Chain Extension and Synergistic Flame-Retardant Effect of Aromatic Schiff Base Diepoxide on Polyamide 6/Aluminum Diethylphosphinate Composites.

ABSTRACT: A way to suppress the deterioration in mechanical properties of polyamide 6 (PA6) is required, especially with high loading of flame retardants in the matrix. In this study, a novel aromatic Schiff base diepoxide (DES) was synthesized. It exhibited an efficient chain extension effect on PA6 and a synergistic flame-retardant effect with aluminum diethylphosphinate (AlPi) for PA6. The PA6 composite with 16 wt.% AlPi only passed UL-94 V-0 rating at 1.6 mm thickness, while the combination of 1.5 wt.% DES with 13 wt.% AlPi induced PA6 to achieve a UL-94 V-0 rating at 0.8 mm thickness. The tensile, flexural, and Izod notched impact strengths were increased by 16.2%, 16.5%, and 24.9%, respectively, compared with those of V-0 flame-retarded PA6 composites with 16 wt.% AlPi. The flame-retarded mechanism of PA6/AlPi/DES was investigated by cone calorimetry and infrared characterization of the char residues and pyrolysis products. These results showed that DES had a synergistic effect with AlPi in condensed-phase flame retardation by promoting the production of aluminum phosphorus oxides and polyphosphates in the char residues.

SUBMITTER: Liang T

PROVIDER: S-EPMC6678687 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Chain Extension and Synergistic Flame-Retardant Effect of Aromatic Schiff Base Diepoxide on Polyamide 6/Aluminum Diethylphosphinate Composites.

Liang Tianxiang T Cai Jianan J Liu Shumei S Lai Hualin H Zhao Jianqing J

Materials (Basel, Switzerland) 20190710 14

A way to suppress the deterioration in mechanical properties of polyamide 6 (PA6) is required, especially with high loading of flame retardants in the matrix. In this study, a novel aromatic Schiff base diepoxide (DES) was synthesized. It exhibited an efficient chain extension effect on PA6 and a synergistic flame-retardant effect with aluminum diethylphosphinate (AlPi) for PA6. The PA6 composite with 16 wt.% AlPi only passed UL-94 V-0 rating at 1.6 mm thickness, while the combination of 1.5 wt. ...[more]

PMID: 31295824

Similar Datasets

Project description:The rapid development of the polymeric materials market has created an urgent demand for the thermoplastic polyamide elastomer (TPAE) owing to its greater functionality, and ability to be synthesized via a facile and industrial route. In this work, a series of novel silicone-containing polyamides (PA1212/Si12) were successfully synthesized from 1,12-dodecarboxylic acid (LA), 1,12-dodecarbondiamine (DMDA), and 1,3-bis (amino-propyl) tetramethyldisiloxane (BATS), via a one-pot melt polycondensation method in the absence of a catalyst. FTIR, 1H-NMR, GPC and inherent viscosity results cohesively prove that the polymerization of monomers was well conducted, and the chemical structure was in high accordance with the design. As expected, the Si12 unit-content of the copolymers regulate the properties of the series. As the feeding ratio of BATS in the diamines increases from 5 mol% to 40 mol%, the thermal transition temperatures, Tg and Tm, decline steadily before finally stabilizing at ~6 °C and 160 °C, respectively, indicating that the co-polyamides possess improved chain flexibility but restricted crystallization ability. The conspicuous evolution in crystalline morphology of the series was observed by XRD and AFM. The increased PA Si12 phase induces the crystallized PA 1212 phase to transit from a thermally-favorable large and rigid crystal structure (α phase) to a kinetically-favorable small and ductile crystal structure (γ phase). Reflected in their stress-strain behavior, PA1212/Si12 copolymers are successfully tailored from rigid plastic to ductile elastomer. The tensile strength mildly drops from above 40 MPa to ~30 MPa while the reversible elongation increases from ~50% to approximately 350%. Accordingly, the moderate surface tension differences in the monomers facilitate the efficient conduction of the co-polymerization process, and the distributed short siloxane unit in the backbone fulfills the copolymer with desirable elasticity. Interestingly, the novel silicone-containing polyamides also display Si12 unit-content dependent flame retardancy, humidity stability, and unconventional solid-state fluorescence properties. The elastomers exhibit a low bibulous rate and anti-fouling characteristics to dye droplets and mud contamination, pass the V-1 rating (UL 94) with a constantly declining PHRR value, and emit blue luminescence under a 365 nm light source. Herein, we propose a new facile strategy for developing a high-performance and multifunctional silicone-modified polyamide, which bears promising industrialization potential. In addition, this first reported silicone-containing thermoplastic polyamide elastomer, which is self-extinguishing, anti-fouling and blue-luminescent, will further broaden the application potential of thermoplastic polyamide elastomers.

Dataset Information

Chain Extension and Synergistic Flame-Retardant Effect of Aromatic Schiff Base Diepoxide on Polyamide 6/Aluminum Diethylphosphinate Composites.

Publications

Chain Extension and Synergistic Flame-Retardant Effect of Aromatic Schiff Base Diepoxide on Polyamide 6/Aluminum Diethylphosphinate Composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets