Fabrication and mechanical characterization of 3D printed vertical uniform and gradient scaffolds for bone and osteochondral tissue engineering.

ABSTRACT: Recent developments in 3D printing (3DP) research have led to a variety of scaffold designs and techniques for osteochondral tissue engineering; however, the simultaneous incorporation of multiple types of gradients within the same construct remains a challenge. Herein, we describe the fabrication and mechanical characterization of porous poly(?-caprolactone) (PCL) and PCL-hydroxyapatite (HA) scaffolds with incorporated vertical porosity and ceramic content gradients via a multimaterial extrusion 3DP system. Scaffolds of 0?wt% HA (PCL), 15?wt% HA (HA15), or 30?wt% HA (HA30) were fabricated with uniform composition and porosity (using 0.2?mm, 0.5?mm, or 0.9?mm on-center fiber spacing), uniform composition and gradient porosity, and gradient composition (PCL-HA15-HA30) and porosity. Micro-CT imaging and porosity analysis demonstrated the ability to incorporate both vertical porosity and pore size gradients and a ceramic gradient, which collectively recapitulate gradients found in native osteochondral tissues. Uniaxial compression testing demonstrated an inverse relationship between porosity, ?, and compressive modulus, E, and yield stress, ?y, for uniform porosity scaffolds, however, no differences were observed as a result of ceramic incorporation. All scaffolds demonstrated compressive moduli within the appropriate range for trabecular bone, with average moduli between 86?±?14-220?±?26?MPa. Uniform porosity and pore size scaffolds for all ceramic levels had compressive moduli between 205?±?37-220?±?26?MPa, 112?±?13-118?±?23?MPa, and 86?±?14-97?±?8?MPa respectively for porosities ranging between 14?±?4-20?±?6%, 36?±?3-43?±?4%, and 54?±?2-57?±?2%, with the moduli and yield stresses of low porosity scaffolds being significantly greater (p??0.05) to those of the highest porosity uniform scaffolds (porosity gradient scaffolds 98?±?23-107?±?6?MPa, and 102?±?7?MPa for dual composition/porosity gradient scaffolds), indicating that these properties are more heavily influenced by the weakest section of the gradient. The compression data for uniform scaffolds were also readily modeled, yielding scaling laws of the form E???(1?-??)1.27 and ?y???(1?-??)1.37, which demonstrated that the compressive properties evaluated in this study were well-aligned with expectations from previous literature and were readily modeled with good fidelity independent of polymer scaffold geometry and ceramic content. All uniform scaffolds were similarly deformed and recovered despite different porosities, while the large-pore sections of porosity gradient scaffolds were significantly more deformed than all other groups, indicating that porosity may not be an independent factor in determining strain recovery. Moving forward, the technique described here will serve as the template for more complex multimaterial constructs with bioactive cues that better match native tissue physiology and promote tissue regeneration. STATEMENT OF SIGNIFICANCE: This manuscript describes the fabrication and mechanical characterization of "dual" porosity/ceramic content gradient scaffolds produced via a multimaterial extrusion 3D printing system for osteochondral tissue engineering. Such scaffolds are designed to better address the simultaneous gradients in architecture and mineralization found in native osteochondral tissue. The results of this study demonstrate that this technique may serve as a template for future advances in 3D printing technology that may better address the inherent complexity in such heterogeneous tissues.

SUBMITTER: Bittner SM

PROVIDER: S-EPMC6744258 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fabrication and mechanical characterization of 3D printed vertical uniform and gradient scaffolds for bone and osteochondral tissue engineering.

Bittner Sean M SM Smith Brandon T BT Diaz-Gomez Luis L Hudgins Carrigan D CD Melchiorri Anthony J AJ Scott David W DW Fisher John P JP Mikos Antonios G AG

Acta biomaterialia 20190321

Recent developments in 3D printing (3DP) research have led to a variety of scaffold designs and techniques for osteochondral tissue engineering; however, the simultaneous incorporation of multiple types of gradients within the same construct remains a challenge. Herein, we describe the fabrication and mechanical characterization of porous poly(ε-caprolactone) (PCL) and PCL-hydroxyapatite (HA) scaffolds with incorporated vertical porosity and ceramic content gradients via a multimaterial extrusio ...[more]

PMID: 30905862

Similar Datasets

Project description:Osteoarthritis is a highly prevalent rheumatic musculoskeletal disorder that commonly affects many joints. Repetitive joint overloading perpetuates the damage to the affected cartilage, which undermines the structural integrity of the osteochondral unit. Various tissue engineering strategies have been employed to design multiphasic osteochondral scaffolds that recapitulate layer-specific biomechanical properties, but the inability to fully satisfy mechanical demands within the joint has limited their success. Through computational modeling and extrusion-based bioprinting, we attempted to fabricate a biphasic osteochondral scaffold with improved shear properties and a mechanically strong interface. A 3D stationary solid mechanics model was developed to simulate the effect of lateral shear force on various thermoplastic polymer/hydrogel scaffolds with a patterned interface. Additionally, interfacial shear tests were performed on bioprinted polycaprolactone (PCL)/hydrogel interface scaffolds. The first simulation showed that the PCL/gelatin methacrylate (GelMA) and PCL/polyethylene glycol diacrylate (PEGDA) scaffolds interlocking hydrogel and PCL at interface in a 1:1 ratio possessed the largest average tensile (PCL/GelMA: 80.52 kPa; PCL/PEGDA: 79.75 kPa) and compressive stress (PCL/GelMA: 74.71 kPa; PCL/PEGDA: 73.83 kPa). Although there were significant differences in shear strength between PCL/GelMA and PCL/PEGDA scaffolds, no significant difference was observed among the treatment groups within both scaffold types. Lastly, the hypothetical simulations of potential biphasic 3D printed scaffolds showed that for every order of magnitude decrease in Young's modulus (E) of the soft bioink, all the scaffolds underwent an exponential increase in average displacement at the cartilage and interface layers. The following work provides valuable insights into the biomechanics of 3D printed osteochondral scaffolds, which will help inform future scaffold designs for enhanced regenerative outcomes.

Project description:Scaffolds with continuous gradients in material composition and bioactive signals enable a smooth transition of properties at the interface. Components like chondroitin sulfate (CS) and bioactive glass (BG) in 3D scaffolds may serve as "raw materials" for synthesis of new extracellular matrix (ECM), and may have the potential to completely or partially replace expensive growth factors. We hypothesized that scaffolds with gradients of ECM components would enable superior performance of engineered constructs. Raw material encapsulation altered the appearance, structure, porosity, and degradation of the scaffolds. They allowed the scaffolds to better retain their 3D structure during culture and provided a buffering effect to the cells in culture. Following seeding of rat mesenchymal stem cells, there were several instances where glycosaminoglycan (GAG), collagen, or calcium contents were higher with the scaffolds containing raw materials (CS or BG) than with those containing transforming growth factor (TGF)-?3 or bone morphogenetic protein (BMP)-2. It was also noteworthy that a combination of both CS and TGF-?3 increased the secretion of collagen type II. Moreover, cells seeded in scaffolds containing opposing gradients of CS/TGF-?3 and BG/BMP-2 produced clear regional variations in the secretion of tissue-specific ECM. The study demonstrated raw materials have the potential to create a favorable microenvironment for cells; they can significantly enhance the synthesis of certain extracellular matrix (ECM) components when compared to expensive growth factors; either alone or in combination with growth factors they can enhance the secretion of tissue specific matrix proteins. Raw materials are promising candidates that can be used to either replace or be used in combination with growth factors. Success with raw materials in lieu of growth factors could have profound implications in terms of lower cost and faster regulatory approval for more rapid translation of regenerative medicine products to the clinic.

Project description:Over the past two decades, electrospinning has emerged as a common technique to produce biomedical scaffolds composed of ultrafine fibers formed from many natural and synthetic polymers. A major advantage of this technique is the ability to produce scaffolds that resemble the native extracellular matrix in physical, chemical, and topological properties. However, scaffolds fabricated via electrospinning are not formed with a controlled architecture and typically do a poor job of directing cell growth into prescribed structures for tissue/organ development. To address these weaknesses, 3D bioprinting has recently been used to develop scaffolds that have a highly organized and precise global topology. Unfortunately, these 3D bioprinted scaffolds do not typically resemble the native extracellular matrix in physical properties, such as porosity, fiber diameter, and pore size (e.g., the microarchitecture). Thus, the goal of the current study was to develop a technique that harnesses the intrinsic advantages of both conventional electrospinning and 3D bioprinting techniques to produce scaffolds that have the potential to be used within biomedical applications. The physical properties of formed 3D printed electrospun scaffolds were compared with conventional electrospun and 3D printed scaffolds. Further, we conducted initial proof-of-concept biocompatibility studies to illustrate the applicability of the scaffolds within vascular applications. Our results illustrate that 3D printed electrospun scaffolds can be developed, via our technique, that have highly tailored and organized arbitrary geometries with scaffold properties in the range of the innate extracellular matrix. In addition, these scaffolds were shown to support endothelial cell growth. Therefore, we illustrate the development and testing of a novel bioscaffold fabrication technique that may be used for many tissue engineering and regenerative medicine applications, which allows for the direct printing of electrospun scaffolds into well-defined macro-scale geometries that also retain the micro-structures commonly observed in electrospun scaffolds.

Dataset Information

Fabrication and mechanical characterization of 3D printed vertical uniform and gradient scaffolds for bone and osteochondral tissue engineering.

Publications

Fabrication and mechanical characterization of 3D printed vertical uniform and gradient scaffolds for bone and osteochondral tissue engineering.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets