Backbone Chemical Composition and Monomer Sequence Effects on Phenylene Polymer Persistence Lengths.

ABSTRACT: Despite a vast body of the literature devoted to the use of phenylene polymers in the fabrication of graphene nanoribbons, the study of the physical properties of these precursors still poses open questions whose answers will certainly contribute to the design of more efficient/precise synthesis protocols. Particularly, persistence length measurements combined with size exclusion chromatography techniques assign both semiflexible to semirigid structures depending on the molecular weight of the precursor (NaritaNat. Chem.2014, 6, 126-132). Peculiarly, these results suggest an apparent structural change upon increasing the length of the polymers. To address this puzzle, we use single-chain models to study the stiffness of polyphenylene precursors in a theta-like solvent as a function of chain composition and monomer sequence. Steric effects are isolated by considering random walk chains with segment length distributions and the position of monomers determined by the nature of the arene substitution along the backbone. Moreover, two homopolymer limiting cases are defined, that is, meta and para sequences, by associating two types of monomers to each possible substitution pattern. We consider, within these two limiting cases, chains with different compositions and monomer sequences. We compute persistence lengths, mean square end-to-end distances, and gyration and hydrodynamic radii. We find that distinct values of the persistence length for apparently the same chain chemistry are the result of different mixing ratios and the arrangement along the chain of the two positional isomers of the same monomer. Finally, we discuss the relation between two-dimensional density of the number of crossings and the length of polyphenylene segments as they would occur upon strong chain adsorption onto a substrate.

SUBMITTER: Forero-Martinez NC

PROVIDER: S-EPMC6750833 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Backbone Chemical Composition and Monomer Sequence Effects on Phenylene Polymer Persistence Lengths.

Forero-Martinez Nancy C NC Baumeier Björn B Kremer Kurt K

Macromolecules 20190709 14

Despite a vast body of the literature devoted to the use of phenylene polymers in the fabrication of graphene nanoribbons, the study of the physical properties of these precursors still poses open questions whose answers will certainly contribute to the design of more efficient/precise synthesis protocols. Particularly, persistence length measurements combined with size exclusion chromatography techniques assign both semiflexible to semirigid structures depending on the molecular weight of the p ...[more]

PMID: 31543550

Similar Datasets

Project description:The study reports results of using a CO2-laser in continuous wave (3 W; 2 m/s) and quasi-pulsed (13.5 W; 1 m/s) modes to treat films prepared by solvent casting technique from four types of polyhydroxyalkanoates (PHAs), namely poly-3-hydroxybutyrate and three copolymers of 3-hydroxybutyrate: with 4-hydroxybutyrate, 3-hydroxyvalerate, and 3-hydroxyhexanoate (each second monomer constituting about 30 mol.%). The PHAs differed in their thermal and molecular weight properties and degree of crystallinity. Pristine films differed in porosity, hydrophilicity, and roughness parameters. The two modes of laser treatment altered these parameters and biocompatibility in diverse ways. Films of P(3HB) had water contact angle and surface energy of 92° and 30.8 mN/m, respectively, and average roughness of 144 nm. The water contact angle of copolymer films decreased to 80-56° and surface energy and roughness increased to 41-57 mN/m and 172-290 nm, respectively. Treatment in either mode resulted in different modifications of the films, depending on their composition and irradiation mode. Laser-treated P(3HB) films exhibited a decrease in water contact angle, which was more considerable after the treatment in the quasi-pulsed mode. Roughness parameters were changed by the treatment in both modes. Continuous wave line-by-line irradiation caused formation of sintered grooves on the film surface, which exhibited some change in water contact angle (76-80°) and reduced roughness parameters (to 40-45 mN/m) for most films. Treatment in the quasi-pulsed raster mode resulted in the formation of pits with no pronounced sintered regions on the film surface, a more considerably decreased water contact angle (to 67-76°), and increased roughness of most specimens. Colorimetric assay for assessing cell metabolic activity (MTT) in NIH 3T3 mouse fibroblast culture showed that the number of fibroblasts on the films treated in the continuous wave mode was somewhat lower; treatment in quasi-pulsed radiation mode caused an increase in the number of viable cells by a factor of 1.26 to 1.76, depending on PHA composition. This is an important result, offering an opportunity of targeted surface modification of PHA products aimed at preventing or facilitating cell attachment.

Dataset Information

Backbone Chemical Composition and Monomer Sequence Effects on Phenylene Polymer Persistence Lengths.

Publications

Backbone Chemical Composition and Monomer Sequence Effects on Phenylene Polymer Persistence Lengths.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets