Esterification over Acid-Treated Mesoporous Carbon Derived from Petroleum Coke.

ABSTRACT: Multistep activation of a Canadian oilsands petroleum coke that yields an acidified mesoporous carbon catalyst is reported. Microporous-activated carbon (APC; ?2000 m2/g), obtained by thermochemical activation of petroleum coke using KOH, was impregnated with ammonium heptamolybdate and activated by carbothermal hydrogen reduction (CHR). The resulting Mo2C, supported on high-mesopore volume (V meso ?0.4 cm3/g) carbon, yields the desired mesoporous carbon catalyst (V meso ?0.7 cm3/g) following acid washing. The effect of CHR temperature and the benefit of Mo2C loading on mesopore development is reported, and pore development models are discussed. The mesoporous carbons are active for the esterification of acetic acid and 1-butanol at 77 °C, and the butanol conversion correlates with the catalyst acidity, as measured by NH3-TPD.

SUBMITTER: Liu S

PROVIDER: S-EPMC6647988 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Esterification over Acid-Treated Mesoporous Carbon Derived from Petroleum Coke.

Liu Shida S Wang Haiyan H Neumann Patrick P Kim Chang Soo CS Smith Kevin J KJ

ACS omega 20190329 3

Multistep activation of a Canadian oilsands petroleum coke that yields an acidified mesoporous carbon catalyst is reported. Microporous-activated carbon (APC; ∼2000 m2/g), obtained by thermochemical activation of petroleum coke using KOH, was impregnated with ammonium heptamolybdate and activated by carbothermal hydrogen reduction (CHR). The resulting Mo2C, supported on high-mesopore volume (V meso ∼0.4 cm3/g) carbon, yields the desired mesoporo ...[more]

PMID: 31459753

Similar Datasets

High-Purity Graphitic Carbon for Energy Storage: Sustainable Electrochemical Conversion from Petroleum Coke.

Project description:The petroleum coke (PC) has been widely used as raw materials for the preparation of electrodes in aluminium electrolysis and lithium-ion batteries (LIB), during which massive CO2 gases are produced. To meet global CO2 reduction, an environmentally friendly route for utilizing PC is highly required. Here, a simple, scalable, catalyst-free process that can directly convert high-sulfur PC into graphitic nanomaterials under cathodic polarization in molten CaCl2 -LiCl at mild temperatures is proposed. The energy consumption of the proposed process is calculated to be 3 627.08 kWh t-1 , half that of the traditional graphitization process (≈7,825.21 kWh t-1 graphite). When applied as a negative electrode for LIBs, the as-converted graphite materials deliver a competitive specific capacity of ≈360 mAh g-1 (0.2 C) compared with commercial graphite. This approach has great potential to scale up for sustainably converting low-value PC into high-quality graphite for energy storage.

| S-EPMC10015905 | biostudies-literature

Sulfated Well-Defined Mesoporous Nanostructured Zirconia for Levulinic Acid Esterification

Project description:Well-organized zirconia

| S-EPMC9386699 | biostudies-literature

Preparation of Carbon-Based Solid Acid Catalyst from High-Sulfur Petroleum Coke with Nitric Acid and Ball Milling, and a Computational Evaluation of Inherent Sulfur Conversion Pathways.

Project description:A series of petroleum coke (petcoke)-derived solid acid catalysts were prepared via nitric acid treatment with or without ball milling pretreatment. The inherent sulfur in petcoke was converted to sulfonic groups, which were active sites for the esterification of octanoic acid and methanol at 60 °C, with ester yields of 14-43%. More specifically, samples without ball milling treated at 120 °C for 3 h had a total acidity of 4.67 mmol/g, which was 1.6 times that of the samples treated at 80 °C, despite their -SO3H acidities being similar (~0.08 mmol/g). The samples treated for 24 h had higher -SO3H (0.10 mmol/g) and total acidity (5.25 mmol/g) but not increased catalytic activity. Ball milling increased the defects and exposed aromatic hydrogen groups on petcoke, which facilitated further acid oxidation (0.12 mmol -SO3H/g for both materials and total acidity of 5.18 mmol/g and 5.01 mmol/g for BP-N-3/120 and BP-N-8/90, respectively) and an increased ester yield. DFT calculations were used to analyze the pathways of sulfonic acid group formation, and the reaction pathway with NO2• was the most thermodynamically and kinetically favourable. The activities of the prepared catalysts were related to the number of -SO3H acid sites, the total acidity, and the oxygen content, with the latter two factors having a negative impact.

| S-EPMC10609519 | biostudies-literature

Polyaspartic Acid-Derived Micro-/Mesoporous Carbon for Ultrahigh H2 and CH4 Adsorption.

Project description:A poly(amino acid)-based approach for scalable synthesis of micro-/mesoporous carbon (PC) with high specific surface area and narrow distribution of micro- and mesopores is presented. Using cross-linked poly aspartic acid as a precursor, PC was obtained by in situ one-step carbonization without the activating agent. The resulting PC had an ultrahigh adsorption capacity for H2 (4.43 wt %) and CH4 (4.49 mmol g-1). This novel method could significantly decrease the wastewater hazards caused by washout of the considerable amount of the activating agent. The PC showed promising application in gas adsorption and storage.

| S-EPMC7240811 | biostudies-literature

Petroleum coke exposure leads to altered secretome profiles in human lung models.

Project description:Petroleum coke (PC) is a coal-like product that is produced during the refinement of crude oil and bituminous sand. Fugitive dust from open storage of PC in urban areas is a potential human health concern. Animal inhalation studies suggest that PC leads to an adverse pulmonary histopathology, including areas of fibrosis and chronic inflammation; however, little is known about its impact on human health. In order to identify biomarkers and cellular pathways that are associated with exposure, we performed two-dimensional liquid chromatography-mass spectrometric analyses on secreted proteins from two human lung culture models. A total of 2795 proteins were identified and relatively quantified from an immortalized cell line and 2406 proteins from primary cultures that were either mock treated or exposed to particulate matter with a diameter of 2.5-10 ?m PC or filtered urban air particulates for 16 h. Pathway analysis on secretomes from primary lung cultures indicated that PC exposure suppressed the secretion of proteins involved in the organization of the extracellular matrix and epithelial differentiation. Because these cellular processes could facilitate fibrosis, we performed chronic 12-day exposure studies on three-dimensional human lung cultures consisting of epithelia and stromal fibroblasts. Relative to mock-treated cells, matrix metallopeptidase 9 levels in the conditioned media were lower by 4 days postexposure and remained suppressed for the duration of the experiment. Immunocytochemical staining of collagen III, a marker associated with fibrosis, showed increased accumulation in the epithelial layer and at the air-liquid interface.

| S-EPMC6853184 | biostudies-literature

Thermogravimetric Determination of the Kinetics of Petroleum Needle Coke Formation by Decantoil Thermolysis.

Project description:This work presents the results of thermogravimetric analysis of decantoil. The microstructure of the extracted petroleum coke during the thermolysis of decantoil in an inert nitrogen atmosphere at 1000 °C was studied by scanning electron microscopy and interpreted as acicular. The model free kinetic approach based on Friedman's isoconversion method was used to calculate the kinetic characteristics of decantoil thermolysis-activation energy and pre-exponential factor. The individual hydrocarbon composition of decantoil was determined by gas chromatography mass spectrometry, which was used to determine the activation energy of evaporation of its fractions. The total energy spent on the chemical reactions of cracking and thermopolycondensation was determined when the degree of decantoil conversion was changed from 0.1 to 0.9.

| S-EPMC7676338 | biostudies-literature

Mesoporous Carbon Microfibers for Electroactive Materials Derived from Lignocellulose Nanofibrils.

Project description:The growing adoption of biobased materials for electronic, energy conversion, and storage devices has relied on high-grade or refined cellulosic compositions. Herein, lignocellulose nanofibrils (LCNF), obtained from simple mechanical fibrillation of wood, are proposed as a source of continuous carbon microfibers obtained by wet spinning followed by single-step carbonization at 900 °C. The high lignin content of LCNF (∼28% based on dry mass), similar to that of the original wood, allowed the synthesis of carbon microfibers with a high carbon yield (29%) and electrical conductivity (66 S cm-1). The incorporation of anionic cellulose nanofibrils (TOCNF) enhanced the spinnability and the porous morphology of the carbon microfibers, making them suitable platforms for electrochemical double layer capacitance (EDLC). The increased loading of LCNF in the spinning dope resulted in carbon microfibers of enhanced carbon yield and conductivity. Meanwhile, TOCNF influenced the pore evolution and specific surface area after carbonization, which significantly improved the electrochemical double layer capacitance. When the carbon microfibers were directly applied as fiber-shaped supercapacitors (25 F cm-3), they displayed a remarkably long-term electrochemical stability (>93% of the initial capacitance after 10 000 cycles). Solid-state symmetric fiber supercapacitors were assembled using a PVA/H2SO4 gel electrolyte and resulted in an energy and power density of 0.25 mW h cm-3 and 65.1 mW cm-3, respectively. Overall, the results indicate a green and facile route to convert wood into carbon microfibers suitable for integration in wearables and energy storage devices and for potential applications in the field of bioelectronics.

| S-EPMC7706107 | biostudies-literature

Efficient Removal of Bisphenol A Using Nitrogen-Doped Graphene-Like Plates from Green Petroleum Coke.

Project description:Green petroleum coke, a form of industrial waste produced in the oil-refining process, was used to synthesize nitrogen-doped graphene-like plates (N-GLPs) together with melamine. In this study, characterization and batch experiments were performed to elucidate the interaction mechanism of N-GLPs and bisphenol A (BPA). Structural analysis of N-GLPs, including scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), Brunauer-Emmett-Teller (BET), and X-ray photoelectron spectroscopy (XPS), showed an obvious graphene-like structure and successful nitrogen doping. In addition, compared with 8.0 m2/g for green petroleum coke, the BET surface area of N-GLPs markedly increased to 96.6 m2/g. The influences of various factors, including contact time, temperature, and initial pH on BPA removal efficiency were investigated. It was found that 92.0% of BPA was successfully removed by N-GLPs at 50 °C. Based on the adsorption experiments, it was shown that electrostatic attraction, hydrogen bonding, and ?-? interaction enhanced the adsorption capacity of N-GLPs for BPA. According to the thermodynamic data, the adsorption process was spontaneous, physical, and endothermic in nature. Therefore, N-GLPs are efficient adsorbent material to remove BPA from wastewater.

| S-EPMC7435634 | biostudies-literature

Conversion of Furfuryl Alcohol into Ethyl Levulinate over Glucose-Derived Carbon-Based Solid Acid in Ethanol.

Project description:In this study, a carbon-based solid acid was created through the sulfonation of carbon obtained from the hydrothermal pretreatment of glucose. Additionally, ethyl levulinate, a viable liquid biofuel, was produced from furfuryl alcohol using the environmentally benign and low-cost catalyst in ethanol. Studies for optimizing the reaction conditions, such as reaction time, temperature, and catalyst loading, were performed. Under the optimal conditions, a maximum ethyl levulinate yield of 67.1% was obtained. The recovered catalyst activity (Ethyl levulinate yield 57.3%) remained high after being used four times, and it was easily regenerated with a simple sulfonation process. Moreover, the catalyst was characterized using FT-IR, XRD, SEM, elemental analysis, and acid-base titration techniques.

| S-EPMC6572322 | biostudies-literature

Esterification of Glycerol With Oleic Acid Over Hydrophobic Zirconia-Silica Acid Catalyst and Commercial Acid Catalyst: Optimization and Influence of Catalyst Acidity.

Project description:Catalytic esterification of glycerol with oleic acid (OA) was optimized over hydrophobic mesoporous zirconia-silica heterogeneous acid catalyst (ZrO2-SiO2-Me&Et-PhSO3H) and benchmarked with commercial catalysts (Aquivion and Amberlyst 15) in order to examine the effect of catalyst acidity on conversion, yield and product selectivity. The process optimisation results showed an 80% conversion with a 59.4% glycerol mono-oleate (GMO) and 34.6% glycerol dioleate (GDO) selectivities corresponding to a combined GMO and GDO selectivity of 94.8% at equimolar OA-to-glycerol ratio, 160°C reaction temperature, 5 wt% catalyst concentration with respect to the OA weight and 4 h reaction time. This work reveals that the hydrophobic and mild acidic ZrO2-SiO2-Me&Et-PhSO3H catalyst outperformed Amberlyst 15 and Aquivion with a yield of 82% and GMO selectivity of 60%. It is found that catalyst acidity is a key parameter for catalytic activity and conversion rate. Nevertheless, high acidity/acid strength reduced the product yield in the glycerol esterification of OA.

| S-EPMC6477701 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data