Nano-confined crystallization of organic ultrathin nanostructure arrays with programmable geometries.

ABSTRACT: Fabricating ultrathin organic semiconductor nanostructures attracts wide attention towards integrated electronic and optoelectronic applications. However, the fabrication of ultrathin organic nanostructures with precise alignment, tunable morphology and high crystallinity for device integration remains challenging. Herein, an assembly technique for fabricating ultrathin organic single-crystal arrays with different sizes and shapes is achieved by confining the crystallization process in a sub-hundred nanometer space. The confined crystallization is realized by controlling the deformation of the elastic topographical templates with tunable applied pressures, which produces organic nanostructures with ordered crystallographic orientation and controllable thickness from less than 10?nm to ca. 1??m. The generality is verified for patterning various typical solution-processable materials with long-range order and pure orientation, including organic small molecules, polymers, metal-halide perovskites and nanoparticles. It is anticipated that this technique with controlling the crystallization kinetics by the governable confined space could facilitate the electronic integration of organic semiconductors.

SUBMITTER: Gao H

PROVIDER: S-EPMC6718603 | biostudies-literature | 2019 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nano-confined crystallization of organic ultrathin nanostructure arrays with programmable geometries.

Gao Hanfei H Qiu Yuchen Y Feng Jiangang J Li Shuang S Wang Huijie H Zhao Yuyan Y Wei Xiao X Jiang Xiangyu X Su Yewang Y Wu Yuchen Y Jiang Lei L

Nature communications 20190902 1

Fabricating ultrathin organic semiconductor nanostructures attracts wide attention towards integrated electronic and optoelectronic applications. However, the fabrication of ultrathin organic nanostructures with precise alignment, tunable morphology and high crystallinity for device integration remains challenging. Herein, an assembly technique for fabricating ultrathin organic single-crystal arrays with different sizes and shapes is achieved by confining the crystallization process in a sub-hun ...[more]

PMID: 31477721

Similar Datasets

Project description:One-dimensional (1-D) ultrathin (15 nm) and thin (100 nm) aligned 1-D (0001) and (0001¯) oriented zinc oxide (ZnO) nanowire (NW) arrays were fabricated on copper substrates by one-step electrochemical deposition inside the pores of polycarbonate membranes. The aspect ratio dependence of the compressive stress because of the lattice mismatch between NW array/substrate interface and crystallite size variations is investigated. X-ray diffraction results show that the polycrystalline ZnO NWs have a wurtzite structure with a = 3.24 Å, c = 5.20 Å, and [002] elongation. HRTEM and SAED pattern confirmed the polycrystalline nature of ultrathin ZnO NWs and lattice spacing of 0.58 nm. The crystallite size and compressive stress in as-grown 15- and 100-nm wires are 12.8 nm and 0.2248 GPa and 22.8 nm and 0.1359 GPa, which changed to 16.1 nm and 1.0307 GPa and 47.5 nm and 1.1677 GPa after annealing at 873 K in ultrahigh vacuum (UHV), respectively. Micro-Raman spectroscopy showed that the increase in E2 (high) phonon frequency corresponds to much higher compressive stresses in ultrathin NW arrays. The minimum-maximum magnetization magnitude for the as-grown ultrathin and thin NW arrays are approximately 8.45 × 10-3 to 8.10 × 10-3 emu/g and approximately 2.22 × 10-7 to 2.190 × 10-7 emu/g, respectively. The magnetization in 15-nm NW arrays is about 4 orders of magnitude higher than that in the 100 nm arrays but can be reduced greatly by the UHV annealing. The origin of ultrathin and thin NW array ferromagnetism may be the exchange interactions between localized electron spin moments resulting from oxygen vacancies at the surfaces of ZnO NWs. The n-type conductivity of 15-nm NW array is higher by about a factor of 2 compared to that of the 100-nm ZnO NWs, and both can be greatly enhanced by UHV annealing. The ability to tune the stresses and the structural and relative occupancies of ZnO NWs in a wide range by annealing has important implications for the design of advanced photonic, electronic, and magneto-optic nano devices.

Dataset Information

Nano-confined crystallization of organic ultrathin nanostructure arrays with programmable geometries.

Publications

Nano-confined crystallization of organic ultrathin nanostructure arrays with programmable geometries.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets