Desiccant Films Made of Low-Density Polyethylene with Dispersed Silica Gel-Water Vapor Absorption, Permeability (H2O, N2, O2, CO2), and Mechanical Properties.

ABSTRACT: Silica gel is a well-known desiccant. Through dispersion of silica gel in a polymer, films can be made that absorb and desorb water vapor. The water vapor absorption becomes reversible by exposing such films to a water vapor pressure below that of the water vapor pressure during absorption, or by heating the film. The intention of this study was to achieve a better understanding about the water vapor absorption, permeability (H2O, N2, O2, CO2), and mechanical properties of films with dispersed silica gel. Low-density polyethylene (PE-LD) monolayer films with a nominal silica gel concentration of 0.2, 0.4, and 0.6 g dispersed silica gel per 1 g film (PE-LD) were prepared and they absorbed up to 0.08 g water vapor per 1 g of film. The water vapor absorption as a function of time was described by using effective diffusion coefficients. The steady state (effective) water vapor permeation coefficients of the films with dispersed silica gel were a factor of 2 to 14 (8.4 to 60.2·10-12 mg·cm·(cm²·s·Pa)-1, 23 °C) higher than for pure PE-LD films (4.3·10-12 mg·cm·(cm²·s·Pa)-1, 23 °C). On the other hand, the steady state gas permeabilities for N2, O2, and CO2 were reduced to around one-third of the pure PE-LD films. An important result is that (effective) water vapor permeation coefficients calculated from results of sorption and measured by permeation experiments yielded similar values. It has been found that it is possible to describe the sorption and diffusion behavior of water by knowing the permeability coefficient and the sorption capacity of the film (Peff.?Seff.·Deff.). The tensile stress changed only slightly (values between 10 and 14 N mm-²), while the tensile strain at break was reduced with higher nominal silica gel concentration from 318 length-% (pure PE-LD film) to 5 length-% (PE-LD with 0.6 g dispersed silica gel per 1 g film).

SUBMITTER: Sangerlaub S

PROVIDER: S-EPMC6679128 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Desiccant Films Made of Low-Density Polyethylene with Dispersed Silica Gel-Water Vapor Absorption, Permeability (H2O, N2, O2, CO2), and Mechanical Properties.

Sängerlaub Sven S Kucukpinar Esra E Müller Kajetan K

Materials (Basel, Switzerland) 20190718 14

Silica gel is a well-known desiccant. Through dispersion of silica gel in a polymer, films can be made that absorb and desorb water vapor. The water vapor absorption becomes reversible by exposing such films to a water vapor pressure below that of the water vapor pressure during absorption, or by heating the film. The intention of this study was to achieve a better understanding about the water vapor absorption, permeability (H2O, N2, O2, CO2), and mec ...[more]

PMID: 31323894

Similar Datasets

Project description:We report state-resolved total removal cross sections and state-to-state rotational energy transfer (RET) cross sections for collisions of CN(A(2)Π, ν = 4, j F1ε) with N2, O2, and CO2. CN(X(2)Σ(+)) was produced by 266 nm photolysis of ICN in a thermal bath (296 K) of the collider gas. A circularly polarized pulse from a dye laser prepared CN(A(2)Π, ν = 4) in a range of F1e rotational states, j = 2.5, 3.5, 6.5, 11.5, 13.5, and 18.5. These prepared states were monitored using the circularly polarized output of an external cavity diode laser by frequency-modulated (FM) spectroscopy on the CN(A-X)(4,2) band. The FM Doppler profiles were analyzed as a function of pump-probe delay to determine the time dependence of the population of the initially prepared states. Kinetic analysis of the resulting time dependences was used to determine total removal cross sections from the initially prepared levels. In addition, a range of j' F1e and j' F2f product states resulting from rotational energy transfer out of the j = 6.5 F1e initial state were probed, from which state-to-state RET cross sections were measured. The total removal cross sections lie in the order CO2 > N2 > O2, with evidence for substantial cross sections for electronic and/or reactive quenching of CN(A, ν = 4) to unobserved products with CO2 and O2. This is supported by the magnitude of the state-to-state RET cross sections, where a deficit of transferred population is apparent for CO2 and O2. A strong propensity for conservation of rotational parity in RET is observed for all three colliders. Spin-orbit-changing cross sections are approximately half of those of the respective conserving cross sections. These results are in marked disagreement with previous experimental observations with N2 as a collider but are in good agreement with quantum scattering calculations from the same study ( Khachatrian et al. J. Phys. Chem. A 2009 , 113 , 3922 ). Our results with CO2 as a collider are similarly in strong disagreement with a related experimental study ( Khachatrian et al. J. Phys. Chem. A 2009 , 113 , 13390 ). We therefore propose that the previous experiments substantially underestimated the spin-orbit-changing cross sections for collisions with both N2 and CO2, suggesting that even approximate quantum scattering calculations may be more successful for such molecule-molecule systems than was previously concluded.

Dataset Information

Desiccant Films Made of Low-Density Polyethylene with Dispersed Silica Gel-Water Vapor Absorption, Permeability (H2O, N2, O2, CO2), and Mechanical Properties.

Publications

Desiccant Films Made of Low-Density Polyethylene with Dispersed Silica Gel-Water Vapor Absorption, Permeability (H<sub>2</sub>O, N<sub>2</sub>, O<sub>2</sub>, CO<sub>2</sub>), and Mechanical Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets