Hierarchically Porous Silica Prepared with Anionic Polyelectrolyte-Nonionic Surfactant Mesomorphous Complex as Dynamic Template.
Ontology highlight
ABSTRACT:
SUBMITTER: Shi C
PROVIDER: S-EPMC6648986 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:In this work, we developed a novel strategy to synthesize porous (alumino)silicate materials using a single structure-directing agent composed of an imidazole unit with a hydrophobic tail, namely, 1,2-dimethyl-3-hexadecyl-1H-imidazol-3-ium bromide (C16dMImz). A wide range of products such as ordered mesoporous silicas, layered silica-alumina, and hierarchically porous mordenite zeolite were obtained by varying synthesis parameters such as temperature and aluminum concentration. By changing crystallization temperature, we could control the degree of silica condensation and tune the textural and morphological properties of the final materials. By varying the aluminum concentration in the gel, we can obtain mesoporous amorphous silica-alumina or crystalline mordenite zeolite with, respectively, weak and strong Brønsted acid sites. Obtained acidic silica-alumina materials displayed promising performance in catalytic reactions of linear paraffin hydroisomerization and Friedel-Crafts alkylation of benzene with benzyl alcohol.
| S-EPMC6823632 | biostudies-literature
Project description:Structural hierarchy, porosity, and isotropy/anisotropy are highly relevant factors for mechanical properties and thereby the functionality of porous materials. However, even though anisotropic and hierarchically organized, porous materials are well known in nature, such as bone or wood, producing the synthetic counterparts in the laboratory is difficult. We report for the first time a straightforward combination of sol-gel processing and shear-induced alignment to create hierarchical silica monoliths exhibiting anisotropy on the levels of both, meso- and macropores. The resulting material consists of an anisotropic macroporous network of struts comprising 2D hexagonally organized cylindrical mesopores. While the anisotropy of the mesopores is an inherent feature of the pores formed by liquid crystal templating, the anisotropy of the macropores is induced by shearing of the network. Scanning electron microscopy and small-angle X-ray scattering show that the majority of network forming struts is oriented towards the shearing direction; a quantitative analysis of scattering data confirms that roughly 40% of the strut volume exhibits a preferred orientation. The anisotropy of the material's macroporosity is also reflected in its mechanical properties; i.e., the Young's modulus differs by nearly a factor of 2 between the directions of shear application and perpendicular to it. Unexpectedly, the adsorption-induced strain of the material exhibits little to no anisotropy.
| S-EPMC5627989 | biostudies-literature
Project description:Recently, amine-functionalized materials as a prospective chemical sorbent for post combustion CO₂ capture have gained great interest. However, the amine grafting for the traditional MCM-41, SBA-15, pore-expanded MCM-41 or SBA-15 supports can cause the pore volume and specific surface area of sorbents to decrease, significantly affecting the CO₂ adsorption-desorption dynamics. To overcome this issue, hierarchical porous silica with interparticle macropores and long-range ordering mesopores was prepared and impregnated with pentaethylenehexamine. The pore structure and amino functional group content of the modified silicas were analyzed by scanning electron microscope, transmission electron microscope, N₂ adsorption, X-ray powder diffraction, and Fourier transform infrared spectra. Moreover, the effects of the pore structure as well as the amount of PEHA loading of the samples on the CO₂ adsorption capacity were investigated in a fixed-bed adsorption system. The CO₂ adsorption capacity reached 4.5 mmol CO₂/(g of adsorbent) for HPS-PEHA-70 at 75 °C. Further, the adsorption capacity for HPS-PEHA-70 was steady after a total of 15 adsorption-desorption cycles.
| S-EPMC5456643 | biostudies-other
Project description:Fabrication of hierarchically porous carbon materials (HPCs) with high surface area and pore volume has always been pursued. However, the currently effective template methods and acid/base activation strategies suffer from the drawbacks of either high costs or tedious steps. Herein, HPCs with 3D macro-mesopores and short-range meso-micropores were fabricated via an easy and sustainable two-step method from biomass. Macro-mesopores were constructed by slightly accumulation/aggregation of carbon spheres ranging from 60?nm to 80?nm, providing efficient mass diffusion pathways. Short-range mesopores and micropores with high electrolyte accessibility were developed in these spheres by air activation. The obtained HPCs showed surface area values up to 1306?m(2)/g and high mesopore volume proportion (63.9%). They demonstrated excellent capacitance and low equivalent series resistance (ESR) as supercapacitor electrode materials, suggesting the efficient diffusion and adsorption of electrolyte ions in the designed hierarchically porous structure.
| S-EPMC4162313 | biostudies-literature
Project description:The adsorption of nonionic surfactants onto hydrophilic nanoparticles (NPs) is anticipated to increase their stability in aqueous medium. While nonionic surfactants show salinity- and temperature-dependent bulk phase behavior in water, the effects of these two solvent parameters on surfactant adsorption and self-assembly onto NPs are poorly understood. In this study, we combine adsorption isotherms, dispersion transmittance, and small-angle neutron scattering (SANS) to investigate the effects of salinity and temperature on the adsorption of pentaethylene glycol monododecyl ether (C12E5) surfactant on silica NPs. We find an increase in the amount of surfactant adsorbed onto the NPs with increasing temperature and salinity. Based on SANS measurements and corresponding analysis using computational reverse-engineering analysis of scattering experiments (CREASE), we show that the increase in salinity and temperature results in the aggregation of silica NPs. We further demonstrate the non-monotonic changes in viscosity for the C12E5-silica NP mixture with increasing temperature and salinity and correlate the observations to the aggregated state of NPs. The study provides a fundamental understanding of the configuration and phase transition of the surfactant-coated NPs and presents a strategy to manipulate the viscosity of such dispersion using temperature as a stimulus.
| S-EPMC10134496 | biostudies-literature
Project description:In this study, we present a detailed comparison between a conventional supercritical drying process and an evaporative drying technique for hierarchically organized porous silica gel monoliths. These gels are based on a model system synthesized by the aqueous sol-gel processing of an ethylene-glycol-modified silane, resulting in a cellular, macroporous, strut-based network comprising anisotropic, periodically arranged mesopores formed by microporous amorphous silica. The effect of the two drying procedures on the pore properties (specific surface area, pore volume, and pore widths) and on the shrinkage of the monolith is evaluated through a comprehensive characterization by using nitrogen physisorption, electron microscopy, and small-angle X-ray scattering. It can clearly be demonstrated that for the hierarchically organized porous solids, the evaporative drying procedure can compete without the need for surface modification with the commonly applied supercritical drying in terms of the material and textural properties, such as specific surface area and pore volume. The thus obtained materials deliver a high specific surface area and exhibit overall comparable or even improved pore characteristics to monoliths prepared by supercritical drying. Additionally, the pore properties can be tailored to some extent by adjusting the drying conditions, such as temperature.
| S-EPMC9858606 | biostudies-literature
Project description:As one of the most important prototypical chromium-based MOFs, MIL-101(Cr) is well-studied and widely employed in various scientific fields. However, due to its small capture window sizes and curved internal apertures, its application in large molecular removal is quite limited, and given its high stability and high synthetic temperature (>200 °C), it is difficult to achieve hierarchically porous MIL-101(Cr). In our study, hierarchically porous MIL-101(Cr) involving a high macro-/meso-/micropores ratio was designed and synthesized using acetic acid as an additive and silicon dioxide (SiO2) nanoparticles as a template. The optimal hierarchically porous MIL-101(Cr) (A-4) possessed a high specific surface area (2693 m2 g-1) and an abundant macro-/mesoporous structure with the addition of SiO2 of 200 mg. Compared with the control sample (A-0) with a less macro-/mesoporous structure, A-4 showed good adsorption properties for both coomassie brilliant blue R-250 (CBB, 82.1 mg g-1) and methylene blue (MB, 34.3 mg g-1) dyes, which were 1.36 times and 9.37 times higher than those of A-0. Moreover, A-4 also had good recyclability, and the removal rate of CBB was still higher than 85% after five cycles of adsorption.
| S-EPMC9416310 | biostudies-literature
Project description:In this work, poly (vinylidene fluoride) (PVDF) hierarchically porous membranes (HPMs) with isolated large pores and continuous narrow nano-pores have been fabricated from its blend with poly (methyl methacrylate) (PMMA) based on the combination of crystallization template with chemical or supercritical CO2 foaming. On the one hand, the decomposition of azodicarbonamide (ADC, chemical foaming agent) or the release of CO2 can produce isolated large pores. On the other hand, PMMA is expelled during the isothermal crystallization of PVDF in their miscible blend, yielding narrow nano-pores upon etching with a selective solvent. In the case of supercritical CO2, the attained PVDF HPMs fail to improve separation performance because of the compact wall of isolated-large-pore and consequent poor connectivity of hierarchical pores. In the case of ADC, the optimal HPM exhibits much higher flux (up to 20 times) without any loss of selectivity compared with the reference only with nano-pores. The enhanced permeability can be attributed to the shorter diffusion length and lower diffusion barrier from isolated large pores, while the comparable selectivity is determined by narrow nano-pores in THE matrix.
| S-EPMC9736639 | biostudies-literature
Project description:Hierarchically porous ZSM-5 was prepared by utilizing a two-step crystallization procedure with carbon-silica composites as precursors. The hierarchically porous zeolites obtained a regular mesoporous structure with aluminum incorporated into the carbon-silica composite frameworks. The carbon-silica composite zeolites were characterized by XRD, TEM, SEM, and nitrogen adsorption/desorption. As-prepared hierarchical zeolites were used in the 1,3,5-triisopropylbenzene (TIPB) cracking reaction and exhibited significantly high TIPB conversion, while the accessibility factors were also determined.
| S-EPMC7178382 | biostudies-literature
Project description:Mechanically stable structures with interconnected hierarchical porosity combine the benefits of both small and large pores, such as high surface area, pore volume, and good mass transport capabilities. Hence, lightweight micro-/meso-/macroporous monoliths are prepared from ordered mesoporous silica COK-12 by means of spark plasma sintering (SPS, S-sintering) and compared to conventionally (C-) sintered monoliths. A multi-scale model is developed to fit the small angle X-ray scattering data and obtain information on the hexagonal lattice parameters, pore sizes from the macro to the micro range, as well as the dimensions of the silica population. For both sintering techniques, the overall mesoporosity, hexagonal pore ordering, and amorphous character are preserved. The monoliths' porosity (77-49%), mesopore size (6.2-5.2 nm), pore volume (0.50-0.22 g cm-3), and specific surface area (451-180 m2 g-1) decrease with increasing processing temperature and pressure. While the difference in porosity is enhanced, the structural parameters between the C-and S-sintered monoliths are largely converging at 900 °C, except for the mesopore size and lattice parameter, whose dimensions are more extensively preserved in the S-sintered monoliths, however, coming along with larger deviations from the theoretical lattice. Their higher mechanical properties (biaxial strength up to 49 MPa, 724 MPa HV 9.807 N) at comparable porosities and ability to withstand ultrasonic treatment and dead-end filtration up to 7 bar allow S-sintered monoliths to reach a high permeance (2634 L m-2 h-1 bar-1), permeability (1.25 × 10-14 m2), and ability to reduce the chemical oxygen demand by 90% during filtration of a surfactant-stabilized oil in water emulsion, while indicating reasonable resistance towards fouling.
| S-EPMC9470055 | biostudies-literature