Surface Engineered Biomimetic Inks Based on UV Cross-Linkable Wood Biopolymers for 3D Printing.

ABSTRACT: Owing to their superior mechanical strength and structure similarity to the extracellular matrix, nanocelluloses as a class of emerging biomaterials have attracted great attention in three-dimensional (3D) bioprinting to fabricate various tissue mimics. Yet, when printing complex geometries, the desired ink performance in terms of shape fidelity and object resolution demands a wide catalogue of tunability on the material property. This paper describes surface engineered biomimetic inks based on cellulose nanofibrils (CNFs) and cross-linkable hemicellulose derivatives for UV-aided extrusion printing, being inspired by the biomimetic aspect of intrinsic affinity of heteropolysaccharides to cellulose in providing the ultrastrong but flexible plant cell wall structure. A facile aqueous-based approach was established for the synthesis of a series of UV cross-linkable galactoglucomannan methacrylates (GGMMAs) with tunable substitution degrees. The rapid gelation window of the formulated inks facilitates the utilization of these wood-based biopolymers as the feeding ink for extrusion-based 3D printing. Most importantly, a wide and tunable spectrum ranging from 2.5 to 22.5 kPa of different hydrogels with different mechanical properties could be achieved by varying the substitution degree in GGMMA and the compositional ratio between GGMMA and CNFs. Used as the seeding matrices in the cultures of human dermal fibroblasts and pancreatic tumor cells, the scaffolds printed with the CNF/GGMMA inks showed great cytocompatibility as well as supported the matrix adhesion and proliferative behaviors of the studied cell lines. As a new family of 3D printing feedstock materials, the CNF/GGMMA ink will broaden the map of bioinks, which potentially meets the requirements for a variety of in vitro cell-matrix and cell-cell interaction studies in the context of tissue engineering, cancer cell research, and high-throughput drug screening.

SUBMITTER: Xu W

PROVIDER: S-EPMC6727376 | biostudies-literature | 2019 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Three-dimensional (3D) printing has great potential for creating tissues and organs to meet shortfalls in transplant supply, and biomaterial inks are key components of many such approaches. There is a need for biomaterial inks that facilitate integration, infiltration, and vascularization of targeted 3D-printed structures. This study is therefore focused on creating new biomaterial inks from self-assembled capillary alginate gel (Capgel), which possesses a unique microstructure of uniform tubular channels with tunable diameters and densities. First, extrusions of Capgel through needles (0.1-0.8 mm inner diameter) were investigated. It was found that Capgel ink extrudes as slurries of fractured and entangled particles, each retaining capillary microstructures, and that extruded line widths W and particle sizes A were both functions of needle inner diameter D, specifically power-law relationships of W~D0.42 and A~D1.52, respectively. Next, various structures were successfully 3D-printed with Capgel ink, thus demonstrating that this biomaterial ink is stackable and self-supporting. To increase ink self-adherence, Capgel was coated with poly-L-lysine (PLL) to create a cationic "skin" prior to extrusion. It was hypothesized that, during extrusion of Capgel-PLL, the sheared particles fracture and thereby expose cryptic sites of negatively-charged biomaterial capable of forming new polyelectrolyte bonds with areas of the positively-charged PLL skin on neighboring entangled particles. This novel approach resulted in continuous, self-adherent extrusions that remained intact in solution. Human lung fibroblasts (HLFs) were then cultured on this ink to investigate biocompatibility. HLFs readily colonized Capgel-PLL ink and were strongly oriented by the capillary microstructures. This is the first description of successful 3D-printing with Capgel biomaterial ink as well as the first demonstration of the concept and formulation of a self-adherent Capgel-PLL biomaterial ink.

Project description:The lateral dimensions of micro- and nanostructures obtained by microcontact printing (μCP) can be easily varied by selecting stamps with the desired spacing and pattern. However, the height of these structures cannot be tuned as easily, and in most cases only 2D structures are obtained. Here, we show how the chemical cross-linking properties of polymer inks designed for μCP can be used to obtain 3D structures with heights ranging from 3 to 750 nm using the same μCP stamps. This is technologically relevant because the ink concentration affects the quality and resolution of the printed image, and therefore can only be varied in a certain range. By exploiting the cross-linking efficiency to tune the height, an additional parameter is available to reach the desired structure height without compromising the image quality. The inks were made from copolymers containing a low percentage of different UV cross-linkable repeat units: nitrobenzoxadiazole (NBD), coumarin (COU), and/or benzophenone (BP). The base polymer of the here presented model system was an antimicrobially active poly(oxanorbornene) (SMAMP), however the concept should be transferable to many other polymer backbones. We describe the fabrication and characterization of the printed micro- and nanostructures made from pure SMAMP, NBD-SMAMP, coumarin-SMAMP, BP-SMAMP, BP-NBD-SMAMP and BP-coumarin-SMAMP polymer inks. The photo-dimerization of COU during UV irradiation at λ = 254 nm was confirmed by UV-Vis spectroscopy. Since NBD and COU are fluorescent, the polymer could be visualized by fluorescence microscopy. Additionally, their height profiles were measured by atomic force microscopy (AFM). The heights of the 3D surface-attached polymer networks obtained from the here presented polymer inks correlated with the gel-content of the corresponding unstructured polymer layers, and thus with the cross-linking efficiency of the NBD, COU and BP cross-linkers. Due to being covalently cross-linked, these 3D-surface attached polymer structures were solvent-stable and stable in aqueous surroundings.

Dataset Information

Surface Engineered Biomimetic Inks Based on UV Cross-Linkable Wood Biopolymers for 3D Printing.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets