SiO2-np nanocomposite multilayer films were synthesized in a single step by reactive magnetron sputtering combined with a nanoparticle aerosol jet. The SiO2 nanoparticles (SiO2-np) were introduced into a growing TiO2 thin film with different time sequences during deposition for a fixed duration. The SiO2-np acting as impurities are introduced into the TiO2 to willingly disturb its growth and to cause growth defects in order to increase the specific surface area of the photocatalytic film. In reason of the non-photoactive properties of the SiO2 nanoparticles, their introduction allows us to study only the effects induced on the film morphology, microstructure, and photocatalytic properties by their incorporation. The fractographies and topographies reveal strong changes in the morphologies depending on the time sequence of the nanoparticle introduction in the thin films. The introduction of SiO2-np from the beginning of the TiO2 film growth leads to the formation of high and large growth defects resulting in a highly diffusive surface. In addition, XRD analysis shows that the crystallite size tends to decrease as the composite film layer gets closer to the surface. Their photocatalytic performance is obtained by following the degradation of orange G dye under UV-visible irradiation. The photocatalytic performance is not only related to the specific surface area of the catalyst film, and the coverage of the photoactive phase on the surface, but also to the crystal quality of the photoactive phase. Furthermore, the samples exhibit good photostability, maintaining the same activity after four degradation cycles. In the specific case of TiO2/SiO2-np, it is demonstrated that the introduction of the nanoparticles only at the beginning of the film growth is more efficient than a continuous introduction. This result suggests that this original process allows the use of a relevant strategy for the nanoparticle introduction according to the required functionality.

Project description:The preparation of visible-light-driven photocatalysts has become highly appealing for environmental remediation through simple, fast and green chemical methods. The current study reports the synthesis and characterization of graphitic carbon nitride/titanium dioxide (g-C3N4/TiO2) heterostructures through a fast (1 h) and simple microwave-assisted approach. Different g-C3N4 amounts mixed with TiO2 (15, 30 and 45 wt. %) were investigated for the photocatalytic degradation of a recalcitrant azo dye (methyl orange (MO)) under solar simulating light. X-ray diffraction (XRD) revealed the anatase TiO2 phase for the pure material and all heterostructures produced. Scanning electron microscopy (SEM) showed that by increasing the amount of g-C3N4 in the synthesis, large TiO2 aggregates composed of irregularly shaped particles were disintegrated and resulted in smaller ones, composing a film that covered the g-C3N4 nanosheets. Scanning transmission electron microscopy (STEM) analyses confirmed the existence of an effective interface between a g-C3N4 nanosheet and a TiO2 nanocrystal. X-ray photoelectron spectroscopy (XPS) evidenced no chemical alterations to both g-C3N4 and TiO2 at the heterostructure. The visible-light absorption shift was indicated by the red shift in the absorption onset through the ultraviolet-visible (UV-VIS) absorption spectra. The 30 wt. % of g-C3N4/TiO2 heterostructure showed the best photocatalytic performance, with a MO dye degradation of 85% in 4 h, corresponding to an enhanced efficiency of almost 2 and 10 times greater than that of pure TiO2 and g-C3N4 nanosheets, respectively. Superoxide radical species were found to be the most active radical species in the MO photodegradation process. The creation of a type-II heterostructure is highly suggested due to the negligible participation of hydroxyl radical species in the photodegradation process. The superior photocatalytic activity was attributed to the synergy of g-C3N4 and TiO2 materials.

Dataset Information

Development of TiO2-SiO2 Photocatalysts Having a Microhoneycomb Structure by the Ice Templating Method.

Publications

Development of TiO<sub>2</sub>-SiO<sub>2</sub> Photocatalysts Having a Microhoneycomb Structure by the Ice Templating Method.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets