The Effect of Material Fresh Properties and Process Parameters on Buildability and Interlayer Adhesion of 3D Printed Concrete.

ABSTRACT: The advent of digital concrete fabrication calls for advancing our understanding of the interaction of 3D printing with material rheology and print parameters, in addition to developing new measurement and control techniques. Thixotropy is the main challenge associated with printable material, which offers high yield strength and low viscosity. The higher the thixotropy, the better the shape stability and the higher buildability. However, exceeding a minimum value of thixotropy can cause high extrusion pressure and poor interface bond strength if the printing parameters are not optimized to the part design. This paper aims to investigate the effects of both material and process parameters on the buildability and inter-layer adhesion properties of 3D printed cementitious materials, produced with different thixotropy and print head standoff distances. Nano particles are used to increase the thixotropy and, in this context, a lower standoff distance is found to be useful for improving the bond strength. The low viscosity "control" sample is unaffected by the variation in standoff distances, which is attributed to its flowability and low yield stress characteristics that lead to strong interfacial bonding. This is supported by our microscopic observations.

SUBMITTER: Panda B

PROVIDER: S-EPMC6651485 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Effect of Material Fresh Properties and Process Parameters on Buildability and Interlayer Adhesion of 3D Printed Concrete.

Panda Biranchi B Noor Mohamed Nisar Ahamed NA Paul Suvash Chandra SC Bhagath Singh Gvp G Tan Ming Jen MJ Šavija Branko B

Materials (Basel, Switzerland) 20190704 13

The advent of digital concrete fabrication calls for advancing our understanding of the interaction of 3D printing with material rheology and print parameters, in addition to developing new measurement and control techniques. Thixotropy is the main challenge associated with printable material, which offers high yield strength and low viscosity. The higher the thixotropy, the better the shape stability and the higher buildability. However, exceeding a minimum value of thixotropy can cause high ex ...[more]

PMID: 31277393

Similar Datasets

Project description:BackgroundScaffolds are of great importance in tissue engineering applications as they provide a mechanically supportive environment for cellular activity, which is particularly necessary for hard tissues such as bone. Notably, the mechanical properties of a scaffold vary with differing design parameters such as those related to scaffold height and internal structure. Thus, the present study aimed to explore the relationship between design parameters and mechanical properties of composite polycaprolactone (PCL) and nano-hydroxyapatite (nHAp) scaffolds fabricated by three-dimensional (3D) printing.MethodsWe designed and printed scaffolds with different internal structures (lattice and staggered) and varying heights (4, 6, 8 and 10 layers), and consistent porosity (50%) for the purpose of comparison. Then, we examined the scaffold microstructure (pore size and penetration between layers) using scanning electron microscopy (SEM) and mechanical properties (elastic modulus and yield strength) using compressive testing.ResultsOur results illustrated that the microstructural parameters were related to scaffold design. At higher heights, pore size increased while penetration between layers decreased; thus, mechanical properties were affected. Results of mechanical testing demonstrated that for lattice scaffolds, elastic modulus was similar for 6 vs 4, and 8 vs 4 layers but ~33% lower for 10 layers vs 4 layers. Similarly, yield strength was comparable for 6 vs 4, and 8 vs 4 layers but ~27% lower for 10 layers vs 4 layers. With staggered scaffolds, when compared to 4-layer results, elastic modulus was similar for 6 layers but was ~43% lower for 8 layers and ~38% lower for 10 layers. Staggered scaffolds had ~38%, ~51%, and ~76% lower yield strength when the number of layers were increased from 4 to 6, 8, and 10 layers, respectively. When comparing lattice and staggered scaffolds with the same layer number, elastic modulus was similar, apart from 8-layer scaffolds where the staggered design was ~42% lower than lattice. Yield strength was similar between 4-layer staggered and lattice scaffolds, while staggered scaffolds with 6, 8, and 10 number of layers showed ~43%, ~45%, ~68% lower strength, respectively, than those found in lattice scaffolds with the same layer numbers.ConclusionsMechanical properties of 3D printed scaffolds depended on scaffold height for both lattice and staggered internal structures. Staggered scaffolds had lower mechanical properties than the lattice scaffolds with the same height and were more sensitive to the change in scaffold height. Taken together, lattice scaffolds demonstrated the advantages of more stable mechanical properties over staggered scaffolds. Also, scaffolds with lower height were more promising in terms of mechanical properties compared to scaffolds with greater height.

Dataset Information

The Effect of Material Fresh Properties and Process Parameters on Buildability and Interlayer Adhesion of 3D Printed Concrete.

Publications

The Effect of Material Fresh Properties and Process Parameters on Buildability and Interlayer Adhesion of 3D Printed Concrete.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets