Significant influence of lignin on axial elastic modulus of poplar wood at low microfibril angles under wet conditions.

ABSTRACT: Wood is extensively used as a construction material. Despite increasing knowledge of its mechanical properties, the contribution of the cell-wall matrix polymers to wood mechanics is still not well understood. Previous studies have shown that axial stiffness correlates with lignin content only for cellulose microfibril angles larger than around 20°, while no influence is found for smaller angles. Here, by analysing the wood of poplar with reduced lignin content due to down-regulation of CAFFEOYL SHIKIMATE ESTERASE, we show that lignin content also influences axial stiffness at smaller angles. Micro-tensile tests of the xylem revealed that axial stiffness was strongly reduced in the low-lignin transgenic lines. Strikingly, microfibril angles were around 15° for both wild-type and transgenic poplars, suggesting that cellulose orientation is not responsible for the observed changes in mechanical behavior. Multiple linear regression analysis showed that the decrease in stiffness was almost completely related to the variation in both density and lignin content. We suggest that the influence of lignin content on axial stiffness may gradually increase as a function of the microfibril angle. Our results may help in building up comprehensive models of the cell wall that can unravel the individual roles of the matrix polymers.

SUBMITTER: Ozparpucu M

PROVIDER: S-EPMC6685656 | biostudies-literature | 2019 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Significant influence of lignin on axial elastic modulus of poplar wood at low microfibril angles under wet conditions.

Özparpucu Merve M Gierlinger Notburga N Cesarino Igor I Burgert Ingo I Boerjan Wout W Rüggeberg Markus M

Journal of experimental botany 20190801 15

Wood is extensively used as a construction material. Despite increasing knowledge of its mechanical properties, the contribution of the cell-wall matrix polymers to wood mechanics is still not well understood. Previous studies have shown that axial stiffness correlates with lignin content only for cellulose microfibril angles larger than around 20°, while no influence is found for smaller angles. Here, by analysing the wood of poplar with reduced lignin content due to down-regulation of CAFFEOYL ...[more]

PMID: 31187131

Similar Datasets

Project description:BackgroundPretreatment is a vital but expensive step in biomass biofuel production. Overall, most of this past effort has been directed at maximizing sugar yields from hemicellulose and cellulose through trials with different chemicals, operating conditions, and equipment configurations. Flowthrough pretreatment provides a promising platform to dissolution of lignocellulosic biomass to generate high yields of fermentable sugars and lignin for biofuels productions.ResultsDissolution of xylan, lignin, and cellulose from poplar wood were significantly enhanced by water-only and dilute acid (0.05% w/w, H2SO4) flowthrough pretreatment when the temperature was raised from 200°C to 280°C over a range of flow rates 10-62.5 mL/min, resulting in more than 98% solid removal. Up to 40% of original xylan was converted to xylose in the hydrolyzate and the rest xylan was solubilized into xylooligomers with negligible furfural formation. Up to 100% cellulose was removed into hydrolyzate with the highest glucose yield of 60% and low 5-hydroxymethylfurfural (5-HMF) formation. The maximal recovered insoluble lignin and soluble lignin were 98% and 15% of original lignin, respectively. In addition, enzymatic hydrolysis of pretreated whole slurries was characterized under various enzyme loadings with or without Bovine serum albumin (BSA) treatment. More than 90% glucose yield and 95% xylose yield were obtained from enzymatic hydrolysis of dilute acid pretreated whole slurries with 10 mg protein Ctec 2 with 2 mg Htec2/g glucan + xylan.ConclusionsNearly complete dissolution of whole biomass was realized through water-only and dilute acid flowthrough pretreatment under tested conditions. Temperature was considered as the most significant factor for cellulose degradation. The cellulose removal significantly increased as temperature reached 240°C for water-only and 220°C for dilute acid. Dilute acid pretreatment resulted in higher yields of recovered xylan and cellulose as monomeric sugars in the hydrolyzate than that for water-only pretreatment. Enzymes readily hydrolyzed the degraded cellulose and xylooligomers in pretreatment hydrolysate. Results suggested that kinetics controlled the flowthrough pretreatment of biomass dissolution, which was also affected by flow rate to certain extent.

Dataset Information

Significant influence of lignin on axial elastic modulus of poplar wood at low microfibril angles under wet conditions.

Publications

Significant influence of lignin on axial elastic modulus of poplar wood at low microfibril angles under wet conditions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets